Search

Herein, the influence of annealing current intensities on magnetic properties of Gd-based microfibers was systematically investigated. The experimental results indicated that the as-prepared microfibers have amorphous structure and excellent thermal-stability, and the Curie temperature T C of which slightly change before and after annealing. The general magnetic physical magnitudes (M s , M r , μ 0 H c and μ m) of microfibers increase firstly and then decrease with the rising of annealing current intensities, and those of the microfibers annealed at 90 mA microfibers are more obvious (M s = 255 A m2/kg and μ m = 0.38 ± 0.01). Similarly, the magnetocaloric parameters of microfibers also increase firstly and then decrease with the rising of current intensities. At 5 T of magnetic field change μ 0 Δ H , the maximum magnetic entropy change Δ S m max and refrigerant capacity RC of 90 mA annealed metallic microfibers are 12.77 J/(kg·K) and 906 J/kg, respectively, and which remarkably increased in compared with the as-prepared state, respectively. From the microstructural evolution perspective, a certain intensity current annealing induces the tendency of micro-regional clusters and nanocrystals, forming atomic ordered regions, and the internal residual stress release with a reduction of magnetic anisotropy. Meanwhile, the magnetic ordering and the critical magnetic-moment rotational driving-force were changed after Fe-doping, resulting in effective improvement of refrigerant capacity. Accordingly, the current-annealed Gd-Al-Co-Fe microfibers can be adopted as low-temperature magnetic refrigeration working-medium, which also provides a theoretical foundation for magnetic refrigeration technology application. Magnetocaloric properties of Gd-Al-Co-Fe metallic microfibers current-annealed at 90 mA are significantly improved according to the microstructural evolution and magnetic ordering modulation. Image 1 • Effects of current annealing intensities on the magnetic properties were investigated in detail. • MCE characteristics of Gd-Al-Co-Fe microfibers could be obviously improved at 90 mA. • Magnetocaloric mechanism is illustrated by the perspective of structural evolution and magnetic ordering transformation. [ABSTRACT FROM AUTHOR]

The effects of trace Fe-doping on the magnetic and magnetocaloric performances of Gd-based metallic microfibers were systematically and detailedly investigated in this article. Experimental results indicated that the Gd-based microfibers prepared by the rotated-dipping process are uniform and continuous, with typically amorphous structure characteristics and favorable thermal stability. Curie temperature T C of Gd-based amorphous microfibers increases with the rising of Fe content, and the T C of GdAlCoFe3 microfibers is the highest at 128.7 K (relatively increased by 15.3 K than before doping). Among the general magnetic performance indicators, the saturation magnetization M s of GdAlCoFe2 microfibers reaches a peak at 264.04 emu/g. Furthermore, the values of magnetocaloric performance indexes of Gd-based amorphous microfibers increase firstly and then decrease with the rising of Fe-doping amount. When the external magnetic field H ex = 50,000 Oe, the maximum magnetic entropy change -Δ S m max, refrigeration capacity RC and relative cooling power RCP of GdAlCoFe1 microfibers are 10.33 J/kg·K, 748.22 J/kg and 1006.90 J/kg, which increased by 0.07 times, 0.13 times and 0.16 times, respectively than before Fe-doping (namely -Δ S m max = 9.68 J/kg·K, RC = 663.79 J/kg, RCP = 871.73 J/kg). From the perspective of microstructural changes, Fe-doping results in the formation tendency of atomic clusters and nanocrystals in micro-regions, the orderly orientation of atoms appears, and the magnetic anisotropy increases accordingly. In addition, the 3d electron layer of the doped Fe element in Gd-Al-Co-Fe quaternary alloy system enhances the RKKY indirectly exchange coupling interaction and changes the state of magnetic entropy, which in turn leads to an increase in Curie temperature and an improvement in magnetocaloric performance. Since RC and RCP are the main indicators in engineering applications, the GdAlCoFe1 amorphous microfibers can be selected as a low-temperature magnetic refrigeration working medium to provide technical guarantee for the application of magnetic refrigeration technology. In comparison to Fe-doped Gd-based amorphous microfibers, # GdAlCoFe1 microfibers have enhanced magnetocaloric properties by coactions of atomic arrangement ordering transformation (AAOT) and magnetic moment ordering transformation (MMOT). Image 1 • Influence of Fe-doping amounts on the magnetocaloric properties was investigated systematically. • MCE properties of # GdAlCoFe1 amorphous fibers were enhanced effectively. • Interaction mechanism was illustrated from the perspective of atomic arrangement and magnetic moment ordering transformation. [ABSTRACT FROM AUTHOR]