In the current research, the moisture-resistant of Mg-MOF-74 was successfully improved by coating with two-dimensional (2-D) hexagonal boron nitride (h -BN) during the facile hydrothermal synthesis process. Both TEM and SEM results revealed that 2-D h -BN is coated on Mg-MOF-74's surface. The crystal structure, morphology, surface area, thermal stability and CH 4 uptake capacity of Mg-MOF-74 were not drastically influenced by coating with h -BN as examined by XRD, FTIR, SEM, and TEM. Further, the coated Mg-MOF-74 demonstrated better stability than uncoated Mg-MOF-74, when being exposed to high humidity, in terms of surface area and CH 4 uptake capacity. It was observed that the coated Mg-MOF-74 with 1 ​wt % h -BN has reached to 1959 ​m2 ​g−1 surface area and CH 4 uptake capacity of 43 ​cm3 ​g−1 after exposure to high humidity for a duration of 1 month. Thus, this research work has opened a new window towards the improvement of the water stability of Mg-MOF-74. [Display omitted] • The water resistance capacity of Mg-MOF-74 could be improved by coating with two dimensional materials h -BN. • Application of h -BN as coating material of Mg-MOF-74. • h -BN coated Mg-MOF-74 provide high surface area and enhanced CH 4 uptake capacity. • The sample Mg-MOF-74@1 wt.% h -BN exhibited the highest water stability. [ABSTRACT FROM AUTHOR]

A new supramolecular compound [Zn(H2EDTA)(H2O)](Q)2(H2O)2 (1), where H4EDTA=ethylenediaminetetraacetic acid and Q=4-(carboxylate)pyridinium, has been prepared by mild hydrothermal reaction and characterized by elemental analysis, IR spectrum and thermogravimetric analysis. Single-crystal X-ray diffraction of 1 [monoclinic, space group C2/c, a=11.310(4) Å, b=9.704(4) Å, c=23.798(10) Å, β=97.401(10)°, Z=4] revealed that the ZnII ion coordinates to the chelating tetradentate ligand H2EDTA and a water molecule, taking a distorted trigonal-bipyramid geometry. The mononuclear [Zn(H2EDTA)(H2O)] subunits are linked to form two-dimensional layered architectures by the lattice water moieties through O–H⋯O hydrogen bonds, which are further extended to a three-dimensional (3D) supramolecular network by 4-(carboxylate)pyridinium guests (resulting from the ring-opening hydrolysis of 2,5-bis(4-pyridyl)-1,3,4-oxadiazole) through extensive hydrogen-bonding interactions. The 3D supramolecular framework is also stabilized by significant face-to-face π–π stacking interactions between the aromatic pyridinium systems. [Copyright &y& Elsevier]