Search

Nanocomposites based on PtPd nanoparticles with chemical ordering like disordered solid solution on surface of multilayer graphene have been prepared through thermal shock of mechanically obtained mixture of double complex salt [Pd(NH)][PtCl] and different carbon materials-exfoliated graphite, graphite oxide and graphite fluoride. An effect of original carbon precursors on formation of PtPd bimetallic nanoparticles was studied using X-ray absorption spectroscopy (XAFS), transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). It was shown that the distribution of bimetallic nanoparticles over the multilayer graphene surface as well as the particles size distribution is controlled by the graphene precursors. For all nanocomposites, the surface of the nanoparticles was found to be Pd-enriched. In case when the thermal exfoliated graphite and graphite oxide were used as the graphene precursors a thin graphitized layer covered the nanoparticles surface. Such a graphitized layer was not observed in the nanocomposite, which used the fluorinated graphite as the precursor. [ABSTRACT FROM AUTHOR]

Nitrogen-doped and pure carbon nanotube (CNT) based composites were fabricated for investigating their dielectric properties in static regime as well as electromagnetic response properties in microwave frequency range (Ka-band). Two classes of host matrix-polystyrene and phosphate unfired ceramics-have been used for composites fabrication. The study reveals miscellaneous effect of nitrogen doping on the dielectric permittivity, dc conductivity and electromagnetic interference shielding efficiency of CNT-based composites, produced with both polymer and ceramic matrices. The high-frequency polarizability, estimated for different-length CNTs, and static polarizability, calculated for nitrogen-containing CNT models using a quantum-chemical approach, show that this effect results from a decrease of the nanotube defect-free-length and deterioration of the polarizability with incorporation of nitrogen in pyridinic form. [ABSTRACT FROM AUTHOR]

Nitrogen-containing carbon (CNx) nanotubes have been grown vertically on silicon substrates by decomposition of a ferrocene/acetonitrile aerosol at temperatures 750, 800, 850, and 900 °С. A CNx nanotube array, produced at 850 °С, had the greatest height ∼220 μm and the smallest nitrogen content ∼3.8 at%. The content of graphitic nitrogen form, referred to a nitrogen atom with three carbon neighbors in a hexagonal lattice, increased gradually with the synthesis temperature. Field electron emission measurements showed that the CNx nanotube arrays have better characteristics than aligned non-doped carbon nanotubes. To reveal effect of nitrogen on the filed threshold, we calculated current-voltage dependencies for CNx nanotube models containing different amount of graphitic and pyridinic nitrogen species. Influence of the synthesis temperature on the height and total nitrogen content in CNx nanotube array and relation of these parameters with the threshold of field emission appearance. [ABSTRACT FROM AUTHOR]

Detonation nanodiamonds (NDs) were deposited on the surface of aligned carbon nanotubes (CNTs) by immersing a CNT array in an aqueous suspension of NDs in dimethylsulfoxide (DMSO). The structure and electronic state of the obtained CNT-ND hybrid material were studied using optical and electron microscopy and Infrared, Raman, X-ray photoelectron and near-edge X-ray absorption fine structure spectroscopy. A non-covalent interaction between NDs and CNT and preservation of vertical orientation of CNTs in the hybrid were revealed. We showed that current-voltage characteristics of the CNT-ND cathode are changed depending on the applied field; below ~3 V/µm they are similar to those of the initial CNT array and at the higher field they are close to the ND behavior. Involvement of the NDs in field emission process resulted in blue luminescence of the hybrid surface at an electric field higher than 3.5 V/µm. Photoluminescence measurements showed that the NDs emit blue-green light, while blue luminescence prevails in the CNT-ND hybrid. The quenching of green luminescence was attributed to a partial removal of oxygen-containing groups from the ND surface as the result of the hybrid synthesis. [ABSTRACT FROM AUTHOR]