Due to the rapid development of intelligent technology and the pursuit of green environmental protection, responsive materials with single response and actuation can no longer meet the requirements of modern technology for intelligence, diversification, and environmental friendliness. Therefore, intelligent responsive materials have received much attention. In recent years, with the development of new materials and technologies, cellulose materials have become increasingly used as responsive materials due to their advantages of sustainability and renewability. This review summarizes the relevant research on cellulose-based intelligent responsive materials in recent years. According to the stimuli responses, they are divided into temperature-, light-, electrical-, magnetic-, and humidity-responsive types. The response mechanism, application status, and development trend of cellulose-based intelligent responsive materials are summarized. Finally, the future perspectives on the preparation and applications of cellulose-based intelligent responsive materials are presented for future research directions. [ABSTRACT FROM AUTHOR]

Wooden building materials have advantages in terms of biodegradability, non-toxicity, pollution-free and recycling. Currently, applications of natural wood are extremely limited because of low density, low strength and toughness. Therefore, we reported an effective modification strategy with nano-scale cellulose nanofibrils design to prepare a synergistically enhanced cellulosic material. Via three steps: i) the secondary alcohol hydroxyl groups in C 2 , C 3 position were cut; ii) oxidize the hydroxyl group at C 2 , C 3 position to achieve dialdehyde cellulose; and iii) oxidized again to obtain dicarboxylic cellulose. Subsequently, thanks to the regulation of the average moisture content, the moisture content in the wood surface and subsurface increased in a short time. The wood softening layer contributes to the hotpressing treatment of the wood. The mechanical properties and dimensionality have been greatly improved. The obtained delignified oxidated hot-pressed wood with 0.55 mmol/g carboxyl group content demonstrates excellent strength of 328.8 ± 7.43 MPa and Young's modulus of 8.1 ± 0.14 GPa, which is twice than that of natural wood. Delignified oxidated hot-pressed wood also shows exceptional toughness of 8.3 ± 0.28 MJ/m3. Other than that, the shore hardness indicates 0.55 mmol/g carboxylic group, which could increase the hardness at the wood surface hardness to 72.5 ± 4.29°. [ABSTRACT FROM AUTHOR]