Search

In this paper, nanocrystalline Nd[(Zn0.925Co0.075)1/2Ti1/2]O3 (NZCT75) powders were synthesized through glycine–nitrate combustion method with the intent of reducing the sintering temperature and improving the microwave dielectric properties of NZCT75 ceramics. Phase composition, structure, and morphology of the powders were analyzed by thermogravimetric analysis–differential thermal analysis (TG–DTA), Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The XRD results showed that the as-synthesized powder after rapid self-propagating combustion was highly crystallized and was mainly composed of NZCT75 phase and small amount of unknown phase. The unknown phase could be vanished through the calcination process of 600 °C. Compared to solid-state reaction route, a reduction of about 600 °C in the synthesis temperature for pure phase NZCT75 was realized. A large amount of pores with inhomogeneous distribution in size and shape was found from the SEM image of the as-synthesized powder due to the rapid combustion reaction between glycine and nitrates. The TEM study revealed that the average particle size of the calcined powder is around 31.9 nm. The bulk sample prepared by the nanosized powder could be sintered to 98.8% of the theoretical density at 1250 °C, reducing about 160 °C more than the solid-state reaction method. Meanwhile, excellent microwave dielectric properties of NZCT75 ceramics presented a dielectric constant of 37.17, a quality factor of 257,600 GHz, and a temperature coefficient of resonant frequency of – 29.48 ppm/oC. This study develops a facile approach to synthesize nanocrystalline powder for a promising application in microwave dielectric ceramics. [ABSTRACT FROM AUTHOR]

We report a successful fabrication of 0.6Ca0.61Nd0.26TiO3–0.4Nd(Zn0.5Ti0.5)O3 (hereinafter abbreviated as 6CNT–4NCT) microwave ceramics with good sintering activity and desired dielectric properties from EDTA-gel combustion synthesized powders in this paper. The as-synthesized nanopowders have been characterized by X–ray diffraction (XRD), Fourier transformation infrared (FT–IR), scanning electron microscopy (SEM), and transmission electron microscopy (TEM) techniques, respectively. The sintering behavior and dielectric performance have been evaluated on the sintered ceramics. The as-obtained product with amorphous structure could be directly crystallized and produced pure 6CNT–4NCT solid solution phase with orthorhombic perovskite structure at a relatively low temperature of 700 °C, without formation of any intermediate phase. TEM images revealed that homogeneous and well dispersed spherical-shaped nanostructure with an average particle size of 23.8 nm was formed at 800 °C. Well-dense 6CNT–4NCT bulk ceramics with 98.8% relative density were obtained at a relatively low sintering temperature of 1225 °C due to high sintering activity of nanopowders. Moreover, the bulk ceramics exhibited a higher quality factor (Q × f) value than those prepared via the conventional solid-state reaction method. Desired microwave dielectric properties were achieved at 1200 °C: dielectric constant εr = 57.2, Q × f = 59,360 GHz, and temperature coefficient of resonant frequency τf = + 1.95 ppm/°C. This study indicates that the EDTA-gel combustion route is a convenient, low-cost, and interesting route to fabricate high-quality microwave ceramics for practical applications. [ABSTRACT FROM AUTHOR]