Search

Objective: This study evaluated the effect that different techniques for removing dental caries had on the strength of the microtensile bond to caries-affected human dentine created by three bonding agents., Materials and Methods: Forty-five human molar teeth containing carious lesions were randomly divided into three groups according to the technique that would be used to remove the caries: a conventional bur, an Er:YAG laser or a chemo-mechanical Carisolv(®) gel (n=15). Next, each of the three removal-technique groups was divided into three subgroups according to the bonding agents that would be used: Clearfil(®) SE Bond, G-Bond(®), or Adper(®) Single Bond 2 (n=5). Three 1mm(2) stick-shaped microtensile specimens from each tooth were prepared with a slow-speed diamond saw sectioning machine fitted with a diamond-rim blade (n=15 specimens). For each removal technique one dentine sample was analysed using scanning electron microscopy., Results: There were statistically significant differences in the resulting tensile strength of the bond among the techniques used to remove the caries and there were also statistically significant differences in the strength of the bond among the adhesive systems used. The etch-and-rinse adhesive system was the most affected by the technique used to remove the caries; of the three techniques tested, the chemo-mechanical removal technique worked best with the two-step self etch adhesive system., Conclusion: The bond strength values of the etch-and-rinse adhesive system were affected by the caries removal techniques used in the present study. However, in the one- and two-step self etch adhesive systems, bond strength values were not affected by the caries removal techniques applied. While a chemo-mechanical caries removal technique, similar to Carisolv(®), may be suggested with self etch adhesive systems, in caries removal techniques with laser, etch-and-rinse systems might be preferred., Clinical Significance: Caries removal methods may lead to differences in the characteristics of dentine surface. Dentine ultra structure generally affects the bonding of adhesive materials commonly used in restorative dentistry. Whereas etch-and-rinse system, like the ones used in the present study, are affected by these changes, the self etch systems are not affected. Hence, clinicians may opt for caries removal methods and systems appropriate for each patient and practice., (Copyright © 2012 Elsevier Ltd. All rights reserved.)

The aim of this study was to evaluate the mineral content of dentin prepared using an Er,Cr:YSGG laser at four different power settings, acid etching, and air abrasion. The study teeth comprised 35 molars which were randomly divided into seven equal groups. The occlusal third of the crowns were cut with a slow-speed diamond saw. The groups were as follows: group A, control group; group B, dentin etched with 35% buffered phosphoric acid for 30 s; group C, dentin abraded at 60 psi with 50-µm aluminium oxide for 1 s; groups D-G, dentin irradiated with the Er,Cr:YSGG laser at 1.50 W (group D), 2.25 W (group E), 3.00 W (group F), and 3.50 W (group G). The levels of Mg, P, Ca, K and Na in each dentin slab were measured by inductively coupled plasma-atomic emission spectrometry (ICP-AES). Data were analysed by one way analysis of variance and Tukey HSD tests. There were no significant differences between the groups in the levels of Ca, P and Na, and the Ca/P ratio (p>0.05); however, there were significant differences in the levels of K (p<0.001) and Mg (p=0.13). In addition, the levels of Mg in the air abrasion group were higher than in the other groups (p<0.01). Etching with the Er,Cr:YSGG laser system, air abrasion and acid etching did not affect the levels of Ca, P and Na, or the Ca/P ratio, in the dentin surface.

Purpose: The purpose of this study was to evaluate the effect of age of dentin and enamel on the microtensile bond strengths of a glass-ionomer based, all-in-one, single-step, self-etching adhesive system (Reactmer Bond, RB) and an antibacterial, two-step self-etching primer system (ABF Bond, ABF)., Materials and Methods: Extracted molars from 3 age groups (20 to 25, 35 to 40, and 50 to 55 years) were used. Enamel was removed from the occlusal surfaces of the teeth, and the entire flat surfaces were covered with composite resin (4 mm in height) following application of bonding agents. The bonded specimens were thinly sectioned parallel to the long axis of the tooth into 0.87 +/- 0.03 mm2 rectangular sections, resulting in 6 to 7 enamel specimens and 10 to 15 dentin specimens per tooth. The specimens were subjected to the microtensile test at a crosshead speed of 1 mm/min. The data were analyzed by Univariate ANOVA, Tukey HSD, and regression analysis., Results: The bond strength of ABF to both enamel and dentin was higher than the bond strength of RB. Bond strengths of ABF to dentin were significantly higher than the bond strengths to enamel (p < 0.05). The 35- to 40-year age group of ABF showed the highest bond strength of all. In RB dentin groups, 34% of specimens showed cohesive failure in composite resin material., Conclusion: Bond strength values to enamel were not affected by age of teeth in either bonding system. Dentinal bond strength using ABF changed according to age of the teeth. Age did not affect bond strength values of RB to dental hard tissues. However, the high number of cohesive failures in Reactmer paste indicated low tensile strength of the material.

