Transformer oil-based nanofluid-impregnated pressboard (NIP) with TiO 2 nanoparticles has been previously shown to exhibit substantially higher AC breakdown strength than that of pure oil-impregnated pressboard (OIP). In this study, OIP and NIP with TiO 2 nanoparticles were prepared and experiments on DC breakdown strength of were performed. It was found that NIP possesses higher resistance to DC breakdown strength than that of OIP. To reveal the working mechanism, a pulsed electro acoustic (PEA) device was used to measure the space charge accumulation and dissipation characteristics in OIP and NIP. The results show that the density of deep level traps in NIP is visibly reduced owing to the addition of TiO 2 nanoparticles and homopolar space charge accumulation on both sides of NIP is suppressed. Moreover, the charges injected from electrodes into NIP under DC voltage is also restrained owing to the increase of the Schottky potential barrier. Thus, the DC breakdown performance of NIP is considerably improved. [ABSTRACT FROM AUTHOR]

Creeping flashover of mineral-oil-impregnated pressboard under impulse stress is a common insulating failure in oil-immersed transformers, arousing increasing attention. Recent studies have shown that the breakdown strength of transformer oil under positive lightning impulse voltage can be significantly improved through nanoparticles-based modification, and Fe3O4 has shown the best improvement in breakdown strength compared to other nanoparticles that have been used. This paper presents the creeping flashover characteristics of pure oil-impregnated pressboard (OIP) and nanofluid-impregnated pressboard (NIP) based on Fe3O4 nanoparticles under positive and negative lightning impulse voltages, respectively. It was found that NIP possessed higher resistance to creeping flashover than OIP. The relative permittivities of oil and oil-impregnated pressboard before and after nanoparticles-based modification were measured, and the results revealed that the addition of nanoparticles led to a better match in relative permittivity between oil and oil-impregnated pressboard, and a more uniform electric field distribution. Furthermore, the shallow trap density in NIP was obviously increased compared to that of OIP through the thermally stimulated depolarization current (TSDC), which promoted the dissipation of surface charges and weakened the distortion of the electric field. Therefore, the creeping flashover characteristics of oil-impregnated pressboard were greatly improved with Fe3O4 nanoparticles. [ABSTRACT FROM AUTHOR]