Cr4+:YbAG (Cr4+:Yb3Al5O12) crystal with a size up to Φ24 mm×30 mm was grown by the Czochralski method. In the absorption spectrum, there are two absorption bands at 939 and 969 nm, respectively, which are suitable for InGaAs diode laser pumping, and there is an absorption band at 1030 nm, which is suitable for passive Q-switched laser output at 1.03 μm. A broad emission spectrum from 970 to 1100 nm was exhibited from 940 nm wavelength pumping. This crystal is promising as a self-Q-switched laser crystal used for compact, efficient, highly stable, passive self-Q-switched thin chip solid-state lasers. [Copyright &y& Elsevier]

• Spectral properties and high-efficiency broadband laser operation of Tm:CYGA crystal at 2 μm were demonstrated. • The maximum continuous-wave output power of 1.43 W was obtained. • A 284.7 nm tuning coverage was realized with a BF. We report on spectral properties and a high-efficiency broadband laser operation of Tm:CaY 0.9 Gd 0.1 AlO 4 (Tm:CYGA) crystal. The polarized absorption and emission spectra, gain cross sections and fluorescence lifetime are systematically studied, presenting a broad absorption and emission spectra and thus a smooth gain band. Furthermore, under an absorbed pump power of 4.35 W, a maximum continuous-wave (CW) laser output power of 1.43 W at 1967.8 nm is obtained, corresponding to a slope efficiency of 42.2 %. The beam quality factors (M2) in X-axis and Y-axis are measured to be 1.011 and 1.027, respectively. A tunable Tm:CYGA laser with a tuning range of 284.7 nm from 1837.5 to 2122.2 nm is achieved employing a birefringent filter (BF). The results indicate that the Tm:CYGA crystal is an excellent laser medium for generating high-efficiency broadband CW laser, indicating its potential for ultrashort pulse generation in the 2-μm spectral range. [ABSTRACT FROM AUTHOR]

Nd-doped PbClF crystals were grown with modified Bridgman method. Broad and flat emission band at 1.0 μm was observed. The FWHM value of 0.0091 wt.% Nd3+-doped PbClF crystal at 1064 nm reached up to 30 nm with the peak emission cross-section of 1.05×10-19 cm2. All the results indicated that Nd-doped PbClF crystal should be a promising tunable and ultrafast laser material. (© 2012 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim) [ABSTRACT FROM AUTHOR]

High-quality Dy:PbWO 4 crystal has been successfully grown by the Bridgman method. Fluorescence properties of the grown crystal at the yellow-light region were discussed. The absorption cross-section of Dy3+ ions at 454 nm was calculated to be 0.142 × 10−20 cm2, which corresponded to the transition from 6H 15/2 to 4I 15/2 level. Based on Judd-Ofelt theory, the J-O intensity parameters Ω t and the emission cross-section were calculated. The fluorescence lifetime of 4F 9/2 level was measured to be 193 μs. • Dy: PbWO 4 crystal was grown successfully by the Bridgman method. • Judd-Ofelt theory was used to analyze the spectral properties of Dy: PbWO 4 for the first time. • Dy: PbWO 4 crystal is a potential laser medium for yellow laser operation. [ABSTRACT FROM AUTHOR]

Abstract: For the first time, a quaternary doping system of Er3+, Yb3+, Ce3+, Na+: CaF2 single crystal was demonstrated to have high fluorescence yield in the 1.5μm region. Through a simplified model, the branching ratio of the Er3+ 4I11/2→4I13/2 transition was estimated to be improved more than 40 times by the deactivating effect of Ce3+ in the quaternary-doped CaF2 crystal with dopants of 0.2-at% Er3+ and 2.0-at% Ce3+. Owing to the broad emission bandwidth and large emission cross-section, the quaternary-doped CaF2 system shows the great potential to achieve the high laser performance in the 1.5μm region. [Copyright &y& Elsevier]

Abstract: The effects of Na+ doping level on the thermal conductivities, absorption and emission spectra, and fluorescence lifetimes of Yb3+,Na+:CaF2 crystals were systematically studied. Sites structure, covalent force, and crystal field strength of Yb3+:CaF2 crystals were markedly varied by codoping Na+ as charge compensator. The 2.0at% Yb3+ and 3.0at% Na+-codoped CaF2 crystal was demonstrated to operate in diode-pumped passively mode-locking scheme. Transform-limited 1ps laser pulses were obtained, showing the crystal capable of producing ultra-short laser pulses. [Copyright &y& Elsevier]

• Diode-pumped CW Pr,Mg:SRA lasers at 643 nm, 724 nm and 622 nm are demonstrated. • The highest output power of the diode-pumped Pr,Mg:SRA laser is 675 mW. • Passively Q-switched Pr,Mg:SRA lasers are also demonstrated, for the first time. • The shortest pulse width is 105.6 ns for the 622 nm laser, while 211.7 ns for the 643 nm laser. We report on compact blue-diode-pumped Pr,Mg:SrAl 12 O 19 (SRA) lasers in continuous-wave and passively Q-switched regimes. For continuous-wave mode, three lasers have been achieved with maximum output powers of 675 mW, 566 mW and 312 mW at wavelengths of 643 nm, 724 nm and 622 nm, respectively. The maximum slope efficiencies with respect to absorbed power for the three lasers are 18.7%, 16.6% and 11.1%. Using a uniaxial Co2+-doped strontium, lanthanum and magnesium aluminate (Co:ASL) crystal as saturable absorber with remarkable absorptions at 643 nm and 622 nm, we have achieved passively Q-switched Pr,Mg:SRA lasers at the two emissions with maximum output powers of 175 mW and 118 mW, respectively, for the first time to our knowledge. The shortest pulse widths for the two lasers are 211.7 ns and 105.6 ns. Correspondingly, we estimated that pulse energies and peak power are 2.13 μJ and 10.1 W for the 643 nm laser as well as 0.98 μJ and 9.27 W for the 622 nm laser. This work reveals that Pr,Mg:SRA as one of the few reported Pr3+-doped oxides could be potential in generating compact and efficient lasers in visible spectral range. [ABSTRACT FROM AUTHOR]

