The chemical durability of borosilicate glass used to confine nuclear wastes is known to vary nonlinearly with their composition, making glass dissolution rate predictions difficult. Here, we focus on the effect of Al, an important oxide of these materials. The initial and residual glass dissolution rates were investigated through experiments conducted at 90 °C and pH 9. Our results show that low Al content glasses dissolve initially faster than glasses with higher Al content, but quickly achieve a lower residual rate due to the rapid formation of a more passivating gel. Nevertheless, the high Al content gel will eventually achieve passivation with a slower reorganization. The strengthening effect of Al on the Si-O bond hydrolysis will result in more stable gels, suggesting that slightly higher Al content in the gel will improve nuclear high-level waste glass durability in geological disposal conditions. [ABSTRACT FROM AUTHOR]

Borosilicate glasses are widely used to confine high-level radioactive wastes. The lifetime of these materials could reach hundreds of thousands of years if leaching of the glass into groundwater enables the formation of a passivating gel layer. Even in this regime, the glass will never stop corroding as thermodynamic equilibrium between glass and solution cannot be achieved. Therefore, accurate predictions of glass durability including passivation, require a deep understanding of the mechanisms controlling the so-called residual rate. However, despite tremendous efforts, these mechanisms remain poorly understood. Here, focusing on the behavior of the soluble elements of the International Simple Glass (B, Na, and Ca), we show that the residual rate is controlled by the behavior of B, a glass former supposed to dissolve instantaneously when in contact with water and thus widely considered as an ideal tracer. We then demonstrate that B release is controlled by multiple processes highly dependent on the pH. At the beginning of the passivating layer formation, the hydrolysis of B-O-Si linkages is rate-limiting and has an activation energy of ∼60 kJ mol−1, a value slightly lower than that for breaking Si-O-Si linkages. Once the fraction of closed pores resulting from gel restructuring is high enough, then diffusion of both reactants (water molecules) and some products (mainly Baq, Caaq) through the growing gel layer becomes rate-limiting. Consequently, B and Ca accumulate in an inner layer referred to as the active zone, with potential feedback on the B-O-Si hydrolysis. A new paradigm, including B as a key element of the system, is proposed to develop a comprehensive model for the corrosion of borosilicate glass. [ABSTRACT FROM AUTHOR]