Objective: This study has investigated the influence of BisGMA, BisEMA, BisEMA 30, and two UDMA-based monomers (UDMA and Fit 852), with TEGDMA as co-monomer, on the degree of conversion, water sorption, water solubility, and optical properties of experimental dental composites., Methods: Materials were formulated at 70/30 molar rations using BisGMA, BisEMA, BisEMA 30, UDMA or FIT 852, as base monomers, combined with TEGDMA. 60wt% of silanated-glass particles was added. Degree of conversion (DC) and polymerization kinetics were monitored using Fourier-transformed infrared spectroscopy in the near-IR range. Water sorption (Wsp) and solubility (Wsl) were assessed using mass variation after 60days water storage. Color was evaluated using a digital spectrophotometer, applying the CIELab parameters 24h after dry storage and 60days after water immersion to calculate ΔE values. All data were analyzed using ANOVA and Tukey's test (pre-set alpha=0.05)., Results: The BisGMA-based co-monomer mixture presented the lowest DC (62±1%), whereas BisEMA 30 had the highest DC value (95±2%). The highest Wsp was observed for BisEMA 30 (12.2±0.8%), and the lowest for BisEMA (0.4±0.1%). BisEMA has shown the lowest Wsl (0.03±0.01%) and BisEMA 30 the highest one (0.97±0.1%). The ΔE values showed that BisEMA 30 (7.3 color units) and Fit 852 (3.8 color units) altered the color stability providing ΔE>3.3, which is considered clinically unacceptable., Conclusions: The chemical composition and structure of the base monomer influenced the degree of conversion, water sorption, water solubility, and color stability. Considering the overall results, it is possible to state that the base monomer BisEMA mixed with the co-monomer TEGDMA presented the best performance in terms of all the parameters tested., Significance: The resin matrix composition might influence physical property degradation processes and color stability of dental resin composites. Formulations based on BisEMA seem most promising for materials' development., (Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.)

Objectives: To investigate the influence of nanoscale inorganic content over optical and surface properties of model composites before and after ageing., Methods: Three model composites were formulated with silica fillers in nanoscale of 7 nm (G1), 12 nm (G2) and 16 nm (G3), at 45.5% by weight in a matrix of BisGMA/TEGDMA 1:1. Color coordinates (CIE L*a*b* parameters), color difference (ΔE*), translucency parameter (TP), surface gloss (SG) and surface roughness (SR) were measured before and after ageing procedures of immersion in water and toothbrush abrasion. Surface hardness (SH) were evaluated before and after immersion in absolute ethanol. Results were submitted to two-way ANOVA followed by Tukey's post hoc test performed at a pre-set alpha of 0.05., Results: Regarding CIE L*a*b* parameters, a darkening, a redness and a blueness effect, were respectively detected after water storage for all groups. Smaller filler sizes (G1) had the highest CIE b* values, whereas medium (G2) (p<0.05) had higher values than larger fillers (G3) (p<0.05) either before or after water immersion. Toothbrush abrasion did not produce any significant effect on CIE a* and CIE b* values, however increased CIE L*, decreased TP in addition to produce rougher and matte surfaces in all groups. Filler size did not influence ΔE* (p>0.05), although a tendency towards lower values in smaller filler materials was observed. Ageing after immersion in absolute ethanol decreased SH for all model composites., Conclusions: Filler sizes and ageing procedures influenced the optical and surface properties of the nanostructured composites evaluated in this study., Clinical Significance: Filler size influenced optical and surface properties of resin composites. Materials containing smaller filler size offered improved optical stability and surface properties that can lead to longer maintenance of the restoration's appearance in the oral environment., (Copyright © 2013 Elsevier Ltd. All rights reserved.)

Objectives: The aim of this study was to formulate materials with high color stability and reduced degradation by using photoinitiator systems derived from phosphine oxides alternative to the traditional camphorquinone (CQ)/amine system., Methods: Materials were formulated with the monomers BisGMA and TEGDMA as organic matrix. The photoinitiators tested were CQ+amine (EDMAB), phenylbis(2,4,6-trimethylbenzoyl)phosphine oxide (BAPO), BAPO+EDMAB, diphenyl(2,4,6-trimethylbenzoyl)-phosphine oxide (TPO) and TPO+EDMAB. A 60% mass of silanated glass filler particles was added. Degree of CC conversion was evaluated by Fourier-transformed infrared spectroscopy 10min after photopolymerization. The color properties were evaluated by a digital spectrophotometer, applying the CIELab parameters, either before photoactivation, immediately after photoactivation, 24h after dry storage, and one month after water immersion. Water sorption and solubility were assessed by mass gain or loss after storage in water for 30 days. Data were analyzed using ANOVA and Tukey's test (5%)., Results: Degree of conversion did not differ statistically among all the tested formulations. Regarding color, only groups with TPO presented satisfactory color stability after one month of water storage (ΔE<3.3). Water sorption and water stability did not differ among the groups., Conclusions: Degree of conversion, water sorption and water solubility did not differ among all the tested groups. The TPO-based groups were the only materials with satisfactory color stability after one month of water storage., Clinical Significance: The use of a photoinitiator system containing TPO might improve the color stability of resin composites compared with the traditional CQ/amine system while attaining similar physico-chemical properties for the composite., (Copyright © 2012 Elsevier Ltd. All rights reserved.)

