The surface modified hydrophilic zinc sulfide nano powder was prepared by hydrothermal method, and the corresponding zinc sulfide/polyurethane organic-inorganic composite transparent coating via in-situ polymerization. The structure of ZnS Nanoparticles and organic-inorganic composite coating were characterized by Infrared Spectroscopy, X-Ray Diffraction, Laser Particle Size Analyzer and Scanning Electron Microscopy. The optical properties were measured by Ultraviolet-Visible spectrophotometer and ellipsometry. The results show that the monodisperse hydrophilic nano zinc sulfide powder with a particle size of about 70 nm can be obtained by thioglycolic acid (TGA) modification, which has good compatibility with waterborne polyurethane. Nano zinc sulfide increased the refractive index of the coating significantly and the refractive index of the coatings could be controlled in the region of 1.46–1.71 organic-inorganic composite coating by adding ZnS. When the amount of nano ZnS added was 30%, the refractive index of the hybrid coating can reach 1.71, and the transmittance was more than 90%. The cured coatings were smooth and no agglomeration between nano ZnS particles could be found. After application on the surfaces of resin lens, the coatings presented better impact resistance, which indicated that the coating has application prospects in the field of fine processing of lens' surfaces. [ABSTRACT FROM AUTHOR]

The homogeneous SiO2-TiO2 composite sols were prepared by organic-inorganic synchronous polymerization with titanium isopropoxide and tetrabutyl silicate as precursor. The organic-inorganic composite hard coating with Si-O-Ti as the framework was prepared by adding compound crosslinkers (up-401) and 3-Methacryloxypropyltrimethoxysilane (KH-560). The structure of the coating and the hardened film were characterized by infrared spectrum, scanning electron microscopy, atomic force microscopy, particle size analyzer and thermogravimetry. The refractive index, transmittance and hardness of the hardened film were measured by ellipsometry, UV-Vis spectrophotometer and hardness tester. By adjusting the ratio of Si/Ti and optimizing the reaction conditions, the hardness of the hardened film could reach 6H, and the refractive index could be adjusted from 1.55 to 1.76. At the same time, the application of hard coatings on the surface of optical lens were studied. [ABSTRACT FROM AUTHOR]

In this work, the effect of modified graphene oxide and polytetrafluoroethylene (PTFE) on the tribological and anticorrosion properties of waterborne polyurethane (WPU) was studied. The modified graphene oxide (MGO) was obtained by the surface functionalization modification of graphene oxide (GO) with isophorone diisocyanate (IPDI), and MGO/WPU composite coating and MGO-PTFE/WPU composite coating with different mass fractions of MGO were prepared. The tribological and electrochemical experiment results demonstrated that the tribological properties of the coating and the corrosion resistance of the worn coating were effectively enhanced under the synergistic effect of MGO and PTFE. Finally, a mechanism was proposed to explain the improvement in anticorrosion performance of the worn coating. [ABSTRACT FROM AUTHOR]