Search

Contact experiments between low‐reactivity CaO–BaO–Al2O3‐based mold fluxes, F1 and F2, and 1.4–2.2 mass% of Al‐containing steels are conducted to investigate the effect of interfacial reaction on mold flux properties and the ultimate limit of reaction duration capacity of the developed mold flux. F1 contains 30.76% CaO, 17.03% Al2O3, 13.40% BaO, and 10.70% SiO2, whereas F2 consists of 27.90% CaO, 23.60% Al2O3, 12.90% BaO, and 9.57% SiO2 of the mass. The pre‐ and post‐experimental wettability of slag samples on steel substrates and the lubrication behavior of slags are discussed. The main results reveal that SiO2, Na2O, and B2O3 in the mold flux react with [Al] in the molten steel at steel–slag interface. The variations in slag properties indicate that both reaction durations between F1 reacting with twinning‐induced plasticity (TWIP) and F2 reacting with 20Mn23AlV steel can last for 40 min, whereas F2 has wider potential applicability for the continuous casting of Al‐containing steels. Interfacial reaction deteriorates the wettability of slag F2 on 20Mn23AlV steel substrate and reduces slag consumption, as equilibrium contact angle increases from approximately 3° to 37°, but slag consumption prediction is 0.22 kg m−2, which is likely to meet the requirement for lubrication. [ABSTRACT FROM AUTHOR]

To control heat transfer between the solidifying shell and the water-cooled mold during continuous casting, the transition metal oxides, ZrO2, Y2O3, and Sc2O3, were separately added into the developed low-reactive CaO-Al2O3-based mold slags to investigate the effect on radiation heat transfer. Two kinds of master mold slags were taken into account, one included 18 pct Al2O3 and 18 pct SiO2, and the other one included 28 pct Al2O3 and 8 pct SiO2. The slag viscosity and melting temperature were measured with rotating cylinder viscometer and hemisphere-point method, respectively. The optical parameters of the slag films having different contents of transition metal oxides were measured by Fourier transform infrared spectrometer, and an optical-process model was constructed to consider the radiation from the shell surface and hot and cold sides of the solid films to the mold plate. When ZrO2, Y2O3, and Sc2O3 contents up to 4 pct, the viscosity at 1573 K fluctuated in the range of 0.05 Pa s, the melting temperature varied within a range of 15 K, except for the case of 2 pct Sc2O3, for which the melting temperature was 27 K lower than that of the master mold slag with 8 pct SiO2 and 28 pct Al2O3. The incorporation of the three transition metal oxides up to 4 pct did not have a notable effect on the viscosity or melting temperature. The addition of ZrO2 and Y2O3 effectively decreased the radiation, whereas Sc2O3 had no direct relationship with radiation. When the ZrO2 (Y2O3) concentration was increased from 0 to 4 pct, the reduction rate of radiation transfer was 26.6 pct (13.3 pct) for the mold slag containing 18 pct Al2O3 and 18 pct SiO2. The current study provides a new direction for developing low-reactive mold slag and reducing heat transfer during continuous casting. [ABSTRACT FROM AUTHOR]

To moderate the erosion in a slag-line zone and extend the service life of a submerged entry nozzle during continuous casting of high-Mn and high-Al steel, the current study developed a low-reaction CaO-Al2O3-based slag with lower SiO2 and higher Al2O3 contents than that of conventional CaO-SiO2-based slag. The static sessile drop technique and dynamic rotating cylinder method were utilized to investigate the erosion behavior of ZrO2-graphite refractory by the above slags. The main results indicated that silicate-based slag could wet the ZrO2-graphite substrate completely, while the aluminate-based slag spread rapidly in the first 20 minutes, and then a slag drop with an unchanged profile formed on the substrate. The equilibrium contact angles with the substrate at 1623 K were 0 and 79 deg for the CaO-SiO2 and CaO-Al2O3 based slags, respectively. The comparison of the influences of the rotating speed and the temperature revealed that the decrease of erosion rate could be realized by the developed slag. An examination of ZrO2-saturation limit also indicated that the low-reaction slag could dissolve much more ZrO2 oxidation, accompanied by a less-negative effect on the viscosity of the molten slag. [ABSTRACT FROM AUTHOR]