Objectives: The purpose of this study was to evaluate the reactivity and polymerization kinetics behavior of a model dental adhesive resin with water-soluble initiator systems., Methods: A monomer blend based on Bis-GMA, TEGDMA and HEMA was used as a model dental adhesive resin, which was polymerized using a thioxanthone type (QTX) as a photoinitiator. Binary and ternary photoinitiator systems were formulated using 1mol% of each initiator. The co-initiators used in this study were ethyl 4-dimethylaminobenzoate (EDAB), diphenyliodonium hexafluorophosphate (DPIHFP), 1,3-diethyl-2-thiobarbituric acid (BARB), p-toluenesulfinic acid and sodium salt hydrate (SULF). Absorption spectra of the initiators were measured using a UV-Vis spectrophotometer, and the photon absorption energy (PAE) was calculated. The binary system camphorquinone (CQ)/amine was used as a reference group (control). Twelve groups were tested in triplicate. Fourier-transform infrared spectroscopy (FTIR) was used to investigate the polymerization reaction during the photoactivation period to obtain the degree of conversion (DC) and maximum polymerization rate (R(p)(max)) profile of the model resin., Results: In the analyzed absorption profiles, the absorption spectrum of QTX is almost entirely localized in the UV region, whereas that of CQ is in the visible range. With respect to binary systems, CQ+EDAB exhibited higher DC and R(p)(max) values. In formulations that contained ternary initiator systems, the group CQ+QTX+EDAB was the only one of the investigated experimental groups that exhibited an R(p)(max) value greater than that of CQ+EDAB. The groups QTX+EDAB+DPIHFP and QTX+DPIHFP+SULF exhibited values similar to those of CQ+EDAB with respect to the final DC; however, they also exhibited lower reactivity., Significance: Water-soluble initiator systems should be considered as alternatives to the widely used CQ/amine system in dentin adhesive formulations., (Copyright © 2012 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.)

Objective: To investigate the surface integrity of solvent-challenged ormocer-matrix composites, photoactivated by different light exposure modes, through surface-hardness measurements at different periods of time; and to compare such behavior with dimethacrylate-based materials., Methods: One hundred percent ormocer-based matrix (experimental ormocer (ORM)), a commercial mixed dimethacrylate-ormocer-based matrix (Admira (ADR)) and two commercial dimethacrylate-based matrix composites (experimental controls, (Grandio (GRD) and Premise (PRE)) were evaluated. Disk specimens (4 mm × 2 mm) were prepared from each material and light-activated using either a standard (S) or soft-start (SS) light exposure protocol with an LED-curing unit. Top, irradiated surface Knoop hardness (KHN) was measured within the following experimental groups (n=5): Group 1: immediately after exposure; Group 2: after dry and dark storage, Group 3: after storage in distilled water, and Group 4: immersion in absolute ethanol. Hardness of Groups 2-4 were measured after 7 days storage. Immediate hardness values were submitted to Student's t-tests separately for each material. Hardness values after treatments were submitted to two-way ANOVA and Tukey's post hoc test to compare values among different storage media and light exposure mode protocols. Comparisons among materials were described using percentage of hardness change. Statistical testing was performed at a pre-set alpha of 0.05., Results: Immediate hardness values were not affected by the light exposure mode, regardless of the material. In general, exposure mode did not significantly affect hardness after 7 days storage, regardless of storage media or material. After 7 days dry storage, hardness values increased for all materials relative to immediate testing, and decreased after water and ethanol storage, with ethanol showing the greatest effect. The experimental ormocer-based material had the lowest percentage hardness change and thus proved more resistant to solvent degradation than the other materials, regardless of the light exposure method., Significance: Irradiated surface hardness values and surface integrity were unaffected by light exposure mode, regardless of the material tested. The experimental ormocer-based material presented the least change in hardness as a result of solvent challenge than any of the commercial products: ormocer or conventional resin-based, and thus showed better surface integrity., (Copyright © 2010 Academy of Dental Materials. All rights reserved.)

