An innovative approach for fabricating porous alumina ceramics (PACs) with improved mechanical and thermal properties using walnut shell powders as pore-forming agent combined with alumina sol impregnation is reported in the present work. It is demonstrated that uniform distribution of spherical pores can be observed in as-prepared PACs by using above technical route. The decrease of walnut shell powder sizes significantly promotes the enhancement of crushing strength and reduction of thermal conductivity of the PACs. Meanwhile, the impregnated alumina sol is favoring for the formation of spherical micro-pores, then further improves their mechanical and thermal insulation performances. The lowest thermal conductivity and highest crushing strength of resulting sample reach 0.16 W/m K and 29.2 MPa, respectively. This novel method offers new possibilities to fabricate high-quality PACs. [ABSTRACT FROM AUTHOR]

In order to reduce thermal conductivity but to exhibit better mechanical properties of porous alumina ceramics (PACs), a novel approach, based on the modification of pore structures (i.e. mean pore size, micro-pore proportions and pore shape factor) by impregnation of alumina sol, is reported in the present work. The properties of as-impregnated samples were compared with commercial alumina hollowsphere bricks. Results show that impregnation of alumina sol in PACs has a positive influence on pore structures, leading to a superior strength and a lower thermal conductivity. In particular, when 8 wt% alumina sol solid content is impregnated, the crushing strength (35.3 MPa) and thermal conductivity (0.15 W/m K at 200 °C) of sample are much better than that of the commercial alumina hollowsphere bricks. This novel method for excellent PACs provides promising applications as insulating lining materials in the fields of industrial furnace. [ABSTRACT FROM AUTHOR]