The hydrogen sorption of materials based on 80 wt.% MgH2 with the addition of 15 wt.% Ni or V and 5 wt.% activated carbons synthesized from polyolefin wax, a waste product from polyethylene production (POW), walnut shells (CAN), and peach stones (CPS) prepared by milling under an inert Ar atmosphere for a period of 1 h, is investigated. All precursors are submitted to pyrolysis followed by steam activation in order to obtain the activated carbons. The hydrogen sorption evaluations are carried out for absorption at 473 and 573 K with pressure of 1 MPa and for desorption at 623 and 573 K with pressure of 0.15 MPa. The composition of the samples after milling and hydrogenation is monitored by X-ray diffraction analyses. The 80 wt.% MgH2–15 wt. %Ni–5 wt.% POW or CAN after absorption–desorption cycling and in a hydrogenated state at 573 K and 1 MPa are analyzed by TEM. [ABSTRACT FROM AUTHOR]

Magnesium-based materials are promising as hydrogen storage media due to their high theoretical hydrogen absorption capacity, abundance and low price. The subject of this study are the hydrogen sorption characteristics of the composites 80 wt % MgH2-15 wt % Ni-5 wt % activated carbon (synthesized from polyolefin wax, a waste product of polyethylene production at low pressure which will be denoted further in the text as POW) and 90 wt % MgH2-5 wt % Ni-5 wt % POW, prepared by ball milling under argon atmosphere. Structure, phase and surface composition of the samples before and after hydrogenation are determined by XRD and TEM. The maximum absorption capacity value of the composites at a temperature 573 K and after 60 min. of hydrogenation are 5.3 wt % H2 for the material with higher Ni content and 5.5 wt % H2 for the other sample. The presence of both additives—nickel and activated carbon derived from POW—has a positive impact on hydrogenation kinetics and the capacity achieved. The results from TEM characterization, e.g., the polycrystalline SAED (selected area electron diffraction) show the presence of graphite, Mg and monoclinic Mg2NiH4. [ABSTRACT FROM AUTHOR]