Search

Purpose: To evaluate the effect of an acid containing 2% chlorhexidine (Ac/CHX) or a 2% CHX aqueous solution (Aq/CHX) on the immediate and 5-year bonding properties of resin/dentin interfaces produced by two adhesives. The presence of CHX in these interfaces was also evaluated under micro-Raman spectroscopy., Materials and Methods: Forty-two molars were ground to expose a flat dentin surface. In the control group, the surfaces were etched with conventional phosphoric acid, and Prime&Bond NT (PB) and Adper Single Bond 2 (SB) were applied. In Ac/CHX, an acid containing 2% CHX was applied after adhesive application. In the Aq/CHX group, an aqueous solution of 2% CHX was applied for 60 s after etching. After placing the restoration, specimens were prepared and tested using the microtensile bond strength test (μTBS, 0.5 mm/min) immediately or after 5 years. For nanoleakage (NL), specimens at each period were immersed in silver nitrate solution and examined by EDX-SEM. In addition, specimens at each period underwent examination for CHX using micro-Raman spectroscopy. Data were submitted to appropriate statistical analysis (a=0.05)., Results: After 5 years, NL was more pronounced in the control than in the Ac/CHX or Aq/CHX (p<0.001). Significant reductions in the μTBS were observed for all groups; however, they were more pronounced for the control (p<0.001). CHX was still present in the hybrid layers Ac/CHX or Aq/CHX groups after 5 years., Conclusion: The use of a 2% chlorhexidine-containing acid or the application of an aqueous CHX primer may increase the long-term stability of resin/dentin interfaces.

Aim: The aim of this study was to investigate in vitro the bond strength of composite resins on enamel previously treated with whitening strips., Materials and Methods: A total of 48 bovine incisors were allocated to four experimental groups (n = 12 each): G1 (WSC)- treated with 9.5% hydrogen peroxide whitening strips (3D White Whitestrips® Advanced Vivid/CREST); G2 (WSO)-treated with 10% hydrogen peroxide whitening strips (3D WhiteTM/Oral B); G3 (WG)-treated with 7.5% hydrogen peroxide gel with fluorine, calcium and potassium nitrate (White Class®/FGM); and G4 (C)-control not subjected to bleaching treatment. The specimens were subjected to bleaching over 2 weeks following the manufacturers' instructions. Following the elaboration of the composite resin test specimens, the samples were stored in artificial saliva and subsequently subjected to the micro-shear test using the universal testing machine (EMIC®). The bond strength values were analyzed by one-way ANOVA and Tukey's statistical test (5%)., Results: Significant differences were observed among the investigated groups (p < 0.05). The G3-WG exhibited greater values compared with the control group and the groups treated with strips, G1-WSC and G2-WSO. Analysis of the bond interface revealed that a large fraction of the failures occurred at the enamel-resin interface., Conclusion: The bond strength decreased following 14 days of treatment with bleaching strips, whereas the whitening gel with 7.5% hydrogen peroxide, calcium and fluorine increased the bond strength.

This in vitro study evaluated the Influence of prestretching, in the force decay of orthodontic elastic chains, at three time intervals: 2, 7 and 30 days with the brands Morelli, Orthometric and American Orthodontics. In the experimental group, prestretching was performed, stretching the elastics to increase them by 50% of their original length three times in a quick and sequential mode. All of the elastic chains were kept stretched and stored in artificial saliva at 37°C until the time of force measurement. For comparisons between the control and experimental groups, the Mann-Whitney test was used. For comparisons between time points and brands, the Kruskal-Wallis test was used, and for multiple comparisons, Miller's post-hoc test was used. The results showed statistically significant differences among the different commercial brands tested at the initial time point. The mean force at the initial time point ranged from 2.57 to 3.17 N. By day 2, the force values were between 0.97 and 1.49 N; by day 7, the values were 0.56 and 0.94 N. By day 30, the force values ranged between 0.27 and 0.66 N. We concluded that performing and duration of prestretching and the brand all Influenced the force decay of orthodontic elastic chains. Time had a greater Influence on the decay of the elastics than brand or prestretching.

Objective: This study aims to evaluate the degree of conversion (DC) and hydrolytic degradation through the Vickers hardness test (HV) of a nanoflled (Filtek(TM) Z-250, 3M) and a microhybrid (Filtek(TM)Supreme-XT, 3M) composite resin., Materials and Methods: Eight disk-shaped specimens (4 mm diameter × 2 mm thick, ISO 4049) of each material were prepared for each test. Composites were inserted into single increment in a metallic matrix and light-cured for 40 seconds. VH readings were performed for each specimen at predetermined intervals: immediately after polymerization (control), 1, 2, 3, 7, 14, 21, 30 and 180 days. After curing, initial hardness measurements were performed and the specimens were immersed in artifcial saliva at 37°C. For DC (%), specimens were ground, pressed with KBr and analyzed by FT-IR spectrophotometer., Results: Student t-test showed that there was no difference between the resins for DC (p = 0.252). ANOVA analysis revealed that Z-250 VH means were all greater than S-XT, for both top and bottom surfaces, whatever the storage-period in artifcial saliva (p < 0.001). After 180 days of storage, the hardness obtained for S-XT was similar with that at the baseline, for both top and bottom surfaces. While for Z-250 hardness was not signifcantly different from baseline only for top surface, but there was a signifcant decrease observed in hardness for bottom surface., Conclusion: The materials tested showed no evidence of hydrolytic degradation in a signifcant way, in a 6-month storage-time in artifcial saliva. Nanoflled resin presents a monomer conversion comparable to the conventional microhybrid.

Purpose: To evaluate the microtensile bond strength (µTBS) and nanoleakage (NL) of several universal adhesives to eroded dentin (ED), using etch-and-rinse (ER) or self-etch (SE) strategies, and to characterize the surface using two pH cycling models to erode dentin (citric acid and a soft drink). Materials and Methods: Molars were eroded either by soft-drink or citric acid cycling, or were left untreated as control (SD). For each surface, the following adhesives were applied: 1. All-Bond Universal; 2. Ambar Universal; 3. Clearfil Universal; 4. Futurabond U; 5. One Coat 7 Universal; 6. Peak Universal Bond; 7. Prime&Bond Elect; 8. Scotchbond Universal; 9. Tetric n-bond Universal, and 10. Xeno Select. After application of the composite, specimens were sectioned into composite-dentin sticks and tested under tension (0.5 mm/min). Selected sticks from each tooth were used to assess NL. The occlusal dentin surfaces after erosive cycling were examined using SEM. Data were analyzed by three-way ANOVA and Tukey's post-hoc test (α = 0.05). Results: In ED, there was no difference in µTBS and NL between ER and SE strategies (p > 0.61). Most µTBS and NL values obtained for ED were, respectively, lower and higher than those for SD (p < 0.01), being worse for citric acid ED (p < 0.001). Citric-acid-eroded dentin showed more enlarged tubules, with partial loss of peritubular dentin when compared to soft-drink eroded dentin. Conclusion: The different pH cycling models reduced µTBS and increased NL of the composite/eroded-dentin interface; however, in ED, the performance of the universal adhesives did not depend on the adhesive strategy used. [ABSTRACT FROM AUTHOR]