This study evaluated the temperature rise in two different adhesive (Clearfil SE Bond [CSEB] and EBS-Multi [EBSM]) and composite systems (Clearfil AP-X [CAPX,] Pertac II [PII]) by the same manufacturer when illuminated by four different light sources: Light-emitting diode (LED), Plasma arc curing (PAC), high intensity quartz tungsten halogen (HQTH) and quartz tungsten halogen (QTH). Forty dentin disks were prepared from extracted premolars. These dentin disks were placed in apparatus developed to measure temperature rise. Temperature rise during photopolymerization of adhesive resin and resin composite was then measured. The mean values of temperature increases for adhesive and resin composites did not differ significantly (p=0.769). The highest temperature rise was observed during photopolymerization of EBSM with PAC (5.16 degrees C) and HQTH (4.28 degrees C), respectively. Temperature rise values produced by QTH (1.27 degrees C - 2.83 degrees C for adhesive resin; 1.86 degrees C - 2.85 degrees C for resin composite) for both adhesive and resin composites were significantly lower than those induced by PAC and HQTH (p<0.05). However, these values were significantly higher than those produced by LED (1.16 degrees C - 2.08 degrees C for adhesive resin; 1.13 degrees C - 2.59 degrees C for resin composite). Light sources with high energy output (PAC and HQTH) caused significantly higher temperature rise than sources with low energy output (QTH and LED). However, in this study, no temperature rises beneath 1-mm dentin disk exceed the critical 5.6 degrees C value for pulpal health.

The purpose of this study was to evaluate the effect of simulated intrapulpal pressure on the shear bond strength (SBS) of a self-etching bonding system (Clearfil Liner Bond II) to both enamel and dentine surfaces. Forty-two caries-free human molar teeth were randomly assigned to two equal groups (n=21). One group of 21 teeth was connected to a special pulpal pressure machine, which is developed to simulate in vivo conditions. The buccal and lingual surfaces of the teeth were prepared with a diamond wheel to create flat dentine and enamel surfaces. A self-etching bonding system was then applied under pulpal pressure and 2.5 mm diameter composite cylinders were bonded to the prepared surfaces. The samples were then stored in distilled water at room temperature for 24 h under pulpal pressure before SBS was tested. The second restored group was used as a control and the teeth were not connected to the pulpal pressure apparatus during material application and test procedures. They were stored for 24 h in distilled water at room temperature before the SBS test. Fracture analysis of the enamel and dentinal surfaces was performed using a stereomicroscope. Shear bond strength values to dentine was significantly reduced with pulpal pressure (P < 0.001). However, in the enamel, SBS was increased (P < 0.001). In the control group, the SBS values to dentine and enamel did not show any significant difference (P > 0.05). Based on these results, it can be concluded that further analysis of enamel histology and bonding mechanisms are needed.

Five current dentin adhesives were evaluated for their ability to bond to caries-affected dentin. The materials were: total etch [Solid Bond (SB)], two self-etch [Clearfil SE Bond (CSE), Etch and Prime (EP)], two one bottle [Prime and Bond 2.1 (PB), One Coat Bond (OCB)]. Sixty extracted molar teeth with proximal caries (mesial or distal) extending into mid-dentin were used. By grinding normal and caries-affected proximal surfaces, flat dentin surfaces were obtained. The surfaces were then bonded with each adhesive system and composite resins were added to the surfaces by packing the material into a cylindrical-shaped plastic matrix with an internal diameter of 2.5 mm and height of 3 mm. Shear bond testing was performed following 10 days incubation of specimens in distilled water at 37 degrees C. Results were analysed by Kruskal-Wallis ANOVA, and Mann-Whitney U multiple comparison test and Wilcoxon rank tests. The results obtained with CSE, SB, and EP were similar in caries affected and normal dentin (P > 0.05). But bonds made to normal dentin with OCB and PB were lower (P < 0.05) than bonds to caries-affected dentin. Bonding to caries-affected dentin with CSE (24.49 +/- 5.38), SB (21.49 +/- 9.15), and EP (21.19 +/- 9.17) showed shear bond strengths higher than OCB (17.43 +/- 9.78) and PB (14.10 +/- 7.94) (P < 0.05). Bonding to normal dentin with CSE (29.91 +/- 8.95) was the highest (P < 0.05). SB (21.17 +/- 5.41) and EP (17.45 +/- 6.21) showed shear bond strengths higher than OCB (11.99 +/- 10.15) and PB (10.57 +/- 4.56) (P < 0.05).

