Search

• A series of 0.6 at% Pr:CaF 2 -RF 3 (R= Y3+, Gd3+, Lu3+) crystals were successfully grown by the temperature gradient technique(TGT) method. • By co-doping R3+ ion (R=Y3+, Gd3+, Lu3+), the spectral performance of the crystals could be significantly improved and the function effect is also different. • The spectral performance and spectral quality factor of the crystals were systematically described and compared for the first time. • The spectral modulation effect caused by Y3+, Gd3+ and Lu3+ co-doping ion was discussed. A series of 0.6 at% Pr:CaF 2 -RF 3 (R = Y3+, Gd3+, Lu3+) crystals have been successfully grown by the temperature gradient technique(TGT). The absorption spectra, fluorescence spectra, and fluorescence decay curves were measured and analyzed at room temperature. When the R3+ concentration is higher than a certain value, the diffraction peaks of Pr:CaF 2 -RF 3 crystals were well indexed to the (Ca,Y)F 2 phase. By co-doping R3+ ion (R=Y3+, Gd3+, Lu3+), the spectral performance of the crystals could be significantly improved and the function effect is also different. For 0.6 at% Pr, 28.5 at% Y:CaF 2 crystal, the fluorescence lifetime of 3P 0 energy level was fitted to be 45.46 µs, and the emission cross sections of 3P 0 →3H 6 (605 nm), and 3P 0 →3F 2 (641 nm) were calculated to be 1.78 × 10−20 cm2, and 4.61 × 10−20 cm2 with the full width at half (FWHM) of 20.1 nm and 6.8 nm, respectively. The 0.6 at% Pr, 28.5 at% Y:CaF 2 crystal could be favorble laser medium for ultra-fast laser opreration at 605 nm and 641 nm. For 0.6 at% Pr, 18 at% Gd:CaF 2 and 0.6 at% Pr, 10 at% Lu:CaF 2 crystals, the spectral quality factors σ em• τ f of 3P 0 →3F 2 transition (642 nm) were calculated to be 614.18 × 10−20 cm2•µs and 506.36 × 10−20 cm2•µs with the FWHM of 3.7 nm and 5.3 nm. All the results show that 0.6 at% Pr, 18 at% Gd:CaF 2 and 0.6 at% Pr, 10 at% Lu:CaF 2 crystals are promising gain media for high-efficiency visible laser output at 642 nm, which would compete with commercial Pr: YLF crystal in the future. [ABSTRACT FROM AUTHOR]

Yb,Pr:CaF 2 crystals have been grown successfully by the temperature gradient technique(TGT). The absorption spectra, fluorescence spectra, fluorescence decay lifetime of Pr3+ ions in CaF 2 crystal sensitized by different Yb3+ ions concentration have been measured. The effective J-O intensity parameters were fitted to be Ω 2 =0.36 × 10−20cm2, Ω 4 =2.89 × 10−20cm2, Ω 6 =6.69 × 10−20cm2 for 0.3 at.%Pr,1.5 at.%Yb:CaF 2. And the emission cross sections of 3P 1 →3H 5 (535 nm), and 3P 0 →3F 4 (750 nm) are calculated to be 2.02 × 10−20cm2, and 2.50 × 10−20cm2 with the FWHM of 17.2 nm, and 10.5 nm, respectively. The fluorescence lifetime of 3P 0 has achieved great increasing by sensitizing of Yb3+ ion. Not only the up-conversion luminescence can be achieved, but also the broad band emission from 1D 2 energy level can be observed. The results show that Yb,Pr:CaF 2 could be a potential laser gain medium for visible and near-IR laser operation. • Not only the up-conversion luminescence can be achieved, but also the broad band emission from 1D 2 energy level can be observed by Yb3+ ion sensitizing. • Spectral properties and Judd-Ofelt parameters of Yb,Pr:CaF 2 crystal were investigated and analysed. [ABSTRACT FROM AUTHOR]