Search

The boron nitride nanosheets (BNNSs)/aluminum nitride (AlN) composites were prepared by hot press sintering at 1600°C. The microstructure, mechanical properties, and thermal conductivity of the samples were measured, and the effect of adding BNNSs to AlN ceramics on the properties was studied. It is found that the addition of BNNSs can effectively improve the mechanical properties of AlN. When the additional amount is 1 wt%, the bending strength of the sample reaches the maximum value of 456.6 MPa, which is 23.1% higher than that of the AlN sample without BNNSs. The fracture toughness of the sample is 4.47 MPa m1/2, a 68.7% improvement over the sample without BNNSs. The composites obtained in the experiment have brilliant mechanical properties. [ABSTRACT FROM AUTHOR]

Boron nitride nanosheets (BNNSs)/magnesium oxide (MgO) composites were prepared via hot pressing. Mechanical properties of MgO ceramics were improved obviously in virtue of adding BNNSs. The bending strength of the 1 wt% BNNSs/MgO composite increased by about 85% than that of the monolithic MgO. The fracture toughness increased by 34% with the addition of 1.5 wt% BNNSs. Microstructural analyzes have shown that the toughening mechanisms are combinations of the pull-out and bridging of BNNSs, crack deflection, and crack bypassing mechanisms. The addition of a small amount of BNNSs don't destroy the excellent dielectric properties of composites. The dielectric constant of the sample doped with 1 wt% BNNSs was about 9.5 in the whole X-band and the vast majority of P-band, and the loss tangent was less than 5 × 10−3 in 10–15.8 GHz. [ABSTRACT FROM AUTHOR]

In order to overcome intrinsic brittleness and poor mechanical properties of fused silica (FS), boron nitride nanosheets (BNNSs) as a novel reinforcement were employed for fabrication of BNNSs/fused silica composites. BNNSs with micron lateral size were homogeneously dispersed with FS powder using a surfactant-free flocculation method and then consolidated by hot pressing. The flexural strength and fracture toughness of the composite with the addition of only 0.5 wt.% BNNSs increased by 53% and 32%, respectively, compared with those of pure FS. However, for higher BNNSs contents the improvement in mechanical properties was limited. Microstructural analyzes have shown that the toughening mechanisms are combinations of the pull-out, crack bridging, and crack deflection mechanisms. [ABSTRACT FROM AUTHOR]

BNNSs were prepared efficiently by magnesium borate nitridation. BNNSs/eutectic-composition Al 2 O 3 /YAG/YSZ ceramics were prepared by hot pressing sintering. The addition of BNNSs did not change the phase composition of BNNSs/eutectic-composition Al 2 O 3 /YAG/YSZ ceramics. The bending strength and fracture toughness of 1.5wt%BNNSs/ eutectic-composition Al 2 O 3 /YAG/YSZ ceramic were increased by 19.0% and 18.9% respectively. Doped BNNSs exist at the grain boundary between two or more different grains. The toughening mechanism of BNNSs contains mainly crack deflection, BNNSs pullout and BNNSs bridging. • BNNSs/eutectic-composition Al 2 O 3 /YAG/YSZ ceramics were originally prepared with excellent mechanical properties. • The toughening mechanism of BNNSs was discussed. • The effects of temperature and BNNSs doping amount on the mechanical properties of ceramics were explored. [ABSTRACT FROM AUTHOR]

Uniformly dispersed boron nitride nanosheets (BNNSs) reinforced silicon nitride (Si 3 N 4) composites were prepared by surface modification assisted flocculation combined with SPS sintering. In order to improve the dispersibility of the BNNSs in the composites, the liquid phase stripped BNNSs are surface functionalized by a two-step covalently modification. The amino-modified BNNSs (NH 2 -BNNSs) and Si 3 N 4 powders have opposite surface potential, mixed evenly by electrostatic interaction during flocculation. The results showed that mechanical properties of Si 3 N 4 composites were obviously enhanced by adding NH 2 -BNNSs. The fracture toughness and bending strength of Si 3 N 4 composites added 0.75 wt% NH 2 -BNNSs were increased by 34% and 28%, respectively, compared with monolithic Si 3 N 4. Toughening mechanisms are synergistic action of the torn, pull-out or bridging of BNNSs and crack deflection mechanisms with microstructural analyzes. The dielectric properties of the Si 3 N 4 ceramics are also improved after the addition of NH 2 -BNNSs. [ABSTRACT FROM AUTHOR]

Abstract Boron nitride nanosheets (BNNSs) have attracted increasing attention in the field of two-dimensional materials. In the paper, the BNNSs/alumina composites were fabricated by a flocculation method and hot pressing. It is found that the BNNSs were dispersed uniformly in the alumina matrix by the flocculation technique via pH adjustment. The experimental results showed that with the increasing BNNSs content, the density of the composites decreased. Compared with the monolithic alumina, bending strength of the composite with 1.0 wt% BNNSs was increased by 58.6%; while the fracture toughness was increased slightly. The addition of BNNSs changed the fracture pattern, refined the grains of composites and inhibited abnormal grain growth, which contributed to the improvement of mechanical properties of the composites. [ABSTRACT FROM AUTHOR]