Objectives: To evaluate the effect of amine ratio (ethyl 4-dimethylaminobenzoate, EDMAB) on the maximum rate of polymerization (R(p)(max)), degree of conversion (DC), Knoop hardness (KH), water sorption (Wsp), water solubility (Wsl) and color changes (DeltaE) over time of resin composites formulated with the photoinitiators camphorquinone (CQ), phenylpropanedione (PPD) and CQ-PPD in combination., Materials and Methods: Experimental resin composites were made with photoinitiator:amine ratios of 2:1, 1:1, 1:1.5 and 1:2 by weight. R(p)(max) was evaluated with differential scanning calorimetry (DSC), DC with DSC and Fourier transformed infrared (FTIR) spectroscopy, KH with Knoop indentation, Wsp and Wsl adapted from ISO 4049; and color with a chromameter. The results were analyzed with two-way ANOVA/Tukey's multiple comparison test (p<0.05)., Results: The higher the amine ratio in the composite, the higher was DC, R(p)(max), and KH, and the lower was Wsl, regardless of the photoinitiator type. The use of PPD alone resulted in poorer properties than CQ and CQ-PPD. Many factors seem to affect the color changes and the b-axis data revealed that the higher the amine ratio, the higher was the +b value (yellowing) for CQ and CQ-PPD formulations., Conclusions: Higher amine ratios led to improved polymer properties, but also produced more yellowing in resin composites with CQ and CQ-PPD. The use of PPD alone was not advantageous for producing good final properties when compared to CQ and CQ-PPD.

Objectives: To evaluate the degree of conversion (DC), maximum rate of polymerization (Rpmax), Knoop hardness (KHN) and yellowing (b-value) of resin composites formulated with phenylpropanedione (PPD), camphorquinone (CQ), or CQ/PPD at different concentrations. The hypotheses tested were (i) PPD or CQ/PPD would produce less Rpmax and yellowing than CQ alone without affecting DC and KHN, and (ii) Rpmax, DC, and KHN would be directly related to the absorbed power density (PDabs)., Methods: CQ/amine, PPD/amine and CQ/PPD/amine were used at low, intermediate and high concentrations in experimental composites. Photoinitiator absorption and halogen-light emission were measured using a spectrophotometer, Rp with differential scanning calorimetry (DSC), DC with DSC and FTIR, KHN with Knoop indentation; and color with a chromameter. The results were analyzed with two-way analysis of variance (ANOVA)/Student-Newman-Keul's test (p<0.05). Correlation tests were carried out between PDabs and each of DC, Rpmax and KHN., Results: The PDabs increased with photoinitiator concentration and PPD samples had the lowest values. In general, maximum DC was comparable at intermediate concentration, while Rpmax and KHN required higher concentrations. DC was similar for all photoinitiators, but Rpmax was lower with PPD and CQ/PPD. PPD produced the lowest KHN. Yellowing increased with photoinitiator concentration. PPD did not reduce yellowing at intermediate and/or high concentrations, compared to CQ-formulations. PDabs showed significant correlations with DC, Rpmax and KHN., Conclusion: PPD or CQ/PPD reduced Rpmax in experimental composites without affecting the DC. The use of PPD did not reduce yellowing, but reduced KHN. DC, Rpmax and KHN were dependent on PDabs.

There are few studies that fully characterize the effect of the filler size on the surface, optical and mechanical properties of resin composites. Aim: To determine the influence of the filler size content on surface, optical and mechanical properties before and after accelerated aging. Methods: Seven resin composites were investigated: Filtek Supreme® (3M/ESPE), Estelite Σ Quick® (Tokuyama), Evolu-X® (Dentsply), Esthet-X HD® (Dentsply), Opallis® (FGM), Herculite XRV Ultra® (Kerr) and Filtek Z250® (3M/ESPE). Elastic modulus (EM) and flexural strength (FS) were determined by three-point bending of specimens immersed or not in absolute ethanol for seven days. Roughness (Ra) and gloss (G.U.) analyses were determined before and after ethanol storage for seven days and CIELAB color change (ΔE*) was obtained with a spectrophotometer. Results were analyzed by two-way ANOVA (general linear model) for EM and FS, with repeated measures for roughness and gloss, and one-way ANOVA for ΔE*. All comparisons were performed by Tukey's test (5%). Pearsons' correlation test was performed to determine the correlation between EM, FS, roughness, gloss, and ΔE* with the mean filler sizes. Results: Mechanical properties decreased for all materials when submitted to immersion in ethanol. Increasing filler size gradually increased EM, FS and roughness values; gloss values decreased and didn't significantly affects ΔE*. Nanofiller composites presented higher gloss values than the others. Conclusions: It was possible to determine that the average filler size is a good predictor just for FS and gloss retention. [ABSTRACT FROM AUTHOR]

