Search

Aiming at the problem of over-grinding and under-grinding and the influence of grinding mode and feed size on ore grinding effect. Cassiterite polymetallic sulfide ore was taken as the research object. The grain size distribution of grinding minerals and grinding behavior characteristics were explored based on batch grinding test, by changing grinding method, feed sizes, grinding time and other factors affecting grinding. It was shown by the results that attrition grinding process was a low-energy grinding, the force of ore was small, and the under-grinding was easy to occur, whereas drop grinding and impact grinding processes were high-energy grinding, the ore was subjected to greater force, more fully broken, easy to occur over-grinding phenomenon. The variation amplitude of grinding technical efficiency E and grinding mineral substance tw was stable with grinding time under grinding conditions, and the product size distribution was uniform. Grinding technical efficiency E and grinding product t10 were changed obviously with the grinding time under drop grinding and impact grinding, and the change range was large, and in general, the two grinding indexes are greater than that of attrition grinding. Complicated and without obvious rule was the relationship between the grinding behavior of ore and the feeding size. A theoretical basis for the subsequent research on the strength and interaction of attrition and impact forces in the dropping state was provided by the research results. [ABSTRACT FROM AUTHOR]

Semi-autogenous (SAG) mills are widely used grinding equipment, but some ore with critical particle sizes cannot be effectively processed by SAG mills and turned into pebbles. This research aims to analyze and compare the properties of raw ore and pebbles from a zinc- and tin-bearing ore. The results show that the contents of sphalerite, cassiterite, biotite, antigorite, pyroxferroite, ferroactinolite, and ilvaite in the raw ore are higher than those in the pebbles, and that the pebbles have higher contents of hedenbergite, chlorite, epidote, actinolite, etc. Meanwhile, the abrasion and impact resistance of pebbles is greater than that of the raw ore. In addition, the sphalerite is evenly embedded, and the grinding process is regular. Fine cassiterite associated with harder minerals is difficult to dissociate; it is often found in softer or brittle minerals which may be easily ground into ore mud. The cassiterite in the pebbles is associated with hard and brittle hedenbergite and soft chlorite, making it difficult to recover. This research provides a good foundation for evaluating the recovery value of pebbles and improving the productivity of the SAG process. [ABSTRACT FROM AUTHOR]

To attempt a new approach to improve the grinding of cassiterite–polymetallic sulfide ores while simultaneously reducing cassiterite overgrinding and sulfide undergrinding, this article looked into the effects of grinding chemical additives on the distribution of grinding product size. Six chemicals, namely sodium hexametaphosphate, triethanolamine, ferric sulphate, aluminum chloride, polyaluminum chloride and polyacrylamide, were compared in terms of their influence on the grinding product size distribution. The results showed that the six chemicals changed the distribution results with varying orientations and degrees and that the addition of polyacrylamide achieved the most satisfactory effect by decreasing the production of both coarse and fine size fractions and increasing the production of qualified particles. The effect of the molecular weight of polyacrylamide on the grinding was also discussed. The polyacrylamides with molecular weights of about 3 × 106, 5 × 106, 8 × 106 and 12 × 106 could help to produce less of the coarse size fraction and more of the qualified size fraction, but only the polyacrylamides with molecular weights of 3 × 106 and 5 × 106 produced pronounced changes. Moreover, the polyacrylamides could slightly reduce the production of the fine size fraction. Polyacrylamide with a 5 × 106 molecular weight was better than that with a 3 × 106 molecular weight in aiding the grinding of the discussed ore. It was also found that the aid action of the polyacrylamide with a 5 × 106 molecular weight was related to grinding concentration and that a low grinding concentration of less than 70% solid mass was helpful in exerting its aid action. Using polyacrylamide could shorten the grinding time that is needed to achieve the same, or even improved, product size distribution. [ABSTRACT FROM AUTHOR]

