Search

Two-dimensional transition metal dichalcogenide (TMD) semiconductors have risen as an important material class for novel nanoelectronic applications. Molybdenum disulfide (MoS2) is the most representative TMD compound due to its superior stability and attractive properties for (opto-) electronic devices. However, the synthesis of single-crystalline and functional MoS2 across large-area substrates remains crucial for its successful integration in semiconductor industry platforms. Therefore, this work focuses on the study of MoS2 epitaxy via two well-established industry-compatible synthesis methods, promising for the large-area and single-crystalline integration of van der Waals (vdW) materials. These methods are molecular beam epitaxy (MBE) and metalorganic vapor phase epitaxy (MOVPE) and have studied MoS2 quasi-vdW heteroepitaxy on reconstructed sapphire substrates and MoS2 vdW homoepitaxy on exfoliated MoS2 flakes. By examining the MoS2 structural properties using diffraction and spectroscopy techniques, the epitaxial relation and crystal quality are assessed, which reveals insights into the prevalence of inter- and intragrain defects such as grain boundaries and sulfur vacancies. The MBE method yields superior epitaxial MoS2 registry on both sapphire and MoS2 surfaces as compared to MOVPE, although inferior defectivity arises from the typical lower MBE growth temperature and chalcogen partial pressure. Moreover, both synthesis methods generate high densities of twinned MoS2 grain boundaries, which hamper defect-free integration. As a result, this challenging integration might become an important bottleneck for industrial TMD-based applications with a low tolerance for material defects. [ABSTRACT FROM AUTHOR]

The structure, crystallinity and properties of as-deposited two-dimensional (2D) transition metal dichalcogenides are determined by nucleation mechanisms in the deposition process. 2D materials grown by atomic layer deposition (ALD) in the absence of a template are polycrystalline or amorphous. Little is known about their nucleation mechanisms. Therefore, the nucleation behavior of WS2 during plasma enhanced ALD from WF6, H2 plasma and H2S at 300 °C is investigated on amorphous ALD Al2O3 starting surface and on monocrystalline, bulk sapphire. Preferential interaction of the precursors with the Al2O3 starting surface promotes fast closure of the WS2 layer. The WS2 layers are fully continuous at WS2 content corresponding to only 1.2 WS2 monolayers. On amorphous Al2O3, (0002) textured and polycrystalline WS2 layers form with grain size of 5 to 20 nm due to high nucleation density (∼1014 nuclei/cm2). The WS2 growth mode changes from 2D (layer-by-layer) growth on the initial Al2O3 surface to three-dimensional (Volmer-Weber) growth after WS2 layer closure. Further growth proceeds from both WS2 basal planes in register with the underlying WS2 grain and from or over grain boundaries of the underlying WS2 layer with different in-plane orientation. In contrast, on monocrystalline sapphire, WS2 crystal grains can locally align along a preferred in-plane orientation. Epitaxial seeding occurs locally albeit a large portion of crystals remain randomly oriented, presumably due to the low deposition temperature. The WS2 sheet resistance is 168 MΩμm, suggesting that charge transport in the WS2 layers is limited by grain boundaries. [ABSTRACT FROM AUTHOR]

The process characteristics, the surface chemistry, and the resulting film properties of Ru deposited by atomic layer deposition from (ethylbenzyl)(1-ethyl-1,4-cyclohexadienyl)Ru(0) (EBECHRu) and O2 are discussed. The surface chemistry was characterized by both combustion reactions as well as EBECHRu surface reactions by ligand release. The process behavior on TiN starting surfaces at 325 °C was strongly influenced by Ti(O,N)x segregation on the growing Ru surface with consequences for both the growth per cycle as well as the film properties. For optimized process conditions, the films showed high purity with low C and O concentrations of the order of 1020 at./cm3. Higher deposition temperature led to strong (001) fiber texture of the films on SiO2 starting surfaces. Annealing in forming gas improved the crystallinity and led to resistivity values as low as 11 μΩcm for Ru films with a thickness of 10 nm. [ABSTRACT FROM AUTHOR]