Search

BACKGROUND Before insertion, chairside adjustment kits are heat sterilized for positioning and polishing dental restorations. This study aimed to evaluate the effects of 2 steam sterilization cycles on the efficacy of polishing highly translucent monolithic zirconia (HTMLZ) dental restoration material. MATERIAL AND METHODS 100 HTMLZ disc-shaped specimens were adjusted (grinding, finishing, polishing) with EVE Diacera kit. Two steam sterilization techniques [standard (Gp S), immediate/flash (Gp (F)] of CAK were further subgrouped based on number of sterilization cycles [cycle 1 (control), cycle 5, 10, 15, and 20 (experimental)] (n=10 each). Each subgroup accordingly was evaluated for average surface roughness (Ra) and root mean square roughness (Rq) using a profilometer. Mean and standard deviation of 5 subgroups were statistically analyzed using one-way ANOVA/post hoc Tukey's test. Scanning electron microscopy complemented Ra, Rq measurements. Statistical differences of P≤0.05 were considered significant. RESULTS HTMLZ specimens in both groups showed increased (Ra/Rq) values after repeated sterilization of EVE Diacera kit, with Gp F showing lesser increase than Gp S (20 cycles). Gp F at 10 cycles and Gp S at 15 cycles showed clinically unacceptable roughness threshold (0.25 μm). Differences between subgroups for Ra and Rq values were significant (P≤0.05) with less differences within groups observed in early cycles (1, 10). Results validate the manufacturer's recommendations of using flash sterilization/10 cycles for EVE Diacera kit. CONCLUSIONS Repeated sterilization reduces efficacy of chairside adjustment kit to produce smooth surfaces on HTMLZ. This study recommends flash sterilization to a maximum of 10 times to get the clinically acceptable results of Ra and Rq.

Background: Developing efficient bonding techniques for orthodontic brackets and all-ceramic materials continues to pose a clinical difficulty. This study aimed to evaluate the shear bond strengths (SBS) of metal and ceramic brackets to various all-ceramic CAD-CAM materials, such as lithium disilicate CAD (LDS-CAD), polymer-infiltrated ceramic (PIC), zirconia-reinforced lithium silicate glass ceramic (ZLS), and 5YTZP zirconia after different surface treatments and thermal cycling. Materials and methods: The samples were divided into two groups to be bonded with ceramic and metal lower incisor brackets. Each group was subdivided into a control group devoid of any surface treatment, 10% HF acid (HFA) etching, ceramic etch & prime (MEP), Al2O3 air abrasion, and medium grit diamond bur roughening. After surface treatment, brackets were bonded with composite resin cement, thermal cycled, and tested for shear bond strength. The failed surfaces were evaluated with a digital microscope to analyse the type of failure. The data were statistically analysed using a one-way ANOVA and Tukey HSD tests at p < 0.05. Results: The highest mean bond strengths were found with HFA etching in LDS-CAD (13.17 ± 0.26 MPa) and ZLS (12.85 0.52 MPa). Diamond bur recorded the lowest mean bond strength roughening across all the ceramic groups. There were significant differences in mean shear bond values per surface treatment (p < 0.001) and ceramic materials. Conclusion: Among the surface treatment protocols evaluated, HFA etching and MEP surface treatment resulted in enhanced bond strength of both ceramic and metal brackets to CAD-CAM all ceramic materials. [ABSTRACT FROM AUTHOR]

It is common to detect a gap between the apical portion of the post and the most coronal part of gutta-percha in a root canal during post and core treatment in endodontically treated teeth. It may compromise the seal that gutta-percha material provides in the root canal filling, leading to apical leakage, which is often thought to be one of the most common causes for failure of endodontic treatment. The prevention of apical leakage to achieve a complete apical seal and its effect on periapical health of endodontically treated teeth of post and core in long term clinical research remains unanswered. Post and core treatment were provided to 100 patients by undergraduate students in the year 2016–2017. A total of 70 patients in all were called back to the Prosthodontic Clinic for follow-up care after 4 years to assess the clinical result in terms of the gap between the post-operative and residual gutta-percha. The cemented posts were divided into three groups depending on the space between the cemented post end and the remaining gutta-percha: group I revealed no gaps, group II revealed gaps between >0.1 and 1 mm, and group III revealed gaps more than 1 mm. The periapical index (PAI) was used to determine the apical condition of each tooth. Chi-square test was used for evaluating the data, and a p-value of 0.05 was considered statistically significant. A total of 28.6% post and core treated teeth were found diseased while 71.4% teeth were found normal. In group I, 90% of the teeth and in group II, 66.7% of teeth were evaluated as normal; however, in group III, 41.2% teeth were found diseased. In endodontically treated teeth restored with a post and core, a gap between the apical end of the post and the coronal section of the residual gutta-percha was associated with a greater prevalence of disease. The post and core treatment by undergraduate students achieved a clinically acceptable outcome in terms of the gap between the post end and the remaining gutta-percha. [ABSTRACT FROM AUTHOR]

BACKGROUND: Advances in digital dentistry lead to use of three-dimensional (3D) printed resin denture teeth. Fracture toughness of these teeth must be assessed. OBJECTIVE: This study aimed to compare the chipping and indirect tensile fracture resistance of denture teeth fabricated by 3D printing technique with traditionally fabricated resin denture teeth. METHOD: Four groups (Gr) were made (n = 50/group): Gr-1 3D printed denture teeth (denture teeth; Formlabs Inc., Somerville, MA, USA), Gr-2 SR-Orthosit-PE (Ivoclar Vivadent AG), Gr-3 Portrait IPN (Dentsply Sirona), Gr-4 Pala Premium 8 (Heraeus Kulzer GmbH). Stereolithography 3D printing was used to create the methacrylate-based photopolymerized resin teeth models and remaining group teeth were collected commercially. A 1 mm/min chipping and indirect tensile fracture speed tests were carried out till fracture occurred. The data so obtained were statistically analysed using one-way analysis of variance with Tukey's honestly significant difference multiple comparisons test (p < 0.05). At the end of the test, the fractured areas of the specimens were evaluated by the chief researcher to assess the fracture pattern of the teeth. RESULTS: The indirect tensile fracture values of the 3D printed teeth were more than that of Pala Premium-8 and SR-Orthosit-PE but it was lower than that of Portrait IPN teeth. In chipping test, buccal chipping of the loaded cusp was seen in 3D printed resin without distortion and in indirect tensile test in 3D printed resin teeth, line of fracture emerges near the loading point propagates from the inner incline of both cusps and extends cervically, unlike in other groups where first deformation occurs then fracture. CONCLUSION: Prosthetic teeth fabricated by the 3D printing technique using printable resin material provide adequate fracture resistance as denture teeth. [ABSTRACT FROM AUTHOR]