Deterioration assessment of materials is essential to the continued effective operation of critical components in thermal power plants. Establishing the degree of creep exhaustion of power engineering alloys operating at high temperatures and stresses guides maintenance strategies to ensure reliable plant operation. Within progressive inspection philosophies, traditional laboratory‐based creep testing is often difficult to conduct on ex‐service steel due to the limited material availability from which to machine standard specimen geometries. This work investigates a technique for the measurement of creep strain curves at several stresses and at 600°C from a single test using a nontraditional specimen geometry together with full‐field strain measurement through digital image correlation (DIC). Of interest is ex‐service X20CrMoV12‐1 (X20) which is widely used in older, subcritical thermal power plants. The paper aims to show that multiple creep curves can be resolved over a spatially varying stress field using DIC whilst preserving material economy. Differences in creep behaviour between ex‐service X20 with varying levels of service exposure are evident from quantitative comparisons of the creep strain and rate curves through threshold stress computation which agrees with hardness measurements and microstructural observation of subgrains and precipitates using electron microscopy. These single‐specimen tests yield high densities of creep data which can be used in the calibration of creep damage models for characterisation of ex‐service X20. [ABSTRACT FROM AUTHOR]

The lifetime of steam pipelines in long-term operation in coal-fired power plants are limited due to material damage that resulted from creep exposure. In the present study, the authors comparatively assess the damage of ex-service 12% Cr piping steel with varying degrees of exposure while using accelerated creep tests that employ digital image correlation (DIC) as well as microstructural investigation that is based on electron microscopy. The DIC technique, which allows multiple creep curves to be measured at temperatures ranging from 550–600 °C from a single specimen, revealed higher Zener–Hollomon parameters for a high damage material with a high void density when compared to a material with lower damage and lower void density. Both of the material states showed similar hardness values, subgrain sizes, and boundary character, despite the difference in void densities. Slightly higher inter-particle spacing of MX precipitates results in a lower threshold stress of 79 MPa for the high damage steel when compared to 97 MPa for the low damage material. Besides large Laves phase particles (>0.2 µm) that are found in the higher damaged materials that result in solid solution depletion, the most prominent microstructural damage indicator was a lower density of M23C6 precipitates. Therefore, the observations indicate that the Zener–Hollomon parameter and M23C6 particles are good damage assessment indicators between the most extreme damage states and they predict a lower damage level for a medium void density material. [ABSTRACT FROM AUTHOR]