Search

The use of a provisional restoration is an important phase in the treatment of the dental prosthetic patient. A good provisional restoration should satisfy the following requirements: pulpal protection, positional stability, ease in cleaning, accurate margins, wear resistance, dimensional stability, and serve as a diagnostic aid in treatment assessment and esthetics. There is a tendency for discoloration, occlusal wear, and fracture that eventually leads to unnecessary repair. Heat-processed and reinforced methacrylate-based resins have been used to improve the mechanical and physical properties of provisional restorations. Among various improvements, the interpenetrating network crosslinked PMMA (IPN) has been shown to have superior mechanical properties if manufactured through a dough compression molding process at 130 degrees C. However, there have been no published data that relate with the use of this material for fixed provisional restorations. The objective of this study was to compare four methyl methacrylate-based resins for provisional crowns and bridges with varying processing cycles, including JET [self-cure], ACRALON [heat-cured], titanium dioxide filled PMMA [heat-cured], and IPN [heat-cured denture tooth resin]. Properties studied included transverse strength, toughness, rigidity, and hardness. From the results of this study the following conclusions can be made: the IPN group may have had a lower degree of conversion as demonstrated by decreased strength, toughness, and hardness data as compared with Acralon. Increasing the polymerization cycle of unmodified Acralon resin causes a significant increase in strength.

Acrylic resins have been used in many different applications in dentistry, especially in the fabrication of provisional fixed partial dentures. Ideally, a provisional crown and bridge material should be easy to handle and should protect teeth against physical, chemical, and thermal injuries. Some of the problems associated with this use are related to the material's poor mechanical properties. It has been demonstrated that acrylic resin can be strengthened through the addition of structural component of different size distributed in the acrylic matrix, thus forming a composite structure. The purpose of this study was to investigate the addition effects of mixtures of titania (titanium dioxide, TiO(2)) powder and zirconia (zirconium dioxide, ZrO(2)) powder being incorporated with pre-polymerized beads mixed in monomer liquid, on some mechanical and physical properties of PMMA resin. The pre-polymerized powder poly(methyl methacrylate) resin was admixed with titania and zirconia powder. A mixing ratio was controlled by volume % of 0, 1.0, 2.0, and 3.0 (samples with 0 v/o served as control groups). For using mixture of titania and zirconia, total amount of the mixture was controlled by volume % of 1.0, 2.0, and 3.0, in which titania and zirconia were mixed at the ratio 1 :1, 1 :2 and 2 :1. Prior to mechanical tests, all rectangular-shaped samples (25 mm x 2 mm x 5 mm) were stored in 37 degrees C distilled water for 7 days after polishing all six sides of samples. Samples were then subjected to the three-point bending flexion test to evaluate the bending strength as well as the modulus of elasticity. Weight gain and exothermic reaction survey were investigated as well. All data were collected and analyzed with one-way analysis of variance (ANOVA) and Sidak method (p=0.05). It was found that the addition of particles generally decreased the water absorbed by the composite system. Only 1 percent by volume concentration of 1 :1 ratio and 2 percent by volume concentration of 1 :2 and 2 :1 ratios had significantly higher strength than control group. There was significantly higher toughness (in terms of energy-to-break) for 1 percent by volume concentration of 1 :1 ratio and 2 percent by volume concentration of 2 :1 ratio than control group. There was no significant difference between control group and all percent by volume combinations in modulus of elasticity. In addition, there was no significant variations of exothermic reaction.

This study investigated the effect of marginal gap width, luting cement, and restorative material on the wear resistance of the luting cement in areas where no occlusal contact is present. Three types of resin luting cement and one resin-modified glass-ionomer cement were used with two inlay systems, a resin composite, and an all-ceramic system. Bovine enamel represented tooth structure. Toothbrush abrasion was the wear modality. Three predetermined gap widths were selected: 240 +/- 30 microns, 150 +/- 30 microns, and 60 +/- 30 microns. All specimens were thermocycled. Regardless of the luting cement or the restorative material, there was a significant difference (P < 0.05) in wear resistance of the cement among the three gap distances at both the enamel and restoration interface. Vertical wear of the luting cement at the enamel interface increased linearly with marginal gap distance when all four cements were considered together (r2 > 0.51), regardless of type of restorative material used. The resin-modified glass-ionomer cement showed the least amount of wear for all variables considered. Significant differences in wear were found between the four luting cements at wide gap distances (240 microns) at the enamel interface, regardless of type of restorative material used. No significant differences were found between the two restorative materials at the enamel interface at the three gap distances.

Four acrylic resins and two composite resins for fabricating provisional fixed prosthodontic restorations were studied to determine temperature change during polymerization, surface hardness, marginal fit, wear resistance, transverse strength, transverse repair strength, surface roughness and polishability, color stability, and stain resistance. While certain materials exhibited advantageous properties in one or more of the tests, no one material was superior to the others in all tests.