1. Microstructure Evolution of near α Titanium Alloy during Multi-Step Thermomechanical Deformation Process
- Author
-
Bolong Li, Qing Shan Liu, Peng Qi, Zuo Ren Nie, Cong Cong Wang, and Tong Bo Wang
- Subjects
010302 applied physics ,Materials science ,Mechanical Engineering ,Titanium alloy ,02 engineering and technology ,Deformation (meteorology) ,021001 nanoscience & nanotechnology ,Condensed Matter Physics ,Microstructure ,01 natural sciences ,Mechanics of Materials ,Scientific method ,0103 physical sciences ,General Materials Science ,Composite material ,0210 nano-technology - Abstract
A new type of near α high temperature titanium alloy of Ti-Al-Sn-Zr-Mo-Si-Er was studied. The samples with different primary α phase content were prepared by solid solution at 950 °C/1 h—1010 °C/1 h. The multi-step hot compression experiments were carried out by Gleeble-3500 in a sequence of upper region of α + β phase, then followed by lower region of α + β phase. The effects of primary α phase content and deformation temperature on the microstructure of the alloy were studied by means of true stress-strain curve and optical microscope. The results show that the content of primary α phase gradually decreases from 45.4% at 950°C to 0% at 1010°C. As the deformation temperature decreases from 940°C to 900°C, the content of α phase increases gradually from 65% to 94%, which is changed from dynamic recrystallization to deformed structure elongated along RD direction. It is found that the arrangement of α phase along RD direction is the longest at 920°C. With the increase of the deformation temperature in the multi-step high temperature region from 970°C to 990°C, the width of deformed α phase decreases from 3.64 μm at 970°C to 2.71 μm at 990°C. The optimized microstructure is composed of 20% primary α phase arranged along RD direction. This process has a certain potential in the process of hot deformation of the alloy. Key words: high temperature titanium alloy, primary α phase, multi-step hot deformation
- Published
- 2021
- Full Text
- View/download PDF