Nickel ferrite owns a lot of advantages as electrode materials for supercapacitor, such as high energy density and excellent theoretical capacity. Whereas, the electrochemical performances of NiFe 2 O 4 in terms of rate performance and cycle stability are not satisfactory due to the low conductivity. While carbon fiber is a kind of material with high conductivity. Hence, NiFe 2 O 4 @ slit modified hollow carbon fiber is obtained through the coaxial electrospinning method. The slits on hollow carbon fibers are beneficial to the contact of inner NiFe 2 O 4 nanoparticles with electrolyte. Results of electrochemical tests show that at a current density of 1 A/g, the specific capacitance of NiFe 2 O 4 @ slit modified hollow carbon fiber is calculated to be 225.4 F/g, higher than that of NiFe 2 O 4 nanoparticles of 134.8 F/g. Moreover, a better cycle and rate performances (100 % vs 80 %; 71.9 % vs 47.5 %) are achieved. This work displays that slit modified hollow carbon fiber can improve the electrochemical performance of NiFe 2 O 4 efficiently. [Display omitted] • Carbon fibers are introduced to enhance the rate and cycle performances of NiFe 2 O 4. • Slits are obtained utilizing Al 2 O 3 sacrificial hard templates. • Slits are beneficial to the contact of NiFe 2 O 4 and electrolyte. [ABSTRACT FROM AUTHOR]

Core-shell hierarchical structured composites have demonstrated great advantages in numerous energy storage devices. In particular, structured composites with rationally structural components and controllable morphology are the most effective in enhancing electrochemical properties. In this work, MnO 2 @NiCo 2 O 4 @Ti 3 SiC 2 /CC (carbon cloth) core-shell hierarchical structured composites were designed and successfully synthesized via electrospinning followed by a two-step hydrothermal reaction. The Ti 3 SiC 2 /CC nanofibers and core-shell nanoarrays were able to improve the specific capacitance and cycling stability. In the three-electrode system, the specific capacitance of MnO 2 @NiCo 2 O 4 @Ti 3 SiC 2 /CC was observed as 1938.2 F/g at a current density of 1 A/g, while the rate capability retention was observed as 81.7% between 1 and 10 A/g. Furthermore, a superior cycling stability was observed following 5000 cycles with a specific capacitance retention rate of 55.4%. Employing MnO 2 @NiCo 2 O 4 @Ti 3 SiC 2 /CC as the all solid-state supercapacitor positive electrode exhibited a high energy density of 58.0 W h/kg at the power density of 800 W/kg. Results demonstrate the potential of the MnO 2 @NiCo 2 O 4 @Ti 3 SiC 2 /CC as an electrode material with phenomenal electrochemical properties for supercapacitors. [ABSTRACT FROM AUTHOR]