Two commercially available mordenites, obtained from Zeolyst (Si/Al = 10 at/at) and BASF (Si/Al = 8 at/at), were subjected to post-synthesis treatments. The impact of acid treatment, alkaline treatment (desilication) and a combination of both on porosity, crystallinity and catalysis were studied in detail. It was found that sequential acid and alkaline treatments were most effective to obtain mesoporous mordenite with external surface areas up to 250 m2 g-1. Electron tomography was used to visualize the mesoporosity of a series of sequential acid- and alkaline-treated mordenite samples. Mesopore formation started close to the external surface area and progressed toward the center of the crystallites for higher porosities. Liquid-phase alkylation of benzene with propylene to cumene was chosen to study the catalytic performance of the enhanced accessibility of various mordenite samples. The activity of the most porous mordenite was found to be close to that of a commercial zeolite beta, while selectivity toward the undesired n-propylbenzene was found to be significantly lower for mordenite (∼70 ppm) than for zeolite beta (∼175 ppm). These catalytic data indicate that the acid- plus alkaline-treated mordenite could be a viable catalyst in the cumene process.

Several commercially available samples consisting of agglomerated small mordenite crystallites with low Si/Al ratios (5.7–10 at/at) have been treated in aqueous NaOH solution. It was found that the porosity can be enhanced when the sodium hydroxide solution is sufficiently concentrated. Treatment in 1 M NaOH for 15 min resulted in inter-crystalline porosity and the mesopore volume was increased from 0.01 to 0.21 cm3 g−1 together with an increased external surface area from 36 to 85 m2 g−1. The micropore volume and crystallinity were preserved after the treatment. Both H-MOR and Na-MOR mordenite agglomerates have been successfully treated: the Na-MOR requires a longer contact time to obtain similar porosity. By carefully choosing the alkaline concentration and contact time, intra-crystalline mesoporosity can be obtained for mordenite with Si/Al ratios as low as 10. Catalytic tests with proton mordenite showed that alkaline treatment leads to more than one order of magnitude of activity gain in the liquid-phase alkylation of benzene with propene to form cumene, while selectivity is preserved. These results demonstrate that alkaline treatment also on high-aluminum content mordenites is an effective tool to enhance accessibility and thereby its catalytic performance.