Search

To fabricate a C/C-SiC (Carbon fiber-reinforced Silicon Carbide) with favorable mechanical properties via the Liquid Silicon Infiltration process, it is crucial to focus on the first fabrication step, the creation of a CFRP (carbon fiber-reinforced plastic). Hence, the selection of a fitting polymer is essential. Besides thermosets, thermoplastics can be used as matrix material. Nevertheless, the high melt viscosity of thermoplastics leads to problems regarding the fiber bundle infiltration. This study shows for the first time that this problem can be avoided by using C/C-SiC based on a novel short fiber C f /PEEK fiber hybrid yarn. The yarn was warm pressed into a CFRP, pyrolyzed and infiltrated with C/C-SiC. The product of each processing step was characterized with a focus on the analysis of the microstructure. Additionally, for the C/C-SiC, three-point bending tests were conducted. Those results were simular compared to reference literature. [Display omitted] [ABSTRACT FROM AUTHOR]

Processing carbon fiber reinforced thermoplastic parts includes heating to form the thermoplastic matrix. The needed heat can be applied externally or internally to the preform. One possibility to generate intrinsic heat involves the use of carbon fibers as a resistive element to induce joule heat. So far, most research efforts have been based on contacting continuous carbon fibers on both ends to melt the thermoplastic matrix of a pre-impregnated preform. The objective of this project is to use a dry hybrid yarn textile in a one-step process to impregnate and rapidly consolidate the dry textile in less than a minute. The desired molding process is based on joule heating of carbon fibers due to an applied current in the transverse fiber direction. This article focuses on the detection of the involved macroscopic parameters. The first composites produced by means of this new method exhibit a high potential with heating times of 15 s, a void fraction below 1%, and flexural properties comparable to the state of the art. [ABSTRACT FROM AUTHOR]

This article reports the results of investigations carried out to produce yarns consisting of staple carbon fiber (CF) obtained from process waste for the manufacturing of composites suitable especially for thermoset applications. For this purpose, a comparative analysis is done on processability between 100% staple CF and 60 weight% staple CF mixed with 40 weight% PVA fibers in carding, drawing and spinning process. The hybrid yarns are produced by varying twist level. The PVA fibers of the hybrid yarn are then dissolved using hot water treatment. The mechanical properties of yarns consisting of 100% staple CF and hybrid yarns consisting of staple CF and PVA before and after hot water treatment are investigated. Furthermore, test specimen is also prepared by impregnating 100% staple CF yarn and the hybrid yarns (after the dissolving of PVA) with epoxy resin. The results of the tensile test of the yarns in consolidated state reveals that the hybrid yarn produced with 80 T/m after hot water treatment exhibits approximately 75% of the tensile strength of virgin filament tow, and it is expected that the hybrid yarns can be applied for the manufacturing of thermoset based composites for load bearing structures.

Processing carbon fiber reinforced thermoplastic parts includes heating to form the thermoplastic matrix. The needed heat can be applied externally or internally to the preform. One possibility to generate intrinsic heat involves the use of carbon fibers as a resistive element to induce joule heat. So far, most research efforts have been based on contacting continuous carbon fibers on both ends to melt the thermoplastic matrix of a pre-impregnated preform. The objective of this project is to use a dry hybrid yarn textile in a one-step process to impregnate and rapidly consolidate the dry textile in less than a minute. The desired molding process is based on joule heating of carbon fibers due to an applied current in the transverse fiber direction. This article focuses on the detection of the involved macroscopic parameters. The first composites produced by means of this new method exhibit a high potential with heating times of 15 s, a void fraction below 1%, and flexural properties comparable to the state of the art. [ABSTRACT FROM AUTHOR]

This article reports the results of investigations carried out to produce yarns consisting of staple carbon fiber (CF) obtained from process waste for the manufacturing of composites suitable especially for thermoset applications. For this purpose, a comparative analysis is done on processability between 100% staple CF and 60 weight% staple CF mixed with 40 weight% PVA fibers in carding, drawing and spinning process. The hybrid yarns are produced by varying twist level. The PVA fibers of the hybrid yarn are then dissolved using hot water treatment. The mechanical properties of yarns consisting of 100% staple CF and hybrid yarns consisting of staple CF and PVA before and after hot water treatment are investigated. Furthermore, test specimen is also prepared by impregnating 100% staple CF yarn and the hybrid yarns (after the dissolving of PVA) with epoxy resin. The results of the tensile test of the yarns in consolidated state reveals that the hybrid yarn produced with 80 T/m after hot water treatment exhibits approximately 75% of the tensile strength of virgin filament tow, and it is expected that the hybrid yarns can be applied for the manufacturing of thermoset based composites for load bearing structures. [ABSTRACT FROM AUTHOR]