Search

The crystal growth, optical spectra and lifetime of Dy:CaGdAlO 4 crystal were investigated for the first time to our best knowledge. Single Dy:CaGdAlO 4 crystal with size of Φ4 × 40 mm 3 was grown by floating zone method. The peak absorption cross-sections were calculated to be 2.43 × 10 −21 cm 2 and 1.28 × 10 −21 cm 2 at 453 nm for σ and π polarizations. The Judd-Ofelt (JO) parameters of Ω 2 , Ω 4 and Ω 6 were calculated to be 1.8 × 10 −20 cm 2 , 1.0 × 10 −20 cm 2 and 0.5 × 10 −20 cm 2 , respectively. The emission cross-sections were calculated to be 0.51 × 10 −20 cm 2 and 0.55 × 10 −20 cm 2 for σ and π polarizations. The fluorescence decay time is 222 μs. The results indicate that the Dy:CaGdAlO 4 crystal is a potential candidate for yellow laser operation. [ABSTRACT FROM AUTHOR]

Abstract: Yb3+-doped (Lu0.5Y0.5)3Al5O12 (Yb:LuYAG) single crystal has been grown by the Czochralski method. The segregation coefficient of Yb3+ was studied by the inductively coupled plasma atomic emission spectrometry (ICP-AES) method. The crystal structure has been determined by X-ray diffraction analysis. The absorption and emission spectra and fluorescence lifetime of Yb:LuYAG crystal were measured at room temperature. The spectroscopic parameters of Yb:LuYAG crystal were compared with those of Yb:YAG and Yb:LuAG crystals with the same doping level. The results indicate that Yb:LuYAG crystals are potential candidates for high-power ultrashort pulse lasers. [ABSTRACT FROM AUTHOR]

Abstract: A Yb3+-doped CaYAlO4 laser crystal has been grown by the Czochralski technique. The segregation coefficient was measured by Inductively Coupled Plasma Atomic Emission Spectrometry (ICP-AES). The cell parameters were analyzed with X-ray diffraction experiments. Color defects in Yb:CaYAlO4 have been evidenced to be similar to those in undoped CaYAlO4. The polarized absorption spectra and the fluorescence spectrum of the Yb:CaYAlO4 crystal were measured at room temperature. The fluorescence decay time of the Yb3+ ion was investigated. The results show that Yb:CaYAlO4 has potential as a laser gain medium for an ultrashort laser system. [Copyright &y& Elsevier]

Abstract: A high optical quality erbium doped Lu2SiO5 single crystal has been grown by the Czochralski method. The distribution coefficient of Er3+ was measured to be ∼0.926. The absorption and emission spectra as well as the fluorescence decay curve of the excited state 4I13/2 were measured at room temperature. The spectroscopic parameters were calculated using the Judd–Ofelt theory, and the J–O parameters Ω 2 , Ω 4 and Ω 6 were found to be 4.451×10-20, 1.614×10-20 and 1.158×10-20 cm2, respectively. The room-temperature fluorescence lifetime of the Er3+ 4I13/2→4I15/2 transition was measured to be 7.74ms. The absorption and emission cross-section as well as the gain cross-section in the eye-safe regime of 1400–1700nm were also determined and discussed. [Copyright &y& Elsevier]

Sm:YAlO 3 (Sm:YAP) crystal with size of Φ28 × 80 mm3 was grown by Czochralski (Cz) method. Polarized absorption spectra and fluorescence spectra of Sm:YAP crystal were discussed for the first time. The peak emission cross-sections were calculated to be 0.80 × 10−21 cm2 (604 nm for a-polarization), 1.82 × 10−21 cm2 (604 nm for b-polarization) and 1.63 × 10−21 cm2 (610 nm for c-polarization), respectively. The Judd-Ofelt (JO) intensity parameters were calculated to be Ω 2 = 2.59 × 10−20 cm2, Ω 4 = 1.78 × 10−20 cm2 and Ω 6 = 2.98 × 10−20 cm2, respectively. The decay lifetime of 4G 5/2 energy level was measured to be 2.51 ms. All above results indicate the Sm:YAP crystal may be a potential candidate of reddish-orange laser pumped directly by the GaN/InGaN laser diode. • Sm:YAlO 3 crystal was grown by Cz method. • Polarized optical spectra of Sm:YAlO 3 crystal were investigated. • The transitions of 4G 5/2 → 6H 7/2 have the highest branching ratio value, which is suitable for reddish-orange laser. [ABSTRACT FROM AUTHOR]