To solve the problem involved in the grinding of cassiterite–polymetallic sulfide ore in which fine grinding causes the cassiterite to be overground or coarse grinding leads to inadequate liberation of sulfide minerals, the influences of the ball grinding medium on the size distribution of the grinding product were investigated. Two types of ball filling patterns, namely, single-sized and multi-sized ball grinding media, were adopted in wet batch grinding tests. The results show that increasing the grinding time resulted in a rapid increase in minus 0.038 mm particles and a slight increase in the Sn grade in this fine size fraction. The smaller the ball filling fraction was, the more obviously the ball size affected the size distribution of the grinding product, the variation of which with the ball size became complicated with the increase in the ball filling fraction. Obvious jumping phenomena in the plotting of the percentages of the discussed size fractions against the ball size were observed when the balling filling fraction was larger than 30%; the most obvious jumping phenomena took place at a 35% ball filling fraction. The results of the grinding tests with the multi-sized media show that the size distribution of the grinding product was closely related to that of the mixed ball sizes and their composition percentages. [ABSTRACT FROM AUTHOR]

When cassiterite polymetallic sulfide ore is being ground in the ball mill, the contradiction between over grinding of cassiterite and under grinding of sulfide ore is inevitable due to their mechanical property differences. In this paper, a selective grinding characterization method is proposed to optimize the grinding of cassiterite polymetallic sulfide ore based on the respective selective grinding indexes, namely, the changes in the cumulative grade and cumulative quantities of metal. The preferred grinding characteristics were studied by varying three grinding operation factors, the grinding time, grinding concentration, and mill speed, as these all affect the selective grinding behavior of the ball mill. In the proposed method, the breaking process preferentially begins with the Zn minerals in the cassiterite polymetallic sulfide ore; however, Sn minerals are found to break first when the specific energy of the grinding media is large. The differences in the crushing characteristics of Zn and Sn minerals narrow down as the grinding time and concentration increase. When the grinding concentration is lower than 50%, the two types of minerals are broken with little difference. However, when the grinding concentration is higher than 50%, the Zn minerals are broken prior to the Sn minerals. [ABSTRACT FROM AUTHOR]

We investigated the influence of microwave and conventional heating pretreatments on the grinding of cassiterite associated with pollimetallic ore. The minerals that exhibited a stronger microwave absorption ability crushed first, which is the main difference between the microwave and the traditional heating pretreatments. The distribution of Fe, Pb, Zn, and Sn increased in the fine size range (−0.425 mm). The Fe and Pb grades in the size ranges of −3.2 + 2 mm and −2 + 1 mm after the microwave pretreatment (6 kW, 1 min) were lower than those of the traditional heating (12 kW, 400 °C, 20 min), indicating that the microwave selective heating was beneficial for pyrite and jamesonite. The grade and distribution of Sn decreased significantly in the size ranges of −3.2 + 2 mm and −2 + 1 mm and increased in the size ranges of −0.425 + 0.15 mm and −0.15 + 0.074 mm. Microwave heating treatment promoted the grinding of sulfide ore and reduced the cassiterite overgrinding. [ABSTRACT FROM AUTHOR]

Due to the differences in beneficiation methods and mineral properties between cassiterite ore and polymetallic sulfide ore, there is an inherent contradiction between cassiterite overgrinding and sulfide ore undergrinding. A method to optimize and characterize the grinding performance is presented in this paper. In this method, the grinding characteristics are defined by the qualified particle size range index under unit energy consumption. By changing the grinding time, grinding concentration, and filling ratio, the optimized grinding conditions were evaluated, and they were predicted and verified by the response surface method. The results corroborate that when the grinding time of cassiterite is 4 min and the grinding time of sulfide ore is 8 min, the grinding qualified size range index under unit energy consumption is the largest. Cassiterite is brittle and easy to grind due to low hardness, while sulfide is difficult to grind due to high hardness. Hence, the time to beneficiate tin ore is when the grinding time is 4 min, and that to beneficiate sulfide ore is when the regrinding time is approximately 4 min. In this way, the contradiction between overgrinding cassiterite and undergrinding sulfide ore can be alleviated on the basis of the most effective utilization of grinding energy. The optimal grinding concentration and filling ratio are 65% and 37%, respectively. The response surface prediction and test results are almost identical, with an error of ±2%. Thus, the effectiveness of grinding characterization method is verified. [ABSTRACT FROM AUTHOR]