Minority carrier lifetimes in doped and undoped mid-wave infrared InAs/InAsSb type-II superlattices (T2SLs) and InAsSb alloys were measured from 77-300 K. The lifetimes were analyzed using Shockley-Read-Hall (SRH), radiative, and Auger recombination, allowing the contributions of the various recombination mechanisms to be distinguished and the dominant mechanisms identified. For the T2SLs, SRH recombination is the dominant mechanism. Defect levels with energies of 130 meV and 70 meV are determined for the undoped and doped T2SLs, respectively. The alloy lifetimes are limited by radiative and Auger recombination through the entire temperature range, with SRH not making a significant contribution. [ABSTRACT FROM AUTHOR]

Tunnel junctions in cascaded structures must provide adequate barriers to prevent carriers from leaking from one emission region to the next without first recombining radiatively, while at the same time remain low in tunneling resistance for current recycling. In this study, a variety of tunnel junction designs are compared in otherwise identical four stage InAs/GaSb superlattice light emitting diodes, which past studies have found hole confinement to be problematic. Here we used GaSb on the p-side of the junction, while varying materials on the n-side. The authors find Al0.20In0.80As0.73Sb0.27 tunnel junctions function best due to the low set of the conduction band; Ga0.75In0.25As0.23Sb0.77 also works well, though is more resistive due to a reduced set of the conduction band; and GaSb, while giving good hole confinement, results in a very resistive junction. Graded superlattice junctions can also work well, though they show sensitivity to doping levels, and present some challenges in growing strain-free. [ABSTRACT FROM AUTHOR]