Search

Diamond exhibits large application potential in the field of power electronics, owing to its excellent and desirable electronic properties. However, the main obstacles to its development originate from the small‐sized single‐crystal wafers and the instability of the electrical conductivity. This work presents a metal‐oxide‐semiconductor field‐effect transistor (MOSFET) on a diamond substrate derived from a five‐inch (110) highly preferred polycrystalline diamond film. The MOSFETs with excellent performance are fabricated by combining an H‐terminated channel and an epitaxially grown boron‐doped layer as the source/drain contacts of the diamond devices. According to the electrical statistical results of ≈110 devices on the polycrystalline diamond substrate, 44% of devices show normally‐off operation with a maximum current density of 400 mA mm−1, while 56% of devices demonstrate normally‐on operation with a maximum current density of 525 mA mm−1. The normally‐off characteristics are more related to the higher amounts of nitrogen concentration than the grain boundaries. The stable boron‐doped source and drain provide a high concentration of holes, which facilitate transport in the surface p‐type channel induced by the H‐termination. The characteristics of the MOSFETs are inspiring for the fabrication of complementary inverter circuits on large diamond wafers. [ABSTRACT FROM AUTHOR]

This letter reports a high drain current density and normally-off operation metal-oxide-semiconductor field-effect transistors (MOSFETs) with a gate insulator of 100 nm-Al2O3. A heavily boron-doped layer as the source/drain region was deposited on a (110) polycrystalline diamond substrate to achieve a low ohmic contact resistance. The MOSFETs demonstrate a maximum current density of −400 mA mm $^{-{1}}$ normalized by gate width and a maximum current density of $- 2000\,\,\mu \text{m}$ mA mm−1 normalized by gate length and gate width, which are the highest values for normally-off diamond FETs. The Grain boundaries (GBs) and the nitrogen impurities ($\sim {3}\,\,\times \,\,{10}^{{17}}$ cm $^{-{3}}$) as ionized donors in the channel region caused the threshold voltage (${V}_{\text {th}}$) to shift in the negative direction, exhibiting normally-off characteristics. This technique provides a promising method to achieve high-performance diamond devices, and help improve safety and save energy in switching systems. [ABSTRACT FROM AUTHOR]

The direct-current arc plasma jet method is advantageous for the rapid deposition of large-area self-supporting diamond films. However, dark defects tend to be generated during the growth process, significantly affecting the performance of the diamond. In this study, we use the direct-current arc plasma jet method to prepare transparent and translucent samples. Subsequently, we compare their optical, thermal, and mechanical properties and analyze the differences in their performances via microstructure and defect analyses. The results indicate that the transparent diamond samples exhibit excellent optical and thermal properties, with a transmittance of 68.4 % at a wavelength of 10.6 μm and a thermal conductivity similar to that of type-IIa single crystal diamond (i.e. 2002 W/(m·K)). Meanwhile, the translucent diamond exhibits outstanding mechanical properties, with a fracture strength of 984 MPa. Characterization results based on electron backscatter diffraction and X-ray computed tomography suggest that a preferred orientation along the (220) planes is conducive to the densification growth of the samples, thereby enhancing their optical and thermal properties. However, the generation of numerous twins results in interlocking between grains, which improves sample's mechanical properties but introduces porosity and impurities, thus deteriorating its optical and thermal performance. [Display omitted] • Optical and thermal diamond films were deposited by DC-arc plasma jet CVD with growth rates >6 μm/h. • Strong (220) texture and numerous twins can improve optical transmittance and fracture strength, respectively. • X-ray CT was used to reveal defects distribution and content within diamond samples. [ABSTRACT FROM AUTHOR]

Diamond is a highly attractive material for many applications in material science, engineering, chemistry, and biology because of its favorable properties. The preparation of large-area freestanding diamond plate can greatly reduce the production cost of diamond and promote the industrialization of diamond. In this study, the dual-magnetic field mode was introduced to optimize the magnetic field distribution in direct current arc plasma jet chemical vapor deposition (DC Jet CVD) system, and the arc plasma was effectively controlled under the coupling of electric field and magnetic field. The uniformity of the plasma distribution above the substrate surface is significantly improved, resulting in long-term stable and uniform growth of the 8-inch freestanding diamond plate. The influence of dual-magnetic field mode on magnetic field generation, arc feature, and reactive group distribution was studied. 8-inch freestanding diamond plates with an average thickness of 2.8 mm were prepared by dual-magnetic controlled DC Jet CVD. The results showed that the 8-inch diamond plate preferred a high (220) orientation, and the deviation of thickness of which was around 10 % of the averaged values. Raman spectroscopy of diamond revealed a 6.6 cm−1 of full width at half maximum (FWHM) and calculated 1.20 GPa compressive stress in the 8-inch diamond plate. By means of mechanical and thermal property measurements, the large area diamond plate shows a robust structure with the average values of three-point bending fracture strength of 987.2 MPa, and extremely high thermal conductivity of 1797.8 W/(m·k) as well. The deviation of three-point bending fracture strength and the thermal conductivity over the 8-inch diamond plate was around 7.9 % and 12.6 % of the respective averaged values. [Display omitted] • A uniform and robust 8-inch diamond plate was prepared using a dual-field DC arc CVD system. • The average three-point bending fracture strength of the 8-inch diamond plate was 987.23 MPa, and the average thermal conductivity was 1797.80 W/(m•K). • The effect of dual magnetic field mode on the distribution of arc morphology and arc plasma groups was analyzed using a high-speed camera and filter. [ABSTRACT FROM AUTHOR]

