Search

How the membrane support affects the performance of thin-film composite (TFC) membranes has long been under debate. Our present study experimentally establishes that the support pore number density (number per unit area) as well as its surface porosity play pivotal roles in affecting the characteristics and permselectivity of TFC membranes. The structure of hollow fiber supports was finely tuned and characterized via a series of techniques, which provided a link to the physicochemical properties of the interfacially polymerized polyamide films. During the spinning process, decreasing the content of N -methyl-2-pyrrolidone in the bore fluid drastically reduced the pore size and surface porosity of the support. The resultant TFC membranes showed a lower water permeability (tested under 1 bar using 500 ppm NaCl). Adding lithium chloride to the polymer dope also led to a support with smaller pores and lower porosity, but increased surface pore number density. The resulting TFC membranes had a substantially higher water permeability and slightly higher salt rejection. In both arrays of membranes, all membranes shared similar thickness of polyamide leaf but a more crumpled film was found on a less porous support, suggesting that the surface porosity of the support affected the effective surface area of films. However, the TFC membrane with a higher effective surface area did not necessarily possess a higher permeability. Rather, a TFC membrane having a support with a higher surface porosity or a higher pore number density exhibited a higher water permeability, demonstrating that the lateral transport path of water through films had a significant impact on the water permeability of TFC membranes. Interestingly, in both cases, the selectivity of the TFC membranes was maintained when the water permeability increased. This study clarifies longstanding misunderstandings concerning the effects of the support on TFC membrane performance and provides insight into fabricating highly permeable and selective TFC membranes. • A base film embedded in the polyamide layer determines performance of TFC membranes. • Enlarging surface porosity of supports could enhance permeability of TFC membranes. • Increasing pore density of supports could enhance permeability of TFC membranes. • Supports affect lateral diffusion of water through films and thereby permeability. • Rejection was maintained while the permeability of TFC was drastically enhanced. [ABSTRACT FROM AUTHOR]

A scaled-up hollow fibre thin-film composite (TFC) module was successfully developed for organic solvent forward osmosis (OSFO) application in the pharmaceutical industry. The membrane consists of cross-linked P84 polyimide substrate with a polyamide selective layer, formed via interfacial polymerisation. The performance of the lab-scale module was compared to the scaled-up module in reverse osmosis and forward osmosis modes. The results from both tests revealed that the solvent permeability of the scaled-up module decreased while its selectivity increased slightly. This might be caused by the uneven distribution of liquids during interfacial polymerisation, leading to varied membrane performance. The scaled-up module was further tested for OSFO performance using a range of PEG-400 concentrations (0.5–2 M) in acetone and isopropanol as draw solutions. At 2 M PEG-400 concentration, the module demonstrated high isopropanol and acetone permeability of 0.63 LMH and 13.9 LMH, respectively. Moreover, the reverse solute flux of PEG-400 in acetone and isopropanol were relatively low at 0.188 g/l and 0.153 g/l, respectively. The module was further tested for OSFO application in the pharmaceutical industry by concentrating levofloxacin in acetone, using 2 M PEG-400 as draw solution. The process was able to concentrate levofloxacin from 1000 ppm to 16,000 ppm with very low reverse solute flux of 0.178 g/l. Therefore, this work presents a scalable TFC membrane for OSFO application in the pharmaceutical industry. [Display omitted] • Scaled-up module (0.4 m2) of TFC hollow fibre membrane for organic solvent forward osmosis process was successfully fabricated. • High porosity (79%) and low structural parameter (217 μm) for membrane substrate was achieved. • Membrane exhibited excellent acetone and IPA solvent flux of 13.9 LMH and 0.63 LMH, respectively, using a 2 M PEG-400 draw solution. • A pharmaceutical stream was concentrated to a factor of 16 with low specific reverse solute flux [ABSTRACT FROM AUTHOR]

A scaled-up hollow fibre thin-film composite (TFC) module was successfully developed for organic solvent forward osmosis (OSFO) application in the pharmaceutical industry. The membrane consists of cross-linked P84 polyimide substrate with a polyamide selective layer, formed via interfacial polymerisation. The performance of the lab-scale module was compared to the scaled-up module in reverse osmosis and forward osmosis modes. The results from both tests revealed that the solvent permeability of the scaled-up module decreased while its selectivity increased slightly. This might be caused by the uneven distribution of liquids during interfacial polymerisation, leading to varied membrane performance. The scaled-up module was further tested for OSFO performance using a range of PEG-400 concentrations (0.5–2 M) in acetone and isopropanol as draw solutions. At 2 M PEG-400 concentration, the module demonstrated high isopropanol and acetone permeability of 0.63 LMH and 13.9 LMH, respectively. Moreover, the reverse solute flux of PEG-400 in acetone and isopropanol were relatively low at 0.188 g/l and 0.153 g/l, respectively. The module was further tested for OSFO application in the pharmaceutical industry by concentrating levofloxacin in acetone, using 2 M PEG-400 as draw solution. The process was able to concentrate levofloxacin from 1000 ppm to 16,000 ppm with very low reverse solute flux of 0.178 g/l. Therefore, this work presents a scalable TFC membrane for OSFO application in the pharmaceutical industry. [Display omitted] • Scaled-up module (0.4 m2) of TFC hollow fibre membrane for organic solvent forward osmosis process was successfully fabricated. • High porosity (79%) and low structural parameter (217 μm) for membrane substrate was achieved. • Membrane exhibited excellent acetone and IPA solvent flux of 13.9 LMH and 0.63 LMH, respectively, using a 2 M PEG-400 draw solution. • A pharmaceutical stream was concentrated to a factor of 16 with low specific reverse solute flux [ABSTRACT FROM AUTHOR]

Polyamide thin film membranes have shown outstanding performance in organic solvent nanofiltration (OSN). However, it is still challenging to produce polyamide hollow fibres for OSN, mainly due to limited solvent resistance of hollow fibre substrates and the difficulty to synthesize polyamide thin film on the surface of hollow fibre substrates. In this study, polyamide-based hollow fibre composite members for low pressure OSN were successfully developed. Solvent resistant polyimide hollow fibre substrates were first prepared through a non-solvent induced phase separation process, followed by chemical cross-linking with hexamethylene diamine. A polyamide thin film layer was then synthesized via interfacial polymerization, by circulating the reactant monomers including polyethyleneimine (PEI), piperazine (PIP) and trimesoyl chloride (TMC) through the hollow fibre lumen. The polyamide thin film with a thickness of ~60 nm was formed on the inner surface of the hollow fibre substrates. The membranes exhibited excellent nanofiltration (NF) performance under 2 bar operating pressure. The permeability of water, acetone and isopropanol was 6.8, 11.6 and 4.5 l m−2 h−1 bar−1, respectively. The membranes also achieved 99.9% and 91.8% rejection to rose bengal (1017 Da) and acid fuchsin (585 Da), respectively, in acetone. Furthermore, a 72-h filtration test was conducted and the membrane showed steady performance throughout the testing period. This study demonstrates the possibility of fabricating polyamide hollow fibre membranes for organic solvent nanofiltration at low pressure, which is desirable for practical applications. • Solvent resistant polyimide hollow fibre membranes were fabricated through chemical cross-linking. • Polyamide-based (PEI/PIP) layer was formed onto polyimide substrate to obtain a relatively loose selective layer. • Membranes achieved 11.6 and 4.5 l m−2 h−1 bar−1 permeability in acetone and isopropanol at 2 bar respectively. • Membranes maintained more than 90% rejection for acid fuchsin in 72-h filtration test, showing stable OSN performance. [ABSTRACT FROM AUTHOR]