Search

Abstract: Objectives: The increased usage of composite dental restorations underscores the need for continued improvements in material properties. Well-controlled sample fabrication and reproducible methods to quantify and compare material properties will accelerate material design and optimization. Our objectives were to fabricate samples encompassing a range of processing parameters and develop techniques that systematically quantify multiple properties of these samples, thus reducing sample-to-sample variation while concurrently testing numerous processing conditions. Methods: Gradient samples were prepared to evaluate the effects of composition and irradiation time. Comonomer ratio of 2,2-bis[p-2′-hydroxy-3′-methacryloxypropoxy]-phenyl]propane (BisGMA) and triethylene glycol dimethacrylate (TEGDMA) was varied discretely, and irradiation time was varied continuously across each composition. Degree of conversion was measured using infrared spectroscopy, mechanical properties were evaluated using nanoindentation, and cell viability and density were quantified using fluorescence microscopy. Results: Higher BisGMA contents increased elastic moduli while higher TEGDMA contents increased conversions. Cell response depended only on irradiation time and not composition, with conversions of at least 52% and 60% required for unaffected viability and cell density, respectively. A single composition–irradiation combination to achieve all of the ‘best’ properties (highest conversion, highest elastic modulus, lack of cytotoxicity) was not identified, illustrating the necessity of testing all combinations for multiple relevant properties. Significance: Simultaneously screening composition and conversion increased the experimental throughput and allowed for the quantification of chemical, mechanical, and biological properties in a controlled, reproducible fashion. This 2D gradient approach is useful for optimizing compositions and processing parameters to achieve the desired combination of properties. [Copyright &y& Elsevier]

Abstract: Objective: Use X-ray microcomputed tomography (μCT), to test the hypothesis that composite shrinkage and sites of potential leakage in human teeth are non-uniformly distributed and depend on cavity geometry and C-factor. Methods: Two holes of equal volume but different dimensions were drilled into the exposed dentin of extracted human molars. The cavities were filled with composite and teeth were scanned, before and after curing, using μCT. Three-dimensional (3D) reconstructions of the data were prepared and analyzed using image analysis software. Results: 3D reconstructions showed that cavity geometry did not affect the polymerization shrinkage. The shrinkage for all restorations was 2.66±0.59%, and cavity dimensions did not affect the volume lost, either in quantity or location on the sample. Potential leakage sites were identified by gap formations and found to be non-uniformly distributed along the tooth–composite interface. Leakage in regions calculated by μCT was confirmed by visualization of sectioned samples with confocal laser scanning microscopy. Significance: μCT evaluation will add tremendous value as part of a suite of tests to characterize various properties of dental materials. The non-uniform distribution of potential leakage sites about the cavities that was determined by μCT emphasizes the inadequacy of traditional methods of determining leakage, which are capable of analyzing only limited areas. Additionally, μCT evaluation can produce quantitative analyses of shrinkage and leakage, compared to the conventional methods, which are qualitative or semi-quantitative. Finally, experimentally determined shrinkage and leakage of composite in extracted teeth agrees with the results of similar experiments in model cavities, confirming the validity of those models. [Copyright &y& Elsevier]