Here, thermal stabilities for Ohmic contact properties of Pt, Au, and Pd on the same hydrogen-terminated diamond (H-diamond) epitaxial layer are investigated. A long-term annealing process is performed with an annealing temperature and time of 400 °C and 8 h, respectively. Before annealing, good Ohmic contact properties are observed for only two contacts of the Pt/H-diamond and Pd/H-diamond with specific contact resistivity (ρC) values of 2.7 × 10−3 Ω cm2 and 2.6 × 10−4 Ω cm2, respectively. After long-term annealing, all three contacts on the H-diamond show good Ohmic contact properties. The ρC values for the Pt/H-diamond and Au/H-diamond are 3.1 × 10−2 Ω cm2 and 4.2 × 10−4 Ω cm2, respectively. They are higher than that of the Pd/H-diamond (1.1 × 10−4 Ω cm2). Therefore, low ρC and good thermal stability for the Pd/H-diamond are achieved. This is meaningful for pushing forward the development of H-diamond-based electronic devices for high-temperature applications. [ABSTRACT FROM AUTHOR]

In this study, standard diamond bars were prepared using an ultra-thick diamond plate, and the bars had sizes consistent with the International Organization for Standardization (ISO) 14704:2016(E) three-point bending method for measuring the fracture strength. Ultra-thick diamond plate with dimensions of 125 mm (diameter) × 6.5 mm (thickness) were deposited using direct current arc plasma jet chemical vapour deposition. After cutting, grinding, and polishing, 12 diamond bars meeting the requirements of the ISO standard were prepared (36 mm × 4 mm × 3 mm) and tested for fracture strength using the cited ISO standard and elastic modulus using deflection measurements. The fracture strength of the ultra-thick diamond plate was found to be 580 ± 66 MPa. In addition, for comparison, the fracture strengths of standard ZnS, sapphire, and alumina were also analysed. Crucially, this is the first report of the fracture strength of standard-sized diamond plate. The effects of the defects and grain size on the crack formation and failure of the diamond film were analysed. The diamond's fracture strength was affected by the sample thickness, which caused the gradual accumulation of defects as this dimension increased, but not by its length and width. The elastic moduli of sapphire and alumina were compared. Overall, the measurement of the fracture strengths of ultra-thick diamond plate via the ISO standard is important for industrial applications. [ABSTRACT FROM AUTHOR]

In order to realize the practical use of diamond as a semiconductor material, large-area single-crystal diamond wafers with uniform quality are required. Mosaic growth is an effective method to produce inch-grade single-crystal diamonds. However, the quality of the wafer is limited by the junction interface seriously, because cracking occurs easily due to the high internal stress. In this paper, the repetition growth method was adopted to grow mosaic splicing single-crystal diamond without polycrystalline diamond interface. The high-quality single crystal diamond slices were reduplicated by microwave plasma chemical vapor deposition (MPCVD). The substrates were obtained by cutting a piece of CVD diamond along a plane perpendicular to 〈001〉 (with a (100)-oriented surface). The evolution of the growth characteristics around the junction of the substrates at different stages was studied. The results show that the surface of the epitaxial layers gradually evolves from blurry terraces to a regular well-ordered step flow. When the substrates have the same deviation direction and the off-direction angles are within 3°, the junction of the substrates can connect smoothly. Raman mapping shows that there is a mixture of tensile stress and compressive stress near the junction. As the thickness of the epitaxial layer increases from 280 μm to 560 μm, the range of tensile stress near the joint area expands from 85 μm to 150 μm, the maximum tensile stress increases from 0.08 GPa to 0.16 GPa. In addition, the value of FWHM in the X-ray rocking curve is less than 2.80 cm−1 around the junction, which indicates good crystal quality. [Display omitted] • The evolution of growth characteristics around the junction in the mosaic diamond was studied. • The mosaic boundary evolved from blurry terraces to a well-ordered step flow and finally connected. • The lowest value of tensile stress near the joint area was reported as the film thickness increased. • The larger FWHM of Raman peak around the junction is caused by the increased tensile stress. • The "inherit" effect of NV content of the epitaxial layer was observed for the corresponding substrate. [ABSTRACT FROM AUTHOR]

Lift-off is a promising method to prepare thin, high-finish, and freestanding large-area single crystal and polycrystalline diamonds. However, accurate control of the damage layer characteristic to achieve both stress release and lift-off process is difficult. In this work, high-energy C+ was implanted in single crystal diamond and polycrystalline diamond to create subsurface damage. The defect behavior and structural transformation of the ion implantation and annealing process were investigated. The homoepitaxial growth was subsequently carried out and the epitaxial layer was lifted off from the substrate by selectively etching the damaged layer. The results show that the cap layer and the substrate (below the damage layer) keep the sp3 carbon structure before and after annealing, which is confirmed by the atomic-scale electron energy loss spectroscopy (EELS). The high-resolution transmission electron microscopy (HRTEM) images show that after annealing at 1000 °C for 1 h, the damaged layer was transformed from amorphous carbon to a mixture of graphite and amorphous carbon, providing the damaged layer that could be removed by electrochemical solution. Meanwhile, the distorted diamond area was changed to a sharp interface, which ensures the low roughness of the substrate surface after the lift-off process. After etching for 30 h, a freestanding polycrystalline diamond film with a thickness of 100 μm and a surface roughness of 1.68 nm was obtained. The roughness of the lift-off substrate surface is 1.10 nm, indicating the epitaxial growth can be repeated directly without polishing. [Display omitted] • The defect behavior and structural transformation of the high-energy C+ implanted diamonds were investigated. • The stress state of the diamonds before and after ion implantation and after lift-off process were evaluated. • A 100 μm-thick freestanding polycrystalline diamond film with a surface roughness of 1.68 nm was successful obtained. [ABSTRACT FROM AUTHOR]