Nd:SrAl 11 O 19 (Nd:SRA) crystal has been grown by the Czochralski method. Polarized absorption spectra, polarized fluorescence spectra and fluorescence lifetime were investigated. For σ-polarization, the peak absorption cross section at 798 nm is 2.08 × 10−20 cm2 with full width at half maximum (FWHM) of 10.2 nm and the peak emission cross section is 3.36 × 10−20 cm2 at 1048.5 nm with FWHM of 4.80 nm. The Judd-Ofelt parameters Ω 2,4,6 were obtained to be 0.51 × 10−20 cm2, 2.08 × 10−20 cm2, and 2.12 × 10−20 cm2, respectively. Continuous-wave laser operation of the a-cut and c-cut Nd:SRA sample has been demonstrated. The maximum output power of 8.33 W was achieved from c-cut sample at an absorbed power of 27.73 W, corresponding to a slope efficiency of 31.3%. • Nd:SrAl 12 O 19 crystal has been gown by the Czochralski method. • Spectral parameters of Nd:SrAl 12 O 19 crystal were obtained. • Continuous-wave laser was demonstrated from Nd:SrAl 12 O 19 crystal. [ABSTRACT FROM AUTHOR]

High quality 7 at%Er:Y 2 O 3 crystal was successfully grown by Fz method. Judd-Ofelt theory was applied to analyze spectroscopic properties at 2.7 μm. The larger value of Ω 2 shows low local environment symmetry exists in Er:Y 2 O 3 crystal, and the large Ω 4 /Ω 6 indicates better spectral quality. The larger absorption cross-section and FWHM are beneficial to efficient absorption of pump source. The fluorescence spectra and lifetimes of Er:Y 2 O 3 crystal were measured and studied at 2.7 μm. The emission cross-sections at 2723 nm was calculated to be 1.41 × 10−20cm2. Compared with other Er3+ doped crystals, the large spectral quality factors Q and low fluorescence lifetime ratio illustrate that Er:Y 2 O 3 crystal has excellent laser properties at 2.7 μm. In addition, the low inversion ratio also indicates great potential of Er:Y 2 O 3 crystal for laser generation at 2.7 μm. • A high quality 7%Er:Y 2 O 3 laser crystal was successfully grown by Fz method. • Judd-ofelt (J-O) parameterization scheme was applied to analyze the spectroscopic properties of 7%Er:Y 2 O 3 laser crystal at 2.7 μm. • The large spectral quality factors Q with low fluorescence lifetime ratio illustrates that Er:Y 2 O 3 crystal has excellent laser properties at 2.7 µm. • The low inversion ratio indicates great potential of Er:Y 2 O 3 crystal for laser generation at 2.7 μm. [ABSTRACT FROM AUTHOR]

The high optical quality Er:Lu 2 O 3 and Er,Pr:Lu 2 O 3 crystals were grown by Floating zone method. The spectral properties of Er:Lu 2 O 3 and Er,Pr:Lu 2 O 3 crystals were investigated. After co-doping small concentration of Pr3+, the depopulated influence of Pr3+ to the NIR emission was much stronger than the MIR emission. The near-infrared and up-conversion fluorescence were significantly quenched. Moreover, the fluorescence lifetime of 4I 13/2 abviously decreases from 4.02 ms to 1.71 ms in 7% Er, 0.05% Pr: Lu 2 O 3 crystal, and the lifetime ratio is 1.63 with large fluorescence lifetime of 4I 11/2 which is desirable lifetime ratio in these crystals. Thus, the spectral performance was significantly improved by co-doping 0.05 at.% of Pr3+. The high laser performance at 2.7 μm of 7% Er, 0.05% Pr: Lu 2 O 3 crystal is expectable. • The high optical quality Er:Lu 2 O 3 and Er,Pr:Lu 2 O 3 crystals were firstly grown by Floating zone method. • The spectral properties of Er:Lu 2 O 3 and Er,Pr:Lu 2 O 3 crystals were firstly investigated. • After co-doping low concentration of Pr3+, the near-infrared, ESA and up-conversion fluorescence were significantly quenched. • The spectral performance of Er:Lu 2 O 3 crystal was significantly improved at 2.7 μm by co-doping 0.05 at.% of Pr3+. [ABSTRACT FROM AUTHOR]

• The performance of diode-pumped (Nd3+-doped) Ca 0.7 La 0.3 Al 12 O 19 (Nd:CLA) lasers was studied for the first time. • By inserting a Cr4+:YAG absorber, we successfully achieved a passively Q-switched laser. • Comparation between a- and c-cut disordered Nd:CLA lasers were made. A new neodymium-doped (Nd3+-doped) Ca 0.7 La 0.3 Al 12 O 19 (Nd:CLA) disordered crystal was successfully grown by the Czochralski method. The performance of diode-pumped Nd:CLA (a-cut and c-cut) lasers was demonstrated for the first time. For the c-cut crystal continuous-wave (CW) operation, we obtained the highest output power of 2.08 W at the wavelength of 1053.2 nm, and the slope efficiency was 23% versus the incident pump power. By inserting a Cr4+:YAG absorber, we successfully achieved a passively Q-switched laser, and the shortest pulse width was 18.36 ns with a peak power of 364.6 W. Compared with a-cut crystal, c-cut crystal has superior laser characteristics. [ABSTRACT FROM AUTHOR]