Search

The addition of superelastic shape memory alloy fibers (SMAF) into engineering cementitious composites (ECC) can create a new type of SMAF-ECC composite material with good self-recovery and energy dissipation performance, which is very suitable for seismic structures. In this study, 10 groups of beam specimens with different volume contents of SMAF were fabricated, and the bending performance, deflection recovery and energy dissipation ability of these beams were studied through three-point bending cyclic loading tests. The failure mode, peak load, load–deflection curve, crack width and other indicators of the specimens were analyzed, and the relationship expression between fiber content and bending strength was established by fitting analysis. The results show that adding SMA fibers can significantly improve the peak load of ECC beams, with a maximum increase of 48.31%. The knotted SMA fibers can fully exert their superelasticity, providing the beam specimens with crack self-closing and deflection recovery ability. When the volume content of SMA fibers is 0–0.6%, the bending strength, energy dissipation ability and deflection recovery ability of the composite material beams increase with the increase in fiber content. When the volume content of SMA fibers is 0.6–1.0%, the above indicators decrease with the increase in fiber content. The suggested equations can well reflect the relationship between fiber content and beam bending strength. The research results of this paper provide theoretical support for the engineering application of SMAF-ECC composite materials. [ABSTRACT FROM AUTHOR]

Combining Engineered Cementitious Composites (ECC) with shape memory alloy (SMA) fibers can form SMA fiber reinforced ECC (SMAF-ECC) that has excellent deformation recovery and energy dissipation capabilities. Substituting some of the tensioned concrete with this new composite material, along with steel bars, is expected to significantly improve the seismic energy dissipation and self-recovery capabilities of traditional reinforced concrete components. However, a reliable bond between steel bars and SMAF-ECC is critical to ensure their synergistic performance. In this paper, the failure mode and bond strength of steel bars and SMAF-ECC were studied through direct tensile tests, and the influence factors such as steel bar diameter, bond length, and SMAF volume fraction were analyzed. A bond-slip constitutive model for steel bars and SMAF-ECC was proposed. The results show that the failure mode of the tensile test specimens is mainly steel bar pull-out failure; the incorporation of SMAF significantly enhances the bond strength between the steel bar and matrix; increasing the steel bar diameter and bond length both lead to a decrease in bond strength while increasing the SMAF volume fraction can significantly increase the bond strength. Among them, the specimen with a steel bar diameter of 12 mm, bond length of 70 mm, and SMAF volume fraction of 0.5% has the largest increase in bond strength, reaching 52.96%. The proposed improved bond-slip constitutive model is in good agreement with the bond-slip curve obtained in the experiments, with a determination coefficient of 0.99. The research results of this paper provide an important theoretical basis for promoting the engineering application of SMAF-ECC materials. [ABSTRACT FROM AUTHOR]

The incorporation of superelastic shape memory alloy (SMA) fibers into engineered cementitious composite (ECC) materials can provide high seismic energy dissipation and deformation self-centering capabilities for ECC materials. Whether the SMA fibers can be sufficiently bonded or anchored in the ECC matrix and whether the mechanical properties of the SMA fibers in the ECC matrix can be effectively utilized are the key scientific issues that urgently need to be studied. In order to study the mechanical behavior of SMA fiber embedded in ECC matrix, four groups of semi-dog-bone pullout specimens were fabricated, and the cyclic pullout tests were conducted in this paper. The pullout stress, displacement, and self-centering capability were analyzed, and different influencing factors were discussed. The results show that the knotted ends can provide sufficient anchorage force for SMA fibers, and the maximum pullout stress of SMA fiber can reach 1100 MPa, thus the superelasticity can be effectively stimulated. The SMA fibers show excellent self-centering capability in the test. The minimum residual deformation in the test is only 0.29 mm, and the maximum self-centering ratio can reach 0.93. Increasing bond length can increase the ultimate strain of SMA fibers with knotted ends, but reduce the maximum pullout stress. Increasing fiber diameter can increase both the ultimate strain and the maximum stress of knotted end SMA fibers. While neither bond length nor fiber diameter has significant effect on the self-centering ratio. This paper provides a theoretical basis for further study of the combination of SMA fibers and ECC materials. [ABSTRACT FROM AUTHOR]

The combination of superelastic shape memory alloy fibers and ECC materials can form a new SMA fiber reinforced ECC composite material (SMAF-ECC) with good self-centering performance. In order to study the self-centering performance of the new composite material, 6 groups of pre-notch beam specimens were made for three-point bending cyclic loading tests, and the failure phenomenon, hysteresis curve, self-centering effect and influencing factors of the specimens were analyzed. The research results show that when the SMA fibers are effectively anchored in the ECC matrix, the SMA fibers can exert the superelastic properties to provide the ECC beams with recoverying force, and realize the crack self-closure and deflection self-recovery function for the beams, with the minimum residual crack width and deflection is only 0.9 mm and 1.3 mm respectively. Increasing fiber content can cause a small increase in the self-centering ability of the beams. However, only when the fiber diameter is appropriate, better self-centering effect can be achieved, but the difference caused by fiber diameter in the test was only 5%. SMA Fiber end forms have significant influence on self-centering performance. The knotted end beam can get a more than 70% self-centering ratio, while the straight end beams and bended end beams have no self-centering ability. The research results provide important reference for the research and application of this new self-centering materials and their structures. [ABSTRACT FROM AUTHOR]

• The self-recovery performance of SMAF-ECC under cyclic tensile loading were studied, which can provide important basis for establishing a tensile theoretical model. • SMA fibers increase the ultimate strain and ultimate tensile strength of the specimens, and significantly reduce the residual crack width and residual deformation. • The influence of SMA fiber diameter and fiber content to the self-recovery performance of the specimens was studied and analyzed. • The stress state of SMA fibers during the loading process was investigated, providing a basis for evaluating the performance of SMA superelasticity. The incorporation of superelastic shape memory alloy (SMA) fibers into engineered cementitious composites (ECC) has led to a novel composite material, SMAF-ECC, which possesses excellent deformation, energy dissipation, and self-recovery capabilities. To understand the self-recovery performance of this new composite material under tensile loading, this study conducted uniaxial cyclic tension tests on SMAF-ECC specimens to investigate stress, strain, crack width, strain recovery rate, and crack recovery rate, while also considering the primary influencing factors such as SMA fiber diameter and content. The results indicate that the addition of SMA fibers improves the ultimate strain and ultimate tensile strength of ECC; increasing fiber content effectively enhances the strain and crack recovery rates of SMAF-ECC specimens, with the maximum strain recovery rate and crack recovery rate of the tested specimens reaching 69% and 77%, respectively. Both too large and too small SMA fiber diameters lead to reduced recovery rates. In this experiment, when the fiber diameter was 0.5 mm, the strain and crack recovery rates of the specimens were the highest, with a crack recovery rate of 53%, approximately 1.7 times that of specimens with 1 mm and 0.2 mm diameter SMA fibers. These findings provide a reliable basis for establishing a theoretical model of the tensile mechanical properties of SMAF-ECC composite materials. [ABSTRACT FROM AUTHOR]