In this paper, the Floating zone technique was used to grow high-quality Cr3+:YScO 3 crystals. The absorption cross-sections of the 4A 2 →4T 1 transition and 4A 2 →4T 2 transitions were calculated to be 1.71 × 10−20 cm2 at 488 nm and 0.72 × 10−20 cm2 at 666 nm, respectively. The crystal field strength Dq, Racah parameters B, and C were calculated to be 1502 cm−1, 533 cm−1, and 3362 cm−1, respectively. In the Cr3+:YScO 3 crystal, the effective phonon energy and Huang-Rhys factor S were calculated to be 284 cm−1 and 8.62, respectively. The emission cross-section at 988 nm corresponding to the 4T 2 →4A 2 transition was calculated to be 1.44 × 10−20 cm2 with full width at half maximum (FWHM) of 318 nm. All the results show that Cr3+:YScO 3 crystal has the potential to be a tunable and ultrafast laser crystal. • Cr:YScO 3 crystals were successfully grown by the Floating zone technique(FZ) method. • Broad emission spectrum with full width at half maximum (FWHM) of 318 nm in Cr:YScO 3 crystals was observed. • Spectral properties and crystal field parameters of Cr:YScO 3 crystals were investigated and analysed. [ABSTRACT FROM AUTHOR]

Pr 3+ -doped YAlO 3 (YAP) single crystal was successfully grown by the Czochralski (Cz) method. Polarized absorption and polarized fluorescence spectra were measured at the room temperature. The spectroscopic parameters based on the polarized absorption spectra were calculated by Judd-Ofelt (J-O) theory for the first time. The fluorescence lifetime of 3 P 0 energy level was fitted to be 19.16 μs with the quantum efficiency of 95.8%. Through the analyzing of the spectroscopic properties, Pr:YAP crystal was demonstrated to be a promising candidate for solid state laser operation. [ABSTRACT FROM AUTHOR]

Abstract: A laser crystal Er3+:YbVO4 has been grown by the Czochralski method with excellent quality. The rocking curve from the (004) diffraction plane of the as-grown Er3+:YbVO4 crystal was measured and the full-width at half-maximum value was found to be 19.80in. for the (004) face. The effective segregation coefficient of Er3+ was studied by X-ray fluorescence and the crystal structure was determined by means of X-ray diffraction analysis. The polarized absorption spectra and the fluorescence spectra of Er3+:YbVO4 were measured at room temperature. The spectral parameters were calculated based on the Judd–Ofelt theory, and the intensity parameters Ω 2, Ω 4 and Ω 6 are found to be 5.50×10−20, 1.96×10−20 and 2.34×10−20 cm2, respectively. The emission cross-section has been calculated by the Fuechtbauer–Ladenbury method. The spectroscopic parameters of Er3+:YbVO4 are compared with other typical laser hosts. [Copyright &y& Elsevier]

LaMgAl 11 O 19 (LMA) crystal with nominal Sm3+ concentrations of 8 at.% was grown by the Czochralski method. Polarized absorption spectra, polarized emission spectra and fluorescence decay curve of Sm:LMA crystal were recorded at room temperature. The absorption cross-sections at 404 nm were calculated to be 2.33 × 10−20 cm2 and 0.86 × 10−20 cm2 for σ and π polarization, respectively. The spontaneous transition rates, branching ratios and the radiative lifetime of the 4G 5/2 multiplet, were calculated. The Judd-Ofelt theory has been applied to evaluate the Ω t (t = 2, 4, 6) intensity parameters. The highest stimulated emission cross-sections for the 4G 5/2 → 6H 7/2 transition around 594 nm were calculated to be 1.67 × 10−21 cm2 for σ polarization and 1.15 × 10−21 cm2 for π polarization, with full width at half maximum (FWHM) of 7.68 nm and 7.27 nm, respectively. The fluorescence lifetime of the 4G 5/2 manifold was 1.84 ms. All the results show that Sm:LMA crystal would be a promising orange-red solid state laser material. • The most intensive absorption line of Sm3+ ion, suitable for 405 nm InGaN laser diode. • The rigidity of Sm:LMA crystal is higher than some host crystals. • The value Ω 2 of Sm:LMA crystal is comparable to Sm:LiYF 4. • The large parameter σ em τ of Sm3+ in LMA is beneficial for the solid state laser. [ABSTRACT FROM AUTHOR]