Abstract: Rare-earth-doping and various post-growth heat treatments effects on OH− absorption in singly Er- and Yb-doped, doubly Er/Mg- and Er/Yb-doped LiNbO3 crystals have been investigated. The OH− absorption in the rare-earth-doped crystals shows definite anisotropy and is stronger in a Z-cut plate. Rare-earth-doping causes considerable OH− absorption reduction. MgO-codoping induces additional reduction. Slight/heavy rare-earth-doping causes slight/considerable spectral shape change. Thermal reduction treatment causes OH− absorption vanishing whether the crystal is originally congruent or near-stoichiometric. Further oxidation treatment renders the absorption reemerged. Li-rich vapor transport equilibration (VTE) treatment causes significant absorption decrease. For a slightly rare-earth-doped Li-rich VTE-treated crystal, its spectral feature is similar to that of the undoped near-stoichiometric crystal; for a heavily rare-earth-doped VTE-treated crystal, its spectral shape preserves the feature of the heavily rare-earth-doped as-grown crystal. For the Er/Mg-codoped crystal studied, the Li-rich VTE also induces an abrupt conversion of peaking position from 3483 cm−1 to 3535 cm−1. The absorption in the Li-rich VTE-treated crystals also reveals aging effects in spectral shape, peaking position and absorption intensity. Li-poor VTE induces significant absorption increase. In addition, the effect of OH− presence on lifetime of Er3+ emission at 1.5 μm was also studied. The results show that the effect is small for the as-grown congruent crystals and slight for Li-rich VTE-treated ones. [Copyright &y& Elsevier]

Ti-diffused LiTaO 3 strip waveguide was fabricated by in-diffusion of 8-μm-wide, 100-nm-thick Ti-strip at 1300 °C for 6 h in wet O 2 atmosphere. Its composition, surface morphology, lattice parameter, optical properties and Ti profile characteristics were fully characterized. It is shown that the waveguide is in the congruent composition environment. The waveguide surface caves in ∼70 nm below the crystal surface due to Ti-induced lattice contraction, which is verified by X-ray single-crystal diffraction. Optical characterizations show that the waveguide well supports both TE and TM single-mode propagation at the 1.5 μm wavelength, is polarization-insensitive, and has a loss of 0.4 (0.3) dB/cm for the TM (TE) mode. Secondary ion mass spectrometry analysis shows that the Ti profile follows a sum of two error functions in the width direction and a Gaussian function in the depth direction of the waveguide. [ABSTRACT FROM AUTHOR]