Search

Background and Aims The mobile carbon supply to different compartments of a tree is affected by climate, but its impact on cell-wall chemistry and mechanics remains unknown. To understand better the variability in root growth and biomechanics in mountain forests subjected to substrate mass movement, we investigated root chemical and mechanical properties of mature Abies georgei var. smithii (Smith fir) growing at different elevations on the Tibet–Qinghai Plateau. Methods Thin and fine roots (0·1–4·0 mm in diameter) were sampled at three different elevations (3480, 3900 and 4330 m, the last corresponding to the treeline). Tensile resistance of roots of different diameter classes was measured along with holocellulose and non-structural carbon (NSC) content. Key Results The mean force necessary to break roots in tension decreased significantly with increasing altitude and was attributed to a decrease in holocellulose content. Holocellulose was significantly lower in roots at the treeline (29·5 ± 1·3 %) compared with those at 3480 m (39·1 ± 1·0 %). Roots also differed significantly in NSC, with 35·6 ± 4·1 mg g−1 dry mass of mean total soluble sugars in roots at 3480 m and 18·8 ± 2·1 mg g−1 dry mass in roots at the treeline. Conclusions Root mechanical resistance, holocellulose and NSC content all decreased with increasing altitude. Holocellulose is made up principally of cellulose, the biosynthesis of which depends largely on NSC supply. Plants synthesize cellulose when conditions are optimal and NSC is not limiting. Thus, cellulose synthesis in the thin and fine roots measured in our study is probably not a priority in mature trees growing at very high altitudes, where climatic factors will be limiting for growth. Root NSC stocks at the treeline may be depleted through over-demand for carbon supply due to increased fine root production or winter root growth. [ABSTRACT FROM AUTHOR]

Root tensile strength is an important factor to consider when choosing suitable species for reinforcing soil on unstable slopes. Tensile strength has been found to increase with decreasing root diameter, however, it is not known how this phenomenon occurs. We carried out tensile tests on roots 0.2–12.0 mm in diameter of three conifer and two broadleaf species, in order to determine the relationship between tensile strength and diameter. Two species, Pinus pinaster Ait. and Castanea sativa Mill., were then chosen for a quantitative analysis of root cellulose content. Cellulose is responsible for tensile strength in wood due to its microfibrillar structure. Results showed that in all species, a significant power relationship existed between tensile strength and root diameter, with a sharp increase of tensile strength in roots with a diameter <0.9 mm. In roots >1.0 mm, Fagus sylvatica L. was the most resistant to failure, followed by Picea abies L. and C. sativa., P. pinaster and Pinus nigra Arnold roots were the least resistant in tension for the same diameter class. Extremely high values of strength (132–201 MPa) were found in P. abies, C. sativa and P. pinaster, for the smallest roots (0.4 mm in diameter). The power relationship between tensile strength and root diameter cannot only be explained by a scaling effect typical of that found in fracture mechanics. Therefore, this relationship could be due to changes in cellulose content as the percentage of cellulose was also observed to increase with decreasing root diameter and increasing tensile strength in both P. pinaster and C. sativa. [ABSTRACT FROM AUTHOR]