Nanocomposite scaffolds have been developed in order to achieve better mechanical and physiological properties in bone tissue engineering applications. In this study, reinforced poly (3-hydroxybutyrate) (PHB) composite scaffolds made with different weight ratios of nanobioglass (0, 2.5, 5, 7.5, and 10 wt%) and various porosities (70, 80 and 90 wt% of NaCl) were prepared by the salt leaching process. The scaffolds were placed in a PBS solution and their weight loss was measured. The biocompatibility of samples was examined in vitro using the MG63 cell line by indirect test, cell proliferation, and alkaline phosphatase (ALP) assays. Cell attachment on the surface of the scaffolds was observed by scanning electron microscopy (SEM). The biodegradation results showed that increasing the volume fraction of porosity and concentration of bioglass nanoparticles enhanced the weight loss of the scaffolds. The cell study demonstrated that a certain concentration of nanobioglass (7.5 wt%) in the scaffolds can significantly improve cell proliferation, inducing better osteoconductivity, compared to that of the pure PHB scaffolds and controls. In addition, the SEM results showed high cell attachment on these samples. All these factors indicate that samples with 7.5 wt% nanobioglass are a promising scaffold for bone tissue engineering.

One of the most important challenges in composite scaffolds is pore architecture. In this study, poly (3-hydroxybutyrate) with 10% bioglass nanoparticles was prepared by the salt leaching processing technique, as a nanocomposite scaffold. The scaffolds were characterized by SEM, FTIR and DTA. The SEM images demonstrated uniformed porosities of appropriate sizes (about 250-300 microm) which are interconnected. Furthermore, higher magnification SEM images showed that the scaffold possesses less agglomeration and has rough surfaces that may improve cell attachment. In addition, the FTIR and DTA results showed favorable interaction between polymer and bioglass nanoparticles which improved interfaces in the samples. Moreover, the porosity of the scaffold was assessed, and the results demonstrated that the scaffold has uniform and high porosity in its structure (about 84%). Finally it can be concluded that this scaffold has acceptable porosity and morphologic character paving the way for further studies to be conducted from the perspective of bone tissue engineering.