Though many advances have been made in the development of dental adhesives, the immediate, or short-term, disruption created by stress — due to polymerization of resin composite restorative materials within dental cavities — is still a challenge yet to be completely solved in restorative dentistry. Therefore, the aim of this paper is to present a general overview of the subject, concerning resin composite formulations, origins of stress, clinical consequences of stress development, in vitro methods used for its measurement and methods used to reduce stress magnitudes and rates of development. [ABSTRACT FROM AUTHOR]

Abstract: Objectives: Stress development during the polymerization process continues to be a major factor that limits predictability and longevity of resin composite restorations. This study evaluated the effect of the photoinitiator type on the maximum rate of polymerization , stress development (final stress and maximum rate, ), degree of conversion (DC) and cross-link density (CLD) of materials containing camphorquinone (CQ), phenylpropanedione (PPD) or CQ/PPD. Materials and methods: was evaluated via differential scanning calorimetry (DSC). Contraction force measurement was assessed with a single cantilever device for 5min. The samples were subsequently tested by infrared spectroscopy (FTIR) to evaluate the DC. After, samples were soaked in ethanol to evaluate the swelling coefficient (α) as a way to estimate the CLD. The results were analyzed by one-way ANOVA and Tukey''s test (p =0.05). Results: CQ showed the highest and . PPD produced the lowest DC and the highest α. The mixture CQ/PPD produced statistically lower and than CQ alone, but similar DC and CLD. Conclusion: CQ/PPD reduced the and without a reduction in DC and CLD. Therefore, the use of alternative photoinitiator systems could be a promising way to reduce the stress developed during the composite''s polymerization without affecting the final properties. [Copyright &y& Elsevier]

Regular composites could produce less polymerization stress than resin cements when luting laminate veneers but there is no proper evidence to support this theory. The current study aimed to determine the degree of conversion, volumetric shrinkage, polymerization stress and the resultant elastic moduli of materials currently used for adhesive cementation and to determine possible correlations. The study considered (i) regular resin composites (Admira Fusion, Gradia, Grandioso, Palfique, Sirius Z, Viscalor and Z100) at room and pre-warmed (PW) at 69ºC, (ii) flowable composites (Sigma Flow and Grandioso Flow); (iii) solely light-activated cements (AllCem Veneer, Variolink Esthetic and RelyX Veneer); and (iv) one dual-activated resin cement (SpeedCEM). Degree of conversion (DC, n = 3) was accessed with FTIR 1 h after irradiation. Bonded-disk and Bioman II instruments were used to access polymerization shrinkage strain and shrinkage stress, respectively, for 60 min at 23 ± 1◦C (n = 3). The elastic modulus was determined by 3-point bending flexural test (n = 6). The results were submitted to analyse s of variance, Tukey's, and correlation tests. For regular composites, the pre-warming did not affect DC, shrinkage and modulus but significantly increased the stress magnitude. Correlation tests indicated a significant relationship only between stress and polymerization shrinkage (r = 0.811343). Regular composites can produce less polymerization stress than resin cements when luting laminate veneers. Polymerization stress was dependent on the shrinkage magnitude, but not on the degree of conversion nor the elastic modulus. [ABSTRACT FROM AUTHOR]

Abstract The aim of this study was to determine the influence of the monomer type and photoinitiator systems on the degree of C=C conversion and color stability of model self-adhesive flowable composites (SAFCs). Three sets of flowable composites were formulated varying the monomer type: set 1 (control), with bisphenol-A glycidyl methacrylate and triethylene glycol dimethacrylate (BisGMA/TEGDMA) at 50/50 wt%; set 2, with BisGMA/TEGDMA/bis[2(methacryloyloxy)ethyl]phosphate (2MP) at 30/30/40 wt%; and set 3, with BisGMA/TEGDMA/4-ethyl-methacryloxy-trimetilato anhydride (4-META) at 30/30/40 wt%. For each set, different initiator systems were added: camphorquinone (CQ) + ethyl-4-dimethylamino benzoate (EDMAB); diphenyl(2,4,6-trimethylbenzoyl)-phosphine oxide (TPO); phenylbis(2,4,6-trimethylbenzoyl)phosphine oxide (BAPO); and the combinations CQ + EDMAB + TPO and CQ + EDMAB + BAPO. Degree of C=C conversion was determined by Fourier-transformed infrared spectroscopy with an attenuated total reflectance device (ATR-FTIR). The color stability was determined by CIE 00 color difference formula (∆ E * 00), after water (T 1) and coffee (T 2) storages for 30 days. Data was submitted to two-way analysis of variance (ANOVA) followed by Student-Newman-Keuls test (α = 0.05). Degree of conversion and color stability were dependent on the resin matrix composition and the photoinitiator system. The 2MP-based set showed the highest DC, but also the poorest color stability. For the 4-META-base set, TPO and BAPO produced the highest degree of C=C conversion. The use of BAPO produced the best color stability for the acidic-monomer-based sets. [ABSTRACT FROM AUTHOR]