Poly(methyl methacrylate) films and poly(methyl methacrylate)/fullerene composite films were fabricated by casting from toluene solutions. The mass fraction of fullerene (C60) was varied from 0.05-3 wt. %. The effect of the fullerene (C60) content on the thermal degradation parameters of the composite films was evaluated by thermogravimetric (TG) analysis. It was found that the incorporation of C60 improved the thermal stability of the polymers. The films eventually decomposed in three stages. Incorporation of fullerene caused a change in the distribution of mass loss over the stages of degradation in comparison with the pristine polymer. Using differential scanning calorimetry (DSC), the phase transitions from the glassy state to the elastic one was studied for the examined polymeric materials. New data relating to the effect of C60 on the glass transition temperature of composites with low weight fractions of filler were obtained. Specifically, for films containing up to 0.1 wt. % of C60, a single glass transition temperature was found, whereas for composites with a higher concentration of filler, two glass transition temperatures were recorded. [ABSTRACT FROM AUTHOR]

The particle-size distribution in silica powder prepared by the sol-gel method has been determined by dynamic light scattering analysis. The average diameter of the particles was found to be 250 nm. Using a low-temperature nitrogen adsorption-desorption technique, it was found that the synthesised powder may be referred to as mesoporous materials. Polystyrene/silica composite films were fabricated by casting from o-xylene solutions. It was found, using thermogravimetry, that incorporation of silica leads to an increase in both the onset temperature of polymer degradation and in the temperature at which the maximum rate of weight loss occurs. Using differential scanning calorimetry, the phase transitions from the glassy state to the elastic one were studied for the polymeric materials. New data relating to the effect of silica on the glass-transition temperature, Tg, of composites with a low weight fraction of SiO2 were found. Specifically, we found a non-monotonic concentration dependence of the value of Tg. The present results advocate for employing silica as an effective filler for producing polymer composites with enhanced thermal properties. [ABSTRACT FROM AUTHOR]