Mesoporous silicon microspheres were fabricated via in situ magnesiothermic reduction of silicon oxide. Scanning and transmission electron microscopy images indicate that the diameter of the mesoporous silicon microspheres is approximately 500 nm. Mesopores with diameters ranging from 10 to 30 nm are homogeneously distributed in the silicon microspheres. The as-prepared mesoporous silicon microspheres show a reversible capacity of 3000 mAh g at 100 mA g discharge current density. After 60 cycles, the mesoporous silicon microspheres can still deliver a 1500 mAh g capacity at 1000 mA g discharge current density. The high reversible capacity, excellent cycling, and good rate capability of the fabricated material can be attributed to its mesoporous morphology and ultrafine particle size. [ABSTRACT FROM AUTHOR]

Abstract: A MnO nanoparticle/graphene composite was prepared via in situ carbothermal reduction of Mn3O4 on the surface of graphene nanosheets. The formed MnO nanoparticles with diameters ranging from 20nm to 250nm integrated tightly with the graphene nanosheets. As anode material for lithium-ion batteries, the nanocomposite showed a high specific capacity of approximately 700mAhg−1 at 100mAg−1, excellent cyclic stability, and good rate capability. During the charge-discharge process, graphene nanosheets served as a three-dimensional conductive network for MnO nanoparticles. Furthermore, the detachment and agglomeration of MnO nanoparticles were effectively prevented due to the tight combination of MnO nanoparticles and graphene. [Copyright &y& Elsevier]