We present efficient red InGaN 60 × 60 μm2 micro-light-emitting diodes (μLEDs) with an epitaxial tunnel junction (TJ) contact. The TJ was grown by metal-organic chemical vapor deposition using selective area growth. The red TJ μLEDs show a uniform electroluminescence. At a low current density of 1 A/cm2, the emission peak wavelength is 623 nm with a full-width half maximum of 47 nm. The peak external quantum efficiency (EQE) measured in an integrating sphere is as high as 4.5%. These results suggest a significant progress in exploring high efficiency InGaN red μLEDs using TJ technology. [ABSTRACT FROM AUTHOR]

In this work, we demonstrate the detailed optimization of metalorganic chemical vapor deposition (MOCVD)-grown tunnel junctions (TJs) utilizing selective area growth (SAG) for regular size (0.1 mm2) and micro-size InGaN light-emitting diodes (LEDs and µLEDs). Finite-difference time-domain simulations show that the SAG apertures result in a more directional light emission of far-field radiation pattern for the SAG TJ LEDs grown on patterned sapphire substrate. Moreover, it is noted that the n-InGaN insertion layer and Si-doped concentration in the n+GaN TJs layer is essential to realize a low forward voltage (Vf) in TJs LEDs. For both 0.1 mm2 LEDs and µLEDs, the Vf is independent on the SAG aperture space varied from 3 to 8 µm when the Si-doping level in the n+GaN layer is as high as 1.7 × 1020 cm−3. The optimized TJ LEDs exhibit a comparable differential resistance of 1.0 × 10−2 Ω cm2 at 100 A cm−2 and a very small voltage penalty of 0.2–0.3 V compared to the conventional indium tin oxide contact LEDs. The low Vf penalty is caused by a higher turn on voltage, which is the smallest one among the MOCVD-grown TJs LEDs and comparable to the best molecular beam epitaxy-grown TJs LEDs. [ABSTRACT FROM AUTHOR]

High performance GaN-based micro-light-emitting diodes (µLEDs) with epitaxial n-InGaN/n-GaN tunnel junctions (InGaN TJs) were grown by metalorganic chemical vapor deposition (MOCVD). The InGaN TJs µLEDs show a significant reduction of forward voltage (Vf) by ∼0.6 V compared to the common TJs µLEDs. The Vf at 20 A cm−2 is very low varied from 3.15 V to 3.19 V in small InGaN TJ µLEDs with a size less than 40 × 40 µm2, and then significantly increases in large LEDs. Selective area growth (SAG) of TJs can overcome such size limitation by vertical out diffusion of hydrogen through the apertures on top of p-GaN. The InGaN TJ µLEDs overgrown by SAG show a size-independent low Vf ranged from 3.08 V to 3.25 V. The external quantum efficiency (EQE) of the packaged TJ µLEDs was improved by 6% compared to the common µLEDs with indium tin oxide (ITO) contact. This work solves the key challenges of MOCVD-grown TJs. [ABSTRACT FROM AUTHOR]