Search

Purpose The purpose of this paper is to investigate effects of layer thickness on densification, surface morphology, microstructure and mechanical and corrosion properties of 420 stainless steel fabricated by laser-powder bed fusion (L-PBF). Design/methodology/approach Standard specimens were printed at layer thickness of 10, 20 and 30 µm to characterize Archimedes density, surface roughness, tensile strength, elongation, hardness, microstructural phases and corrosion performance in the as-printed and heat-treated condition. Findings Archimedes density slightly increased from 7.67 ± 0.02 to 7.70 ± 0.02g/cm3 and notably decreased to 7.35 ± 0.05 g/cm3 as the layer thickness was changed from 20 µm to 10 and 30 µm, respectively. The sensitivity to layer thickness variation was also evident in properties, the ultimate tensile strength of as-printed parts increased from 1050 ± 25 MPa to 1130 ± 35 MPa and decreased to 760 ± 35 MPa, elongation increased from 2.5 ± 0.2% to 2.8 ± 0.3% and decreased to 1.5 ± 0.2, and hardness increased from 55 ± 1 HRC to 57 ± 1 HRC and decreased to 51 ± 1 HRC, respectively. Following heat treatment, the ultimate tensile strength and elongation improved but the general trends of effects of layer thickness remained the same. Practical implications Properties obtained by L-PBF are superior to reported properties of 420 stainless steel fabricated by metal injection molding and comparable to wrought properties. Originality/value This study successfully the sensitivity of mechanical and corrosion properties of the as-printed and heat-treated parts to not only physical density but also microstructure (martensite content and tempering), as a result of changing the layer thickness. This manuscript also demonstrates porosity evolution as a combination of reduced energy flux and lower packing density for parts processed at an increasing layer thickness.

In this study, we report the mechanical properties, microstructure and corrosion behavior 99+ % dense 420 stainless steel parts fabricated by laser-powder bed fusion (L-PBF). As-printed L-PBF parts exhibited an ultimate tensile strength of 1050 ± 25 MPa, yield strength of 700 ± 15 MPa, an elongation of 2.5 ± 0.2% and a hardness of HRC 55 ± 1. After the heat treatment operation at 315 °C, the ultimate tensile strength improved significantly to 1520 ± 30 MPa, yield strength increased to 950 ± 20 MPa, and elongation increased to 6.3 ± 0.2% respectively whereas hardness remained at HRC 53 ± 1. These properties are higher than previously reported literature values for 420 stainless steel fabricated by L-PBF, metal injection molding and powder metallurgy routes. The microstructure indicated a mixture of martensite and retained austenite phases in the as-printed parts. After heat treatment, the microstructure was richer in tempered martensitic laths that is consistent with the enhancement of ultimate tensile strength, yield strength, and elongation without appreciable change in hardness. The corrosion behavior of the as-printed L-PBF parts exhibited a corrosion current of 2.85 ± 0.4 mA.cm−2, a polarization resistance of 17,100 ± 520 Ω.cm−2 and a corrosion rate of 28 ± 2 μm/year which were comparable to the corrosion properties of wrought 420 stainless steel. A significant increase in pitting potential (170 mV) was obtained after the heat treatment.

The effects of powder characteristics (powder shape, size and type) and processing conditions (laser power and scanning speed) on the mechanical properties and microstructures of laser powder bed fusion (L-PBF) 17-4 PH stainless steel were studied using four types of powders. The % theoretical density, ultimate tensile strength, hardness of L-PBF parts are sensitive to energy density and starting powder shape, size and type. The density and mechanical properties of both water and gas-atomized powders increased with increased energy density. The gas-atomized (D50 = 13 μm) powders which are spherical in shape and water-atomized (D50 = 17 μm) powders of high tap density produced low-porosity and high-density (~97% density) L-PBF parts at low energy densities of 64 and 80 J/mm3. The increase in energy density to 104 J/mm3 resulted in high dense (97 ± 0.5%) water- and gas-atomized powders L-PBF parts. However, even at a high % theoretical density (97 ± 1%), the properties of L-PBF parts varied over a relatively large range (UTS: 500–1100 MPa; hardness: 25–39 HRC; elongation: 10–25%). This large variation in mechanical properties could be attributed the martensite and austenite phase as well as grain size in the L-PBF parts. Furthermore, the martensite and austenite phase content and of the L-PBF parts were also sensitive to the energy density and starting powder type.

In the present work, the friction and wear properties of Polypropylene (PP) based composites filled with Hydroxyapatite (HA) particles were studied. Fillers contents in the PP were 10, 20, and 30 wt%. The effects of hydroxyapatite ratio on the water absorption, friction and wear properties of the polymer composites is presented. The result showed that the addition of HA to the composite changed the water absorption, friction coefficient and wear rate.

WOS: 000510612100009 This study investigates the effects of addition of Carbon nanotube (CNT) at different volume ratios (0.5- 5%) into Ti6Al4V matrix by mechanical alloying in terms of the density, microstructure, hardness and creep under dynamic load. As a result of the good bonding of carbon nanotubes powders with the main matrix, Ti-6Al-4V/CNT composites have experienced change both in microstructure and mechanical properties (such as hardness, density) and, correspondingly, qualitatively creep behaviour of Ti-6Al-4V matrix alloy has been improved compared to the lean one. The density of CNT reinforced Ti6Al4V composites sintered at 1300 degrees C for 3h decreases with increasing CNT content. The hardness tests indicated that the hardness of composites increased with CNT addition. In addition, although creep strain is decreased continually with CNT content until 5%, creep life increased with increasing CNT content until 4% of CNT but decreased above 4%. After sintering at 1300 degrees C under vacuum for 3 hours the density of the composite material reached to a level of 98.5 %, the microhardness to 538 HV and the creep behaviour was improved. The characterization of Ti6Al4V/CNT composites after mechanical alloying was carried out using scanning electron microscopy (SEM), energy dispersive x-rays spectroscopy (EDS) analysis and X-ray diffraction (XRD) methods. Although Ti-6Al-4V alloys are used as biomaterial, this study aimed at using MWCNTs containing Ti-6Al-4V composites at high temperature applications. Because MWCNTs reinforced Ti-6Al-4V composites are cheaper and have lower weight than the other materials used in this kind of applications. Scientific Research Project Program of Marmara UniversityMarmara University [FEN-K-070317-0107] This work was supported by the Scientific Research Project Program of Marmara University (FEN-K-070317-0107).