Search

This study investigated the strength behaviors of dredged clays treated with metakaolin (MK) and fly ash (FA). A series of laboratory tests including direct shear and unconfined compressive strength tests were performed on MK and FA-treated dredged clay at various MK contents and different curing times. The direct shear test results showed that the shear stress and displacement curves for all specimens tested are strain-softening types and influenced by MK content and curing time. The variation curve at a higher MK content or higher curing time is always higher than that at a lower one. The shear strength from the direct shear test at a given vertical stress consistently increases linearly with the increase of MK content while increasing parabolically with curing time. This indicates both curing time and MK content contribute to the development of the shear strength. Both strength parameters c and φ grow with increasing MK content and curing time. Unconfined compressive strength test results show the strain-softening behavior for all tested specimens. Compared with adding FA alone or MK alone, adding both fly ash and MK exhibited a better treatment effect in the unconfined compressive strength, which increases with increasing MK content and curing time. [ABSTRACT FROM AUTHOR]

This study experimentally investigated the strength characteristics of metakaolin (MK) and sodium silicate (SS) treated dredged clay at high water content for use as construction fills. A series of laboratory tests including direct shear tests, unconfined compression tests, SEM and XRD tests were carried out to systematically evaluate the effects of water content, sodium silicate modulus, curing agent content, and curing time on the strength behavior of MK and SS treated dredged clay samples. The direct shear test results showed that the shear strength at a given vertical stress consistently increases with the increase of curing agent content and curing time while decreasing with the modulus of SS. Both cohesion and friction angle increase with increasing curing agent content and curing time, while reducing with the increasing modulus of SS. Unconfined compression test results showed that all samples tested exhibit a strain-softening behavior. The value of unconfined compressive strength increases with the increase of curing agent content and curing time but decreases with the increase of water content and modulus of SS. The optimal dosage combination is a sodium silicate modulus of 0.9, curing agent content of 12%, and curing time of 28d. SEM test confirmed the formation of gels in the treated soil sample, the dredged clay showed a more uniform and denser microstructure after treatment. Through XRD analysis, it is not easy to generate direct chemical reactions with no new mineral components generated in the sample. For high-water content dredged clay, it is recommended to use an optimum dosage combination of MK and SS to achieve a better treatment effect for use as construction fills. [Display omitted] • The strength properties of MK and SS treated dredged clay sample were optimized. • The UCS of treated clay samples at different initial water contents were compared. • The microscopic mechanism of MK and SS treated dredged clay sample was revealed. [ABSTRACT FROM AUTHOR]