Search

Composite biopolymer/conducting polymer scaffolds, such as polylactic acid (PLA)/ polyaniline (PAni) nanofibers, have emerged as popular alternative scaffolds in the electrical-sensitive nerve tissue engineering (TE). Although mimicking the extracellular matrix geometry, such scaffolds are highly hydrophobic and usually present an inhomogeneous morphology with massive beads that impede nerve cell-material interactions. Therefore, the present study launches an exclusive combinatorial strategy merging successive pre- and post-electrospinning plasma treatments to cope with these issues. Firstly, an atmospheric pressure plasma jet (APPJ) treatment was applied on PLA and PLA/PAni solutions prior to electrospinning, enhancing their viscosity and conductivity. These liquid property changes largely eliminated the beaded structures on the nanofibers, leading to uniform and nicely elongated fibers having average diameters between 170 and 230 nm. After electrospinning, the conceived scaffolds were subjected to a N2 dielectric barrier discharge (DBD) treatment, which significantly increased their surface wettability as illustrated by large decreases in water contact angles for values above 125° to values below 25°. X-ray photoelectron spectroscopy (XPS) analyses revealed that 3.3% of nitrogen was implanted on the nanofibers surface in the form of C–N and N–C=O functionalities upon DBD treatment. Finally, after seeding pheochromocytoma (PC-12) cells on the scaffolds, a greatly enhanced cell adhesion and a more dispersive cell distribution were detected on the DBD-treated samples. Interestingly, when the APPJ treatment was additionally performed, the extension of a high number of long neurites was spotted leading to the formation of a neuronal network between PC-12 cell clusters. In addition, the presence of conducting PAni in the scaffolds further promoted the behavior of PC-12 cells as illustrated by more than a 40% increase in the neurite density without any external electrical stimulation. As such, this work presents a new strategy combining different plasma-assisted biofabrication techniques of conducting nanofibers to create promising scaffolds for electrical-sensitive TE applications.

One of the leading causes of failure for any bone implant is implant-associated infections. The implant-bone interface is in fact the crucial site of infection where both the microorganisms and cells compete to populate the newly introduced implant surface. Most of the work dealing with this issue has focused on the design of implant coatings capable of preventing infection while ignoring cell proliferation or vice versa. The present study is therefore focused on investigating the antibacterial and biological properties of nanocomposite coatings based on an amorphous hydrocarbon (a-C:H) matrix containing silver nanoparticles (AgNPs). a-C:H coatings with varying silver concentrations were generated directly on medical grade titanium substrates using a combination of a gas aggregation source (GAS) and a plasma-enhanced chemical vapor deposition (PE-CVD) process. The obtained results revealed that the surface silver content increased from 1.3 at % to 5.3 at % by increasing the used DC magnetron current in the GAS from 200 to 500 mA. The in vitro antibacterial assays revealed that the nanocomposites with the highest number of silver content exhibited excellent antibacterial activities resulting in a 6-log reduction of Escherichia coli and a 4-log reduction of Staphylococcus aureus after 24 h of incubation. An MTT assay, fluorescence live/dead staining, and SEM microscopy observations of MC3T3 cells seeded on the uncoated and coated Ti substrates also showed that increasing the amount of AgNPs in the nanocomposites had no notable impact on their cytocompatibility, while improved cell proliferation was especially observed for the nanocomposites possessing a low amount of AgNPs. These controllable Ag/a-C:H nanocomposites on Ti substrates, which simultaneously provide an excellent antibacterial performance and good biocompatibility, could thus have promising applications in orthopedics and other biomedical implants.

Infection associated with titanium based implants remains the most serious problem in implant surgery hence it is important to find optimal strategies to prevent infections. In the present study, we investigated the surface properties, antibacterial activity and biocompatibility of nanocomposite coatings based on an amorphous hydrocarbon (a-C:H) film containing copper nanoparticles (CuNPs) deposited on Ti discs via a gas aggregation cluster source. Three different Cu/a-C:H coatings with approximately the same amount of embedded CuNPs with and without barrier a-C:H layer were fabricated. The obtained results revealed that different structures of the produced coatings have significantly different release rates of Cu ions from the coatings into the aqueous media. This subsequently influences the antibacterial efficiency and osteoblast cell viability of the treated coatings. Coatings with the highest number of CuNPs resulted in excellent antibacterial activity exhibiting approximately 4 log reduction of E.coli and S.aureus after 24 h incubation. The cytotoxicity study revealed that after 7 day cell seeding, even the coating with the highest Cu at.% (4 at.%) showed a cell viability of 90%. Consequently, the coating, formed with a properly tailored number of CuNPs and a-C:H barrier thickness offer a strong antibacterial effect without any harm to osteoblast cells.

Biocompatible BPA-PPD polyimide is widely used in the packaging of implantable devices. Plasma activation can improve its interaction with the surrounding tissue upon implantation. The influence of He, air, N2 and Ar plasma activation on polyimide's surface hydrophilicity, roughness, topography, composition and cell-surface interaction was evaluated, along with the influence of hydrophobic recovery on such properties. All plasma activations increased the surface hydrophilicity but neither the roughness nor topography changed. The increase was attributed to the incorporated O- and N-functionalities. 24 h after the activations the surface hydrophilicity decreased while maintaining the functionalities, due to the functionalities’ reorientation/migration towards the bulk of polyimide. Air and N2 activations improved the cell-surface interactions with fibroblasts. These were equally influenced by the surface hydrophilicity and the surface functionalities availability. The hydrophobic recovery lowered the initial cell adhesion but not the cell proliferation, as the hydrophobic recovery was progressively reversed in the culture media.