Search

This study aimed to evaluate the effects of radiotherapy (RT) and chemoradiotherapy (CRT) on the wear and surface roughness of in vitro irradiated human enamel and dentin subjected to abrasive challenge. Enamel and dentin specimens (n = 42) were prepared from teeth donated by healthy patients and those with head and neck cancer who had received radiotherapy (RT) or chemoradiotherapy (CRT). The specimens were categorized into three groups: control, RT, and CRT (n = 14 per group for both enamel and dentin). These samples were subjected to an in vitro abrasive experiment using a brushing machine, followed by wear and surface roughness assessments with a confocal laser scanning microscope conducted before and after the abrasive challenge, considering both exposed and non-exposed areas. Statistical analysis used Shapiro-Wilk tests for normality, Wilcoxon tests for comparing two means, and Kruskal-Wallis tests. A significance level of 5% was adopted. In enamel specimens, wear profile values ​​of CRT and RT groups were not different from the control (p > 0.05). The RT group presents lower step values than the CRT and control groups (p < 0.001). No significant difference in final surface roughness was observed in all groups (p > 0.05). In dentin specimens, no significant difference in wear profile and step was observed in all groups (p > 0.05). However, CRT and RT groups present higher values in final surface roughness (p < 0.001). The exposure to ionizing radiation (associated or not to chemotherapy) influenced the surface roughness of dentin and the wear (step) of enamel after the in vitro abrasive challenge.Trial registration: Ethical procedures were approved by the FORP/USP Research Ethics Committee (CAAE: 61308416.4.0000.5419), and Hospital do Câncer de Barretos/Fundação Pio XII (CAAE: 61308416.4.3001.5437)., Competing Interests: Declarations. Conflict of interest: The authors have no conflicts of interest to declare that they are relevant to the content of this article. The authors declare no competing interests. Ethical approval: This was an in vitro experimental study carried out with human teeth donated to the teeth biobank of the Faculty of Dentistry of Ribeirão Preto—University of São Paulo, Brazil (FORP/USP). All patients signed the donation term. Ethical procedures were approved by the FORP/USP Research Ethics Committee (CAAE: 61308416.4.0000.5419), and Hospital do Câncer de Barretos/Fundação Pio XII (CAAE: 61308416.4.3001.5437), as a co-participating institution in teeth donation. Furthermore, we declare that we follow all the guidelines of the Declaration of Helsinki. All eligible participants or legal guardians were informed about the nature of the study and the potential risks and benefits of their participation, signing an informed consent form., (© 2024. The Author(s), under exclusive licence to Springer-Verlag GmbH Germany, part of Springer Nature.)

This study aimed to assess the in vitro effects of re-irradiation on enamel and dentin properties, simulating head and neck cancer radiotherapy retreatment. Forty-five human permanent molars were classified into five groups: non-irradiated; irradiated 60 Gy, and re-irradiated with doses of 30, 40, and 50 Gy. Raman spectroscopy, scanning electron microscopy (SEM), and energy dispersive x-ray spectroscopy (EDS) were employed for analysis. Raman spectroscopy assessed intensity, spectral area, and specific peaks comparatively. Statistical analysis involved Kolmogorov-Smirnov and One-Way ANOVA tests, with Tukey's post-test (significance level set at 5%). Significant changes in irradiated, non-irradiated, and re-irradiated enamel peaks were observed, including phosphate (438 nm), hydroxyapatite (582 nm), phosphate (960 nm), and carbonate (1070 nm) (p < 0.05). Re-irradiation affected the entire tooth (p > 0.05), leading to interprismatic region degradation, enamel prism destruction, and hydroxyapatite crystal damage. Dentin exhibited tubule obliteration, crack formation, and progressive collagen fiber fragmentation. EDX revealed increased oxygen percentage and decreased phosphorus and calcium post-reirradiation. It is concluded that chemical and morphological changes in irradiated permanent teeth were dose-dependent, exacerbated by re-irradiation, causing substantial damage in enamel and dentin., (© 2024. The Author(s), under exclusive licence to Springer-Verlag GmbH Germany, part of Springer Nature.)