The aim of this study was to evaluatein vitrodentine permeability evaluation of 2-Hydroxyethyl methacrylate (HEMA)-based desensitizing products using split-chamber model followingin vivoapplication in the dogs for three experimental time periods of 1 week, 1 month and 3 months. Buccal enamel of upper and lower canines of nine young dogs was removed and flat dentinal surface was obtained using a water-cooled diamond bur. The dentinal surface divided into four quarters, three experimental and a control. Health-Dent and Gluma Desensitizing agent and Single bond were applied to respective quarters of one tooth, according to manufacturers’ instructions. The last quarters were left as control without any applications. For the each experimental period, 10 dentine samples from each group including control were used to measure the hydraulic conductance values. The dentine discs were placed pulp-side down in a split-chamber device in which the plastic spacers containing the rubber 0 rings have a surface area of 1 mm2 and permeability was measured by fluid filtration. The data were expressed as hydraulic conductance (Lp). Differences in dentine permeability obtained for the desensitizing agents against the control were tested for statistical significance using Kruskal–Wallis one-wayanovaand Bonferroni-adjusted Mann–WhitneyU-tests. Differences in permeability in three time periods for each desensitizing agent were analysed using Friedman'sanovaand Wilcoxon signed rank tests. All desensitizing applications caused decreased Lp values compared with the control Lp value at the end of 1 week. In the 1-month samples, between the Lp values of Single bond and control, no statistical difference was found (P > 0·05). At the end of the 3-month period, the Gluma Desensitizing agent had the lowest the Lp value (P < 0·05). The result of this study is that the topical application of desensitizing agents led to decrease in dentine permeability in the dog model. The Gluma Desensitizing agent provide the more lasting tubule-occluding effect than the other material tested in this model. [ABSTRACT FROM AUTHOR]

Ozturk B, Özer F, Belli S. An in vitro comparison of adhesive systems to seal pulp chamber walls. International Endodontic Journal, 37, 297–306, 2004. To compare in vitro the sealing properties of five different dentine adhesive materials (Prime&Bond NT (PBNT); Prompt L-Pop (PLP); Clearfil SE Bond (CSEB); Scotchbond Multi Purpose Plus (SMPP); EBS-Multi (EBSM)) inside the pulp chamber. Seventy-five recently extracted human molar teeth were used. The roof of the pulp chambers and roots were removed under water cooling. Pulp tissue was removed, and the canal orifices were sealed. The pulp chambers were then treated with 5% sodium hypochlorite (NaOCl) for 1 min. The teeth were randomly divided into five groups of 15 teeth each. Adhesive systems were applied to the pulp chamber walls according to the manufacturers' instructions. The samples were connected to Plexiglass plates, and a fluid filtration method was used for quantitative evaluation of leakage. Measurements of fluid movement were made at 2-min intervals for 8 min. The quality of seal of each specimen was measured immediately, after 24 h, 1 week and 1 month. The data were statistically analysed by repeated-measurements multivariate anova, Friedman test, Wilcoxon signed rank test, Kruskal–Wallis of one-way anova and Mann–Whitney U-tests. The pulp chamber wall with and without NaOCl and resin–dentine interfaces of specimens were observed under a scanning electron microscope (SEM). The leakage values of the materials were significantly different at different measurement periods. In all groups, leakage values decreased with time ( P < 0.05). PBNT and PLP had the least leakage during immediate measurements ( P < 0.05). After 1 month, leakage of all adhesive systems was not significantly different ( P < 0.05). SEM observation of pulp chamber walls demonstrated that the irregular dentine surface without smear layer was present in the nontreated group. However, NaOCl application removed the collagen fibrils leaving the dentine surface smooth. At resin–dentine interfaces of specimens, no hybridization zone was observed. None of the materials had created a perfect seal to the pulp chamber walls. PBNT and PLP had better sealing over the short term, but over the long term, there were no differences between the materials. [ABSTRACT FROM AUTHOR]