Search

The production of bleached cellulose pulps from elephant grass (Miscanthus sinensis) via a two-stage soda pulping process and a TCF bleaching sequence is evaluated in this work. The impregnation rapid steam pulping process (IRSP) involves impregnating of the lignocellulosic material with the pulping liquor, withdrawing the excess liquor and rapidly steaming the impregnated material at 180–200°C for a short time. In this paper the process variables and their effect on the kappa number, yield and viscosity of the unbleached pulps are discussed. Bleaching by an ozone-based TCF sequence was tested, and the papermaking properties of the bleached pulp were determined. A kappa number of 19 was obtained by impregnating at an alkali charge of 30 + 0.1% anthraquinone carboxylic acid (AQCA) and pulping at 180°C for only 15 min. Kappa was reduced to 16 by extending pulping time to 26 min. The alkali consumption during impregnation and pulping was 10.2 g NaOH/100 g of dry Miscanthus. Screened pulp yield, visc...

This paper explores the production of carboxymethylcellulose (CMC) fromseveral bleached cellulose pulps obtained from non-wood species. The chemicalcomposition (α-cellulose, hemicellulose and lignin content), the degreeofswelling, viscosity, solubility in concentrated NaOH and crystallinity ofsoda/AQ cellulose pulps from abaca, jute, sisal, linen and Miscanthussinensis were determined. The pulps were carboxymethylated by one andtwo successive reaction steps in aqueous medium under identical conditions. Thedegree of substitution (DS) of CMC was found to be dependent upon the source ofthe cellulose pulp, but generally it was close to 1 with one etherificationtreatment and around 2 after the second. The molar mass of CMC was found to bedependent on the initial intrinsic viscosity of the cellulose pulp. The weightaverage molar mass of our CMCs ranged from 1.5 × 105 to2.8 × 105. Increasing the DS up to 2 improved the CMC solubility, butviscosity slightly decreased due to a slight degradation of the polymer.

This paper concerns the rheological behavior of carboxymethylcelulloses(CMC) derived after one and two successive steps from different non-woodbleached cellulose pulps. CMC rheological characterization was achieved in0.1M NaCl solution, as a function of polymer concentration. Theevidence of a critical concentration (C* < 1 g/L) is discussedfromsteady shear and dynamic experiments. Rheological properties of the CMC werefound to depend on the cellulose source reactivity and on their degree ofsubstitution (DS). Higher molecular weight of initial cellulose was accompaniedby higher apparent intrinsic viscosity of the CMC produced. Depending on theCMCconcentration and on the degree of etherification, the system behaves as asolution or as a gel. In the case of abaca CMC sample, it is shown that afteronly one step of chemical modification and above a polymer concentration of20 g/L, the system behaves as a gel. The gel behavior was studied asafunction of temperature. In the temperature range from 25 to 45°C, the rheological behavior was found to remain almostconstant due to the existence of dispersed swollen aggregates. This unusualcharacteristic represents an advantage for applications such as oil recovery inthe petroleum industry, where viscosity of the recovered fluid should not diminishwith temperature.

Cellulose pulps were prepared from ground branch wood from pine and poplar and ground wheat straw by a fast soda/anthraquinone pulping. This process used high pulping temperatures and short residence times. Various combinations of temperature and time were used so that the H factor for pulps from pine and poplar was a constant 2700 while for pulps from wheat straw it was 270. The chemical composition of the resulting cellulose pulps was characterized and the possibility of synthesizing carboxymethyl cellulose from them was evaluated. The degree of substitution of our CMCs was found to be dependent upon the source of the lignocellullosic material, but independent of the pulping conditions for a specific substrate, (0.75 for pine, 0.82 for poplar and 0.89 for wheat straw). The rheological properties, the intrinsic viscosity and the molecular weight of the CMCs were found to be dependent on the pulping conditions for each lignocellulosic tested. The molecular weights of our CMC samples were 219,000 ...