Search

Novel, tough, strong, and self-healable polyacrylamide (PAAm) gels are fabricated by inducing an appropriate phase-separation structure using a poor solvent. The phase separation induces a gel-glass-like transition of the PAAm gels, providing the gels an anomalously high modulus (211 MPa), fracture stress (7.13 MPa), and fracture energy (4.16 x 10(4) J m(-2)), while keeping a high solvent content (approximate to 60 vol%).

A series of tough polyion complex hydrogels is synthesized by sequential homopolymerization of cationic and anionic monomers. Owing to the reversible interpolymer ionic bonding, the materials are self-healable under ambient conditions with the aid of saline solution. Furthermore, self-glued bulk hydrogels can be built from their microgels, which is promising for 3D/4D printing and the additive manufacturing of hydrogels.

Hydrogels attract great attention as biomaterials as a result of their soft and wet nature, similar to that of biological tissues. Recent inventions of several tough hydrogels show their potential as structural biomaterials, such as cartilage. Any given application, however, requires a combination of mechanical properties including stiffness, strength, toughness, damping, fatigue resistance and self-healing, along with biocompatibility. This combination is rarely realized. Here, we report that polyampholytes, polymers bearing randomly dispersed cationic and anionic repeat groups, form tough and viscoelastic hydrogels with multiple mechanical properties. The randomness makes ionic bonds of a wide distribution of strength. The strong bonds serve as permanent crosslinks, imparting elasticity, whereas the weak bonds reversibly break and re-form, dissipating energy. These physical hydrogels of supramolecular structure can be tuned to change multiple mechanical properties over wide ranges by using diverse ionic combinations. This polyampholyte approach is synthetically simple and dramatically increases the choice of tough hydrogels for applications.

Silicone rubber hollow fiber membrane produces an ideal gas exchange for long-term ECMO due to nonporous characteristics. The extracapillary type silicone rubber ECMO oxygenator having an ultrathin hollow fiber membrane was developed for pediatric application. The test modules were compared to conventional silicone coil-type ECMO modules. In vitro experiments demonstrated a higher O2 and CO2 transfer rate, lower blood flow resistance, and less hemolysis than the conventional silicone coil-type modules. This oxygenator was combined with the Gyro C1E3 centrifugal pump, and three ex vivo experiments were conducted to simulate pediatric V-A ECMO condition. Four day and 6 day experiments were conducted in cases 1 and 2, respectively. Case 3 was a long-term experiment up to 2 weeks. No plasma leakage and stable gas performances were achieved. The plasma free hemoglobin was maintained within a normal range. This compact pump-oxygenator system in conjunction with the Gyro C1E3 centrifugal pump has potential for a hybrid total ECMO system.

An experimental silicone hollow fiber membrane oxygenator for long-term extracorporeal membrane oxygenation (ECMO) was developed in our laboratory using an ultrathin silicone hollow fiber. However, the marginal gas transfer performances and a high-pressure drop in some cases were demonstrated in the initial models. In order to improve performance the following features were incorporated in the most recent oxygenator model: increasing the fiber length and total surface area, decreasing the packing density, and modifying the flow distributor. The aim of this study was to evaluate the gas transfer performances and biocompatibility of this newly improved model with in vitro experiments. According to the established method in our laboratory, in vitro studies were performed using fresh bovine blood. Gas transfer performance tests were performed at a blood flow rate of 0.5 to 6 L/min and a V/Q ratio (V = gas flow rate, Q = blood flow rate) of 2 and 3. Hemolysis tests were performed at a blood flow rate of 1 and 5 L/min. Blood pressure drop was also measured. At a blood flow rate of 1 L/min and V/Q = 3, the O2 and CO2 gas transfer rates were 72.45 +/- 1.24 and 39.87 +/- 2.92 ml/min, respectively. At a blood flow rate of 2 L/min and V/Q = 3, the O2 and CO2 gas transfer rates were 128.83 +/- 1.09 and 47.49 +/- 5.11 ml/min. Clearly, these data were superior to those obtained with previous models. As for the pressure drop and hemolytic performance, remarkable improvements were also demonstrated. These data indicate that this newly improved oxygenator is superior to the previous model and may be clinically acceptable for long-term ECMO application.

Based on the results of in vitro studies of many experimental models, a silicone hollow fiber membrane oxygenator for pediatric cardiopulmonary bypass (CPB) and extracorporeal membrane oxygenation (ECMO) was developed using an ultrathin silicone hollow fiber with a 300 microm outer diameter and a wall thickness of 50 microm. In this study, we evaluated the gas transfer performance of this oxygenator simulating pediatric CPB and ECMO conditions. Two ex vivo studies in a pediatric CPB condition for 6 h and 5 ex vivo studies in an ECMO condition for 1 week were performed with venoarterial bypass using healthy calves. At a blood flow rate of 2 L/min and V/Q = 4 (V = gas flow rate, Q = blood flow rate) (pediatric CPB condition), the O2 and CO2 gas transfer rates were maintained at 97.44 +/- 8.88 (mean +/- SD) and 43.59 +/- 15.75 ml/min/m2, respectively. At a blood flow rate of 1 L/min and V/Q = 4 (ECMO condition), the O2 and CO2 gas transfer rates were maintained at 56.15 +/- 8.49 and 42.47 +/- 9.22 ml/min/m2, respectively. These data suggest that this preclinical silicone membrane hollow fiber oxygenator may be acceptable for both pediatric CPB and long-term ECMO use.

