Search

With the purpose of further reducing surface free energy to achieve better anti-bacterial adhesion effect of fluorinated dimethacrylate (FDMA)/tricyclo (5.2.1.0) decanedimethanol diacrylate (SR833s) based dental resin composites (DS), 1H,1H-heptafluorobutyl methacrylate (FBMA) was used to partially replace SR933s as reactive diluent. According to the degree of substitution, the obtained resin composites were marked as DSF-1 (20 wt.% of SR833s was replaced by FBMA), DSF-2 (40 wt.% of SR833s was replaced by FBMA), and DSF-3 (60 wt.% of SR833s was replaced by FBMA). Bisphenol A glycidyl dimethacrylate (Bis-GMA)/triethylene glycol dimethacrylate (TEGDMA) based resin composite (BT) was used as control. The influence of FBMA concentration on double bond conversion (DC), contact angle, surface free energy, anti-bacterial adhesion effect against Streptococcus mutans (S. mutans), volumetric shrinkage (VS) and shrinkage stress (SS), flexural strength (FS) and modulus (FM), water sorption (WS) and solubility (SL) were investigated. The results showed that FBMA addition could reduce surface free energy from 44.6 mN/m for DS to 32.9 mN/m for DSF-3, and lead to better anti-bacterial adhesion effect (the amounts of adherent bacteria decreased from 2.03 × 105 CFU/mm2 for DS to 6.44 × 104 CFU/mm2 for DSF-3). The FBMA had no negative effects on DC, VS, SS, WS, and SL. Too high a concentration of FBMA reduced FS and FM before water immersion, but the values were still higher than those of BT. [ABSTRACT FROM AUTHOR]

With purpose of preparing Bis-GMA free dental resin composites (DRCs) with anti-adhesion effect against Streptococcus mutans (S. mutans), a new fluorinated dimethacrylate (DFMA) was synthesized and used as base resin of DRCs. Two reactive diluents TEGDMA and SR833s were mixed with DFMA separately to prepare resin matrixes. After mixing with inorganic fillers, two DFMA based DRCs were obtained and named as DT (DFMA/TEGDMA) and DS (DFMA/SR833s) according to the resin matrix composition. Bis-GMA based DRC (BT) was used as control. The double bond conversion (DC), bacteria adhesion, mucin adsorption, contact angle, surface free energy, volumetric shrinkage (VS), shrinkage stress (SS), water sorption (WS) and solubility (SL), flexural strength (FS) and modulus (FM) before and after water immersion were investigated, and all the results were statistically analyzed with ANOVA analysis. The results showed that DT and DS had comparable (ρ > 0.05) surface free energy which was lower than that of BT (ρ < 0.05). Compared with BT, with the same surface roughness (ρ > 0.05), less amount of S. mutans was accumulated on the surface of DT and DS (ρ < 0.05). In all DRCs, the DS had the best resistance to mucin adsorption (ρ < 0.05) due to its high hydrophobicity. Compared with BT, both DFMA based DRCs had advantages such as lower VS and SS (ρ < 0.05), lower WS and SL (ρ < 0.05), and better water resistance. The DS, which had antibacterial adhesion effect, mucin adsorption resistance, lowest VS and SL (ρ < 0.05), and the highest FS and FM no matter before or after water immersion (ρ < 0.05) was considered to have the best comprehensive properties in all DRCs. • Bis-GMA free DRC was prepared using fluorinated dimethacrylate as base resin. • Fluorinated dimethacrylate-based DRCs could have antibacterial adhesion effect. • Fluorinated dimethacrylate-based DRCs had lower shrinkage and shrinkage stress. • Fluorinated dimethacrylate-based DRCs had better mechanical properties. • Fluorinated dimethacrylate-based DRCs had better water resistance. [ABSTRACT FROM AUTHOR]