The current-induced spin-orbit torques (SOTs) in the perpendicularly magnetized Ir22Mn78/Co20Fe60B20/MgO structures are investigated. The damping- and field-like torques are characterized using a harmonic technique. The spin Hall angle of Ir22Mn78 is determined to be θSHE = +0.057 ± 0.002. The SOT-driven magnetization switching is also demonstrated with the assistance of an external in-plane field. Furthermore, the magneto-optical Kerr effect imaging experiments show that the magnetization switching is realized through domain nucleation and domain wall motion. These results may promise potential practical applications in high-performance SOT devices based on the antiferromagnetic materials. [ABSTRACT FROM AUTHOR]

We study the effect of the oxide layer on current-induced perpendicular magnetization switching properties in Hf|CoFeB|MgO and Hf|CoFeB|TaOx tri-layers. The studied structures exhibit broken in-plane inversion symmetry due to a wedged CoFeB layer, resulting in a field-like spin-orbit torque (SOT), which can be quantified by a perpendicular (out-of-plane) effective magnetic field. A clear difference in the magnitude of this effective magnetic field (HzFL) was observed between these two structures. In particular, while the current-driven deterministic perpendicular magnetic switching was observed at zero magnetic bias field in Hf|CoFeB|MgO, an external magnetic field is necessary to switch the CoFeB layer deterministically in Hf|CoFeB|TaOx. Based on the experimental results, the SOT magnitude (HzFL per current density) in Hf|CoFeB|MgO (-14.12Oe/107 A cm-2) was found to be almost 13× larger than that in Hf|CoFeB|TaOx (-1.05Oe/107 A cm-2). The CoFeB thickness dependence of the magnetic switching behavior, and the resulting HzFL generated by in-plane currents are also investigated in this work. [ABSTRACT FROM AUTHOR]