In this study, we present the crystal structure, magnetic properties, and cryogenic magneto-caloric effect (MCE) of RE 2 FeAlO 6 (RE = Gd, Dy, Ho) oxides. The XRD refinement analysis suggests that all the RE 2 FeAlO 6 oxides are crystallized in B-site disordered orthorhombic structure. The RE 2 FeAlO 6 oxides exhibit large MCEs around T C. The peak magnetic entropy change (-Δ S M) and refrigeration capacity (RC) are 25.9 J/(kgK) and 240.1 J/kg for Gd 2 FeAlO 6 , 10.7 J/(kgK) and 274.9 J/kg for Dy 2 FeAlO 6 , 9.6 J/(kgK) and 249.6 J/kg for Ho 2 FeAlO 6 under Δ H of 0–70 kOe, respectively. Notably, Gd 2 FeAlO 6 exhibits promising magneto-caloric performance and therefore is a favorable candidate for cryogenic magnetic refrigeration. [ABSTRACT FROM AUTHOR]

The crystal structure together with the magnetic and magnetocaloric properties in RE 2 Ni 1.5 Ga 2.5 (RE = Dy, Ho, Er and Tm) have been investigated systematically. All the RE 2 Ni 1.5 Ga 2.5 compounds crystallize in a CaIn 2 -type structure of (P63/mmc space group). A second-ordered magnetic phase transition (SOPT) from ferromagnetic to paramagnetic (FM to PM) is occurred in RE 2 Ni 1.5 Ga 2.5 compounds with the Curie temperatures (T C) of approximately 16.1, 10.6, 4.1 and below 2 K for RE of Dy, Ho, Er and Tm, respectively. The magnetocaloric parameters including magnetic isothermal entropy change/temperature-averaged magnetic entropy change -Δ S M max/ TEC (5) and relative cooling power RCP are calculated with the values of 10.01/9.92 J/kg K and 418.6 J/kg for Dy 2 Ni 1.5 Ga 2.5 , 20.12/19.65 J/kg K and 644.1 J/kg for Ho 2 Ni 1.5 Ga 2.5 , 18.07/17.69 J/kg K and 447.1 J/kg for Er 2 Ni 1.5 Ga 2.5 , as well as 18.22/16.75 J/kg K and 330.7 J/kg for Tm 2 Ni 1.5 Ga 2.5 with magnetic field change (Δ H) of 0–7 T, respectively. Notably, Ho 2 Ni 1.5 Ga 2.5 exhibits ralatively high magnetocaloric parameters, which suggests that Ho 2 Ni 1.5 Ga 2.5 is a competitive candidate among the MCE materials in the field of cryogenic magnetic refrigeration (MR). • Magnetic properties and MCE in RE 2 Ni 1.5 Ga 2.5 compounds were studied. • Large values of -ΔS M max, TEC and RCP were observed at low temperature. • Ho 2 Ni 1.5 Ga 2.5 compound is competitive for cryogenic magnetic cooling. [ABSTRACT FROM AUTHOR]

In this work, polycrystalline oxides viz., Ho 2 CrMnO 6 (HCMO) and Er 2 CrMnO 6 (ECMO), were prepared using the sol-gel process, and their crystal structure, magnetic properties, and magnetocaloric effects (MCEs) were studied. X-ray refinement results demonstrate that both oxides exhibited the B -site disordered perovskite type structure (Pbnm space group). A ferromagnetic-paramagnetic phase transition as well as large reversible MCEs was also observed at Curie temperatures (T C) of ~6.1 and ~5.2 K for HCMO and ECMO, respectively. For a magnetic field change (ΔH) of 0–7 T, the maximum magnetic entropy change (-Δ S M), temperature-averaged entropy change (TEC 3), and relative cooling power (RCP) were estimated to be 11.03 J/kgK, 11.02 J/kgK, and 322.7 J/kg for HCMO, and 12.94 J/kgK, 12.80 J/kgK and 277.5 J/kg for ECMO. [ABSTRACT FROM AUTHOR]