One of the limitations of conventional silicone hollow fiber oxygenators compared with microporous membrane oxygenators is poor gas permeability. However, the silicone hollow fiber is free from plasma leakage, which is the major life limiting factor of the microporous membrane oxygenator. It has been difficult to fabricate a fine, thin hollow fiber for reduction of resistance to gas permeability because of the poor mechanical strength of conventional silicone materials. The authors developed a novel silicone material with sufficient mechanical strength, and a fine silicone hollow fiber with a diameter of 30 microns and wall thickness of 50 microns, which is approximately half that of a conventional silicone hollow fiber. Using this newly developed silicone hollow fiber, the authors developed a compact extracapillary flow membrane oxygenator. The oxygenator consists of fine silicone hollow fibers inserted in a housing made of polycarbonate. The housing is a cylindrical case, 20 cm long and 55 mm in inside diameter. The hollow fibers are cross-wound. The surface area of the membrane is 2.0 m2, and priming volume is 230 ml. Gas transfer performance of the newly developed oxygenator was evaluated by in vitro experiments. Oxygen and carbon dioxide transfer rates were 195 ml/min and 165 ml/min, at a blood flow rate 3 L/min. The novel silicone membrane oxygenator developed in this study can be used for extended duration in such applications as extracorporeal membrane oxygenation.

A silicone membrane hollow fiber oxygenator applicable for use as an extracorporeal membrane oxygenator (ECMO) has been developed in our laboratory. This silicone hollow fiber displays astonishing mechanical stability, is barely compressible or stretchable, and assembles easily while maintaining good gas permeability. The priming volume is 140 cc with a surface area of 0.8 m2. This study evaluated the gas transfer performances and biocompatibility of the oxygenator under ECMO and CPB conditions. In vitro studies that were performed at a blood flow rate of 2 L/min, and revealed O2 and CO2 gas transfer rates of 82.35 +/- 0.56 ml/m2/L/min and 38.72 +/- 2.88 ml/m2/L/min, respectively. The commercially available Kolobow (Avecor 1500) oxygenator was used as the control, and had O2 and CO2 gas transfer rates of 53.8 +/- 0.5 ml/m2/L/min and 24.7 +/- 2.0 ml/m2/L/min. To evaluate blood trauma, Normalized Index of Hemolysis (NIH) was measured according to American Society of Testing and Materials (ASTM) standards. The NIH findings were 0.0112 g/100L at a blood flow of 1 L/min, and 0.0152 g/100L at 5 L/min. Three ex vivo experiments, using a blood flow rate of 1 L/min, were performed with venoarterial bypass, and O2 transfer rate and CO2 transfer rate of the oxygenators were well maintained. This indicates that this preclinical silicone membrane hollow fiber oxygenator has superior efficiency, less blood trauma, and is smaller when compared with the only clinically available Kolobow oxygenator.

A new silicone hollow fiber membrane oxygenator for extracorporeal membrane oxygenation (ECMO) was developed using an ultrathin silicone hollow fiber, with a 300 microm outer diameter and a wall thickness of 50 microm. The hollow fibers were mechanically cross-wound on the flow distributor to achieve equal distribution of blood flow without changing the fiber shape. The housing, made of silicone coated acryl, was 236 mm long with an inner diameter of 60 mm. The surface area was 1.0 m2 for prototype 211, and 1.1 m2 for prototype 209. The silicone fiber length was 150 mm, and the silicone membrane packing density was 43% for prototype 211 and 36% for prototype 209. Prototype 211 has a priming volume of 208 ml, and prototype 209 has a priming volume of 228 ml. The prototype 211 oxygenator demonstrates a gas transfer rate of 120 +/- 5 ml/min (mean +/- SD) for O2 and 67 +/- 12 ml/min for CO2 under 2 L of blood flow and 4 L of O2 gas flow. Prototype 209 produced the same values. The blood side pressure drop was low compared with the silicone sheet oxygenator (Avecor, 1500ECMO). These results showed that this new oxygenator for ECMO had efficiency similar to the silicone sheet oxygenator that has a 50% larger surface area. These results suggest that the new generation oxygenator using an ultrathin silicone hollow fiber possesses sufficient gas transfer performance for long-term extracorporeal lung support.