Search

To determine how grain-boundary composition affects the liquid phase sintering of MgO-free Bayer process aluminas, samples were singly or co-doped with up to 1029 ppm Na2O and 603 ppm SiO2 and heated at 1525°C up to 8 h. Na2O retards densification of samples from the onset of sintering and up to hold times of 30 min at 1525°C compared to the undoped samples, but similar to the as-received, MgO-free Al2O3, Na2O-doped samples sinter to 98% density with average grain sizes of ~3 μm after 8 h. Increasing SiO2 concentration significantly retards densification at all hold times up to 8 h. The estimated viscosities (20−400 Pa·s) of the 0.3 to 1.8 nm thick siliceous grain-boundary films in this study indicate that diffusion greatly depends on the composition of the liquid grain-boundary phase. For low Na2O/SiO2 ratios, densification of Bayer Al2O3 at 1525°C is controlled by diffusion of Al3+ through the grain-boundary liquid, whereas for high Na2O/SiO2 ratios, densification can be governed by either the interface reaction (i.e., dissolution) of Al2O3 or diffusion of Al3+. Increasing Na2O in SiO2-doped samples increases diffusion of Al3+ and Al2O3 solubility in the liquid, and thus densification increases by 1%. Based on these findings, we conclude that Bayer Al2O3 densification can be manipulated by adjusting the Na2O to SiO2 ratio. [ABSTRACT FROM AUTHOR]

To determine how grain-boundary composition affects the liquid phase sintering of MgO-free Bayer process aluminas, samples were singly or co-doped with up to 1029 ppm Na2O and 603 ppm SiO2 and heated at 1525°C up to 8 h. Na2O retards densification of samples from the onset of sintering and up to hold times of 30 min at 1525°C compared to the undoped samples, but similar to the as-received, MgO-free Al2O3, Na2O-doped samples sinter to 98% density with average grain sizes of ~3 μm after 8 h. Increasing SiO2 concentration significantly retards densification at all hold times up to 8 h. The estimated viscosities (20−400 Pa·s) of the 0.3 to 1.8 nm thick siliceous grain-boundary films in this study indicate that diffusion greatly depends on the composition of the liquid grain-boundary phase. For low Na2O/SiO2 ratios, densification of Bayer Al2O3 at 1525°C is controlled by diffusion of Al3+ through the grain-boundary liquid, whereas for high Na2O/SiO2 ratios, densification can be governed by either the interface reaction (i.e., dissolution) of Al2O3 or diffusion of Al3+. Increasing Na2O in SiO2-doped samples increases diffusion of Al3+ and Al2O3 solubility in the liquid, and thus densification increases by 1%. Based on these findings, we conclude that Bayer Al2O3 densification can be manipulated by adjusting the Na2O to SiO2 ratio. [ABSTRACT FROM AUTHOR]

This paper examines the influence of SiO2 doping on densification and microstructure evolution in Nd3xY3-3xAl5O12 (Nd:YAG) ceramics. Nd:YAG powders were doped with 0.035-0.28 wt% SiO2 and vacuum sintered between 1484° and 1750°C. 29Si magic-angle spinning nuclear magnetic resonance showed that Si41 substitutes onto tetrahedrally coordinated Al3+ sites. High-resolution transmission electron microscopy showed no grain boundary second phases for all silica levels in samples sintered at 1600°-1750°C. Coarsening was limited by a solute drag mechanism as suggested by cubic grain growth kinetics and transmission electron microscopy energy-dispersive X-ray spectroscopy observations of increased Nd31 concentration near grain boundaries. Increasing SiO2 content increased both densification and grain growth rate and led to increasingly coarsening-dominated sintering trajectories. Fine-grained (< 3 μm), highly transparent (> 82% real in-line transmission) ceramics were produced by sintering 0.035 wt% SiO2-doped ceramics at 1750°C for 8 h. Coarse-grained (18 μm), transparent samples were obtained with 0.28 wt%SiO2-doped Nd:YAG when sintered at 1600°C for 8 h. [ABSTRACT FROM AUTHOR]