Search

Electroreduction of CO2 to C2+ products provides a promising strategy for reaching the goal of carbon neutrality. However, achieving high selectivity of C2+ products at high current density remains a challenge. In this work, we designed and prepared a multi‐sites catalyst, in which Pd was atomically dispersed in Cu (Pd−Cu). It was found that the Pd−Cu catalyst had excellent performance for producing C2+ products from CO2 electroreduction. The Faradaic efficiency (FE) of C2+ products could be maintained at approximately 80.8 %, even at a high current density of 0.8 A cm−2 for at least 20 hours. In addition, the FE of C2+ products was above 70 % at 1.4 A cm−2. Experiments and density functional theory (DFT) calculations revealed that the catalyst had three distinct catalytic sites. These three active sites allowed for efficient conversion of CO2, water dissociation, and CO conversion, ultimately leading to high yields of C2+ products. [ABSTRACT FROM AUTHOR]

Electroreduction of CO2 to C2+ products provides a promising strategy for reaching the goal of carbon neutrality. However, achieving high selectivity of C2+ products at high current density remains a challenge. In this work, we designed and prepared a multi‐sites catalyst, in which Pd was atomically dispersed in Cu (Pd−Cu). It was found that the Pd−Cu catalyst had excellent performance for producing C2+ products from CO2 electroreduction. The Faradaic efficiency (FE) of C2+ products could be maintained at approximately 80.8 %, even at a high current density of 0.8 A cm−2 for at least 20 hours. In addition, the FE of C2+ products was above 70 % at 1.4 A cm−2. Experiments and density functional theory (DFT) calculations revealed that the catalyst had three distinct catalytic sites. These three active sites allowed for efficient conversion of CO2, water dissociation, and CO conversion, ultimately leading to high yields of C2+ products. [ABSTRACT FROM AUTHOR]

Electrochemical reduction of CO2 by renewable electricity offers a promising way to settle excessive greenhouse gases and achieve carbon neutrality under a mild environment. Cu-based catalysts have a unique catalytic activity towards multicarbon (C2+) products in the CO2 electroreduction reaction and are widely studied to promote the corresponding selectivity and activity. Here we report a F-doped Cu (F–Cu) catalyst to improve C2+ products in CO2 electroreduction. A high C2+ product (mainly ethylene and ethanol) faradaic efficiency of 70.4% was achieved on the F–Cu catalyst with a high current density (above 400 mA cm−2) in the flow-cell system. The in situ surface enhanced Raman spectroscopy results and electrochemical performance analysis demonstrated that CO2 could be reduced into CO at low potentials and the adsorption of CO could be strengthened on F–Cu, which is beneficial to the subsequent C–C coupling step and formation of the C2+ products. [ABSTRACT FROM AUTHOR]

Developing electrocatalytic reactions with high‐efficiency can make important contributions to carbon neutrality. However, poor long‐term stability of catalysts is a bottleneck for its practical application. Herein, an "in situ periodic regeneration of catalyst (PR‐C)" strategy is proposed to give long‐term high efficiency of CO2 electroreduction to generate C2+ products over Cu catalyst by applying a positive potential pulse for a short time periodically in the halide‐containing electrolyte. The high Faradaic efficiency (81.2 %) and current density (22.6 mA cm−2) could be maintained completely at least 36 h, while the activity and selectivity decreased continuously without using the PR‐C method. Control experiments and operando characterization demonstrated that the surface structure and oxidation state of Cu could be recovered periodically by the PR‐C method, which was beneficial for CO2 activation and C−C coupling. [ABSTRACT FROM AUTHOR]

Developing electrocatalytic reactions with high‐efficiency can make important contributions to carbon neutrality. However, poor long‐term stability of catalysts is a bottleneck for its practical application. Herein, an "in situ periodic regeneration of catalyst (PR‐C)" strategy is proposed to give long‐term high efficiency of CO2 electroreduction to generate C2+ products over Cu catalyst by applying a positive potential pulse for a short time periodically in the halide‐containing electrolyte. The high Faradaic efficiency (81.2 %) and current density (22.6 mA cm−2) could be maintained completely at least 36 h, while the activity and selectivity decreased continuously without using the PR‐C method. Control experiments and operando characterization demonstrated that the surface structure and oxidation state of Cu could be recovered periodically by the PR‐C method, which was beneficial for CO2 activation and C−C coupling. [ABSTRACT FROM AUTHOR]