Search

Ho-doped and Ho,Pr co-doped BaF 2 crystals were grown using the temperature gradient technique. The absorption spectra, fluorescence spectra, and fluorescence lifetimes were measured and analyzed. For Ho-doped BaF 2 , 1.0 at.% Ho:BaF 2 showed the best luminescence performance in the 3 μm band. After co-doping with Pr3+, the lower-level lifetime of Ho3+ ions in the 3 μm band was significantly reduced, while the upper laser level lifetime was minimally affected, indicating that Pr3+ ions can be effectively used as a deactivating ion of Ho3+ ions in the BaF 2 matrix. For 1.5 at.% Ho, 0.1 at.% Pr:BaF 2 , the lifetime ratio of the upper and lower levels was 0.47, effectively realizing population inversion. • Ho-doped BaF 2 , 1.0 at.% Ho:BaF 2 showed the best luminescence performance in the 3 μm band. • Pr3+ ions can be effectively used as a deactivating ion of Ho3+ ions in the BaF 2 matrix. • For 1.5 at.% Ho, 0.1 at.% Pr:BaF 2 , the lifetime ratio of the upper and lower levels was 2:7, effectively realizing population inversion. [ABSTRACT FROM AUTHOR]

High quality Pr3+ single-doped PbF 2 and Pr3+/Yb3+ co-doped PbF 2 single crystals were grown by temperature gradient technique (TGT). By co-doping Yb3+ ion as Pr3+ ions sensitizer, the visible light emission can be regulated and the largest luminescence branching ratio can be switched from red-orange to blue-green light. Besides, when Pr3+ ions doping concentration is as low as possible, the blue light self-absorption effect can be weakened, which is beneficial to high-efficiency blue laser output. Moreover, the broad band emission around 1.3 μm from 1G 4 energy level can be observed in the Pr3+/Yb3+:PbF 2 crystal with the low maximum phonon energy for the first time. Absorption, emission spectra and luminescence mechanism are well analyzed by the energy transfer process and J-O theory. The laser upper energy level lifetime of Pr3+ ions has a great increase by Yb3+ ion effect. These advantageous spectroscopic characteristics show that the Pr3+/Yb3+:PbF 2 crystal might be potential laser gain materials for blue-green and ∼1.3 μm near-IR laser operation. • By co-doping Yb3+ ion as sensitizer for Pr3+ ions, the visible light emission can be regulated and the largest luminescence component ratio can be changed from red-orange light to blue-green light. • When doping concentration of Pr3+ ion is as low as possible, the self-absorption effect of blue light can be weakened, which is beneficial to high-efficiency blue laser output. • The broad band emission around 1.3 μm from 1G 4 energy level can be observed in the Pr3+/Yb3+: PbF 2 crystal with the low maximum phonon energy for the first time. [ABSTRACT FROM AUTHOR]

Abstract: Spectroscopic measurements of the calcium niobate CaNb2O6 single crystal doped with samarium ions were performed. Polarized absorption and emission spectra as well as luminescence decay curves of this material were recorded as a function of temperature in the 5–300K temperature region. Analysis of low temperature spectra made it possible to determine energies of crystal field components of Sm3+ multiplets involved in the excitation and luminescence phenomena. Number of crystal field levels derived implies that Sm3+ ions in the CaNb2O6 host are accommodated in several different sites. Radiative lifetime of the 4G5/2 metastable level determined based on the Judd–Ofelt analysis of room temperature absorption spectra amounts to 777μs, a value close to that of luminescence lifetime determined from luminescence decay curve. Energy transfer between the NbO6 group and samarium ions was observed in wide temperature range. Intense luminescence related to the 4G5/2→6H7/2 and 4G5/2→6H9/2 transitions centered at 610nm and 660nm, respectively, combined with strong absorption band near 404nm that matches perfectly the pump light provided by commercial InGaN/GaN diode lasers points at a potential of CaNb2O6:Sm3+ for the design of all-solid-state visible lasers. [Copyright &y& Elsevier]

Abstract: Yb-doped PbClF crystals were obtained by a modified Bridgman method. Broadband emission (FWHM=58nm) with long lifetime (5.33ms) was observed in 2.0% Yb3+-doped PbClF crystals. The Stark splitting of Yb3+ 2F7/2 level was calculated to be 801cm−1 in 0.5% Yb3+-doped PbClF crystals, and the corresponding population of lower laser level is about 2.13%. All the results indicated that Yb-doped PbClF crystals should be a promising material to ultrashort pulses output at 1.0μm. [Copyright